Improved toy shell material and preparation method thereof

A technology for shell materials and toys, which is applied in the field of improved toy shell materials and their preparation, can solve the problems of unbreakable shells, easy to burst, children's scratches, etc., and achieves that it is not easy to crack, shortens the injection molding cycle, and optimizes process parameters. Effect

Pending Publication Date: 2019-04-12
PACIFIC INDAL ZHONGSHAN
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the toy shell material in the prior art has the following disadvantages: it is difficult to push the top, and the shell cannot be broken even after pushing the top for half an hour, and it is easy to burst when doing a simulated transportation test, and the fragments after bursting are relatively sharp, which is easy to cause children to scratch

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Improved toy shell material and preparation method thereof
  • Improved toy shell material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] A preparation method of an improved toy shell material, comprising:

[0036] Component A granulation step: Add the EVA, zinc stearate and calcium carbonate in the formula amount into the mixer, stir evenly, then pour into the extruder to extrude the strands, after cooling, divide and cut into granules, get particle A;

[0037] The granulation step of component B: put calcium carbonate, lubricant and EVA in the formula amount into the mixer, stir evenly, then pour into the extruder to extrude the strands, after cooling, divide and cut into granules to obtain Particle B;

[0038] Injection molding step: add granule A and granule B into a mixer according to the formula ratio, stir evenly, and then pour into an injection molding machine for injection molding to obtain an improved toy shell material.

[0039] As a further embodiment, in the granulation step of component A, the stirring speed of the mixer is controlled to be 50-200r / min, and the stirring time is 10 minutes;...

Embodiment 1

[0045] An improved toy shell material prepared from component A and component B; the weight ratio of component A to component B is 1:1; wherein,

[0046] Component A includes the following ingredients by mass percentage: EVA 20%, zinc stearate 3%, calcium carbonate 77%;

[0047] Component B includes the following components in terms of mass percentage: 60% of calcium carbonate, 15% of lubricant, and 25% of EVA. .

[0048] A preparation method of an improved toy shell material, comprising:

[0049] Component A granulation step: Add the EVA, zinc stearate and calcium carbonate in the formula amount into the mixer, stir evenly, then pour into the extruder to extrude the strands, after cooling, divide and cut into granules, Granule A was obtained; the stirring speed of the mixer was controlled to be 100r / min, and the stirring time was 10 minutes; the temperature of zone 1 of the extruder was controlled to be 200°C, the temperature of zone 2 was 190°C, and the temperature of zone...

Embodiment 2

[0053] An improved toy shell material prepared from component A and component B; the weight ratio of component A to component B is 1:0.8; wherein,

[0054] Component A includes the following ingredients by mass percentage: EVA 18%, zinc stearate 2%, calcium carbonate 80%;

[0055] Component B includes the following components in terms of mass percentage: calcium carbonate 58%, lubricant 12%, EVA 30%.

[0056] A preparation method of an improved toy shell material, comprising:

[0057] Component A granulation step: Add the EVA, zinc stearate and calcium carbonate in the formula amount into the mixer, stir evenly, then pour into the extruder to extrude the strands, after cooling, divide and cut into granules, Granule A was obtained; the stirring speed of the mixer was controlled to be 200r / min, and the stirring time was 8 minutes; the temperature of zone 1 of the extruder was controlled to be 200°C, the temperature of zone 2 was 190°C, and the temperature of zone 3 was 190°C; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an improved toy shell material. The improved toy shell material is prepared from a component A and a component B, and the weight ratio of the component A to the component B is1:(0.8-1.2), wherein the component a comprises the following components in percentage by mass: 18-22% of ethylene vinyl acetate (EVA), 2-4% of zinc stearate and 74-80% of calcium carbonate, and the component B comprises the following components in percentage by mass: 58-62% of calcium carbonate, 12-18% of a lubricant and 20-30% of EVA. The invention further discloses a preparation method of the improved toy shell material. The toy shell material can be easily cracked by pushing, a packaged finished product is not easily cracked in a transportation process, sharp points or edges are avoided after the shell material is broken, and thus children are prevented from being scratched.

Description

technical field [0001] The invention relates to a toy shell material, in particular to an improved toy shell material and a preparation method thereof. Background technique [0002] Toy eggshell is a toy that allows children to experience the egg hatching process. It is very mysterious and can fully stimulate children's desire to explore. The toy eggshell is sealed and packaged before hatching. When hatching, it needs to hatch for more than 10 minutes (that is, the doll inside the eggshell pushes the inner wall of the eggshell with external force), so that the outer shell of the toy eggshell gradually breaks, revealing the inside Hiding figure. However, the toy shell material in the prior art has the following disadvantages: it is difficult to push the top, and the shell cannot be broken for half an hour after pushing the top, and it is easy to burst when doing a simulated transportation test. The fragments after bursting are sharper and easily scratched by children. Cont...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08K5/098C08K3/26
CPCC08L23/0853C08K2003/265C08L2205/025C08L2205/03C08K5/098C08K3/26
Inventor 唐勇杨兵
Owner PACIFIC INDAL ZHONGSHAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com