Composite material preparation process for photovoltaic bracket construction

A composite material and preparation process technology, applied in the field of photovoltaic support material preparation technology, can solve the problems of poor corrosion resistance of the support system, affecting the overall use performance of the solar support system, and poor use durability of the support system, so as to ensure the overall use performance, Excellent corrosion resistance, acid resistance and alkali resistance improvement effect

Inactive Publication Date: 2019-04-16
宁夏银星能源光伏发电设备制造有限公司 +1
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the existing solar photovoltaic support system, due to the use of metal materials for construction, usually has the defect of poor corrosion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0022] A composite material preparation process for photovoltaic support construction, comprising the following specific steps:

[0023] S1: Raw material preparation: Prepare resins with the following mass components according to the mass parts: 20 parts of epoxy vinyl ester resin, 5 parts of PDMS, 5 parts of polyacrylic resin, 10 parts of styrene-butadiene transparent impact resin, 15 parts of EVA, ABS resin 15 parts, 5 parts of polypropylene resin, 12 parts of polystyrene resin, 16 parts of polyvinyl chloride resin, 13 parts of polyethylene resin, 0.5 parts of PDMS curing agent, 1.5 parts of EVA curing agent;

[0024] S2: Resin preparation: according to the set raw material components in step S1, first mix epoxy vinyl ester resin, PDMS, polyacrylic acid resin, styrene-butadiene transparent impact resin, EVA, ABS resin, polypropylene resin, and then Put it in a water bath stirrer and stir evenly; after stirring for 30 minutes, add polystyrene resin, polyvinyl chloride resin, ...

specific Embodiment 2

[0031] A composite material preparation process for photovoltaic support construction, comprising the following specific steps:

[0032] S1: Raw material preparation: Prepare resins with the following mass components according to the mass parts: 20 parts of epoxy vinyl ester resin, 5 parts of PDMS, 5 parts of polyacrylic resin, 10 parts of styrene-butadiene transparent impact resin, 15 parts of EVA, ABS resin 15 parts, 5 parts of polypropylene resin, 12 parts of polystyrene resin, 16 parts of polyvinyl chloride resin, 13 parts of polyethylene resin, 0.5 parts of PDMS curing agent, 1.5 parts of EVA curing agent;

[0033] S2: Resin preparation: according to the set raw material components in step S1, first mix epoxy vinyl ester resin, PDMS, polyacrylic acid resin, styrene-butadiene transparent impact resin, EVA, ABS resin, polypropylene resin, and then Put it in a water bath stirrer and stir evenly; after stirring for 30 minutes, add polystyrene resin, polyvinyl chloride resin, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Particle sizeaaaaaaaaaa
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of photovoltaic bracket material preparation processes, in particular to a composite material preparation process for the photovoltaic bracket construction. The process comprises the following specific steps of S1, raw material preparation; S2, resin preparation; S3, resin strengthening; S4, mold forming. Through the technical scheme of the process, thedefects that current metal materials have poor durability and insufficient corrosion resistance can be solved, it is further ensured that an existing photovoltaic bracket system can have better durability, and the overall use performance of a bracket structure can be ensured. The surface wear resistance of a bracket material can be effectively improved, it is ensured that the bracket material canwithstand certain wear resistance, thereby ensuring the durability of the bracket material, and the overall flame retardant performance of the material is guaranteed; the use of a release agent is beneficial to the molding and demoulding of the bracket material, and the process has a good practical value and a promotion value.

Description

technical field [0001] The invention relates to the technical field of preparation technology of photovoltaic support materials, in particular to a preparation process of composite materials used for photovoltaic support construction. Background technique [0002] The solar photovoltaic support is a special support designed for placing, installing and fixing solar panels in the solar photovoltaic power generation system. The general materials are aluminum alloy, carbon steel and stainless steel. [0003] However, the existing solar photovoltaic support system, due to the use of metal materials for construction, usually has the defect of poor corrosion resistance of the support system, resulting in poor durability of the support system, thereby affecting the overall performance of the solar support system. [0004] Therefore, based on the above, this application provides a composite material preparation process for photovoltaic support construction. By rationally improving t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L63/10C08L83/04C08L33/00C08L51/04C08L23/08C08L55/02C08L23/12C08L25/06C08L27/06C08L23/06C08K13/04C08K7/14C08K3/34C08K7/06C08K3/38
CPCC08L63/10C08K2003/385C08L2201/02C08L2205/035C08L83/04C08L33/00C08L51/04C08L23/0853C08L55/02C08L23/12C08L25/06C08L27/06C08L23/06C08K13/04C08K7/14C08K3/34C08K7/06C08K3/38
Inventor 安百俊贾鹏李营李归利水云峰
Owner 宁夏银星能源光伏发电设备制造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com