Anti-static automobile grille and preparation method thereof

An antistatic and grille technology, applied in the field of antistatic automobile grille and its preparation, can solve the problems of not being able to meet the needs of use, and achieve the effects of ensuring service life, enhancing pressure resistance and strength

Inactive Publication Date: 2019-03-19
浙江祥盛汽车科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] As everyone knows, the automobile grille is a structure used for automobile heat dissipation, because it can lead the air to the engine and other heat-generating parts through the principle of aerodynamics to dissipate heat during driving, so it is widely used in the automotive field; and in the prior art The automobile grilles are all made of simple materials. At most, after the preparation is completed, the surface is evenly sprayed with a coating, which can no longer meet the needs of current use. Therefore, we propose an antistatic automobile grille and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The present invention proposes an antistatic automobile grille, whose raw materials are formulated as follows by weight: 40 parts of ABS resin, 20 parts of silicone resin, 12 parts of polypropylene, 5 parts of carbon fiber, 8 parts of glass fiber, 8 parts of mixed metal powder, 5 parts of sodium dodecylbenzene sulfonate, 5 parts of polyaniline, 3 parts of barium stearate, 8 parts of dust absorbent, 1 part of antioxidant, 3 parts of plasticizer, and 3 parts of binder.

[0023] The present invention also provides a kind of preparation method of antistatic automobile grid, comprises the following steps:

[0024] S1. Slowly put ABS resin, silicone resin and polypropylene into the mixing melting furnace in sequence, and during the addition process, it needs to be mixed and stirred in an environment of 60 degrees Celsius. After the addition is completed, the temperature is raised to 200 degrees Celsius. , until it is completely melted, and then filtered to form the first mixe...

Embodiment 2

[0030] The present invention proposes an antistatic automobile grille, whose raw materials are formulated as follows by weight: 45 parts of ABS resin, 23 parts of silicone resin, 14 parts of polypropylene, 5.5 parts of carbon fiber, 9 parts of glass fiber, 9 parts of mixed metal powder, 5.5 parts of sodium dodecylbenzenesulfonate, 5.5 parts of polyaniline, 3.5 parts of barium stearate, 9 parts of dust absorbent, 1.5 parts of antioxidant, 3.5 parts of plasticizer, and 3.5 parts of binder.

[0031] The present invention also provides a kind of preparation method of antistatic automobile grid, comprises the following steps:

[0032] S1. Slowly put ABS resin, silicone resin and polypropylene into the mixing melting furnace in sequence, and during the addition process, it needs to be mixed and stirred in an environment of 65 degrees Celsius. After the addition is completed, the temperature is raised to 230 degrees Celsius. , until it is completely melted, and then filtered to form ...

Embodiment 3

[0038] The present invention proposes an antistatic automobile grille, whose raw materials are formulated as follows by weight: 50 parts of ABS resin, 25 parts of silicone resin, 16 parts of polypropylene, 6 parts of carbon fiber, 10 parts of glass fiber, 10 parts of mixed metal powder, 6 parts of sodium dodecylbenzenesulfonate, 6 parts of polyaniline, 4 parts of barium stearate, 10 parts of dust absorbent, 2 parts of antioxidant, 4 parts of plasticizer, and 4 parts of binder.

[0039] The present invention also provides a kind of preparation method of antistatic automobile grid, comprises the following steps:

[0040] S1. Slowly put ABS resin, silicone resin and polypropylene into the mixing melting furnace in sequence, and during the addition process, it needs to be mixed and stirred in an environment of 70 degrees Celsius. After the addition is completed, the temperature is raised to 250 degrees Celsius. , until it is completely melted, and then filtered to form the first m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-static automobile grille, which comprises the following raw materials in parts by weight: 40-60 parts of ABS (Acrylonitrile Butadiene Styrene) resins, 20-30 parts of silicone resins, 12-20 parts of polypropylene, 5-7 parts of carbon fibers, 8-12 parts of glass fibers, 8-12 parts of mixed metal powder, 5-7 parts of sodium dodecyl benzene sulfonate, 5-7 parts of polyaniline, 3-5 parts of barium stearate, 8-12 parts of dust adsorbents, 1-3 parts of antioxidants, 3-5 parts of plasticizers and 3-5 parts of binders. The invention further discloses a preparation methodof the anti-static automobile grille. According to the anti-static automobile grille, the pressure resistance and strength of the grille are effectively enhanced, the grille has anti-static capability, and meets the requirements of current development.

Description

technical field [0001] The invention relates to the technical field of automobile grille preparation, in particular to an antistatic automobile grille and a preparation method thereof. Background technique [0002] As everyone knows, the automobile grille is a structure used for automobile heat dissipation, because it can lead the air to the engine and other heat-generating parts through the principle of aerodynamics to dissipate heat during driving, so it is widely used in the automotive field; and in the prior art The automobile grilles are all made of simple materials. At most, after the preparation is completed, the surface is evenly sprayed with a coating, which can no longer meet the needs of current use. Therefore, we propose an antistatic automobile grille and its preparation method. Contents of the invention [0003] The present invention proposes an antistatic automobile grille and its preparation method to solve the problems raised in the above-mentioned backgr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L83/04C08L23/12C08L79/02C08K13/04C08K7/14C08K7/06C08K3/08C08K5/42C08K5/098
CPCC08K2003/0812C08K2003/085C08K2003/0881C08K2003/0893C08K2201/017C08L55/02C08L2201/04C08L2205/035C08L83/04C08L23/12C08L79/02C08K13/04C08K7/14C08K7/06C08K3/08C08K5/42C08K5/098
Inventor 林长江
Owner 浙江祥盛汽车科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com