A kind of strip steel cold rolling rolling oil composition and preparation method thereof

A technology of cold rolling and oil composition, which is applied in the field of rolling oil, which can solve problems such as difficult maintenance, influence on lubricity and cleanliness, and slow response speed of concentration, so as to reduce the difficulty of maintenance and management and improve the wide application , the effect of good market prospects

Active Publication Date: 2021-10-22
JIANGSU ZHONGSHENG GAOKE ENVIRONMENTAL CO LTD
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Stable emulsions have good cleanliness and less oil slick, which is convenient for maintenance and management, but their lubricity and cleanliness will be affected; unstable emulsions have good lubricity, but oil slicks will appear during on-site use and the concentration response speed is slow , high fuel consumption, dirty rolling mill, etc., making maintenance difficult

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of strip steel cold rolling rolling oil composition and preparation method thereof
  • A kind of strip steel cold rolling rolling oil composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of steel strip cold rolling rolling oil composition, comprises following composition according to mass percentage:

[0028] Trimethylolpropane Oleate 30%, Palm Oil 15%, Lard 15%, Mineral Oil 150SN 10%, Dioctyldiphenylamine 0.1%, Benzotriazole 0.5%, Sulfurized Lard 5%, Sulfurized Olefin 3%, 6721%, Doverlube NCL-21%, Hypermer A70 10% and GENAPOL X 0809.4%.

[0029] The preparation method of strip steel cold rolling rolling oil composition comprises the steps in the present embodiment:

[0030] 1) Weigh trimethylolpropane oleate, palm oil, lard, and mineral oil 150SN according to the above proportions and add them into the reaction tank, and heat to 80°C while stirring;

[0031] 2) Dioctyldiphenylamine and benzotriazole were weighed according to the above ratio and added to the mixture in step 1, keeping the temperature in step 1 at 80°C, and stirring until the solids were completely dissolved;

[0032] 3) cooling the mixture obtained in step 2 to a temperature ...

Embodiment 2

[0036] A kind of steel strip cold rolling rolling oil composition, comprises following composition according to mass percentage:

[0037] Trimethylolpropane Oleate 30%, Palm Oil 30%, Lard 20%, Mineral Oil 350SN 10%, Dioctyldiphenylamine 2%, Benzotriazole 4%, Sulfurized Lard 1%, Sulfurized Olefin 0.5%, 6720.5%, Doverlube NCL-20.5%, HypermerA701% and GENAPOLX 0801%.

[0038] The preparation method of strip steel cold rolling rolling oil composition comprises the steps in the present embodiment:

[0039] 1) Weigh trimethylolpropane oleate, palm oil, lard, and mineral oil 150SN according to the above proportions and add them to the reaction tank, and heat to 90°C while stirring;

[0040] 2) Dioctyldiphenylamine and benzotriazole were weighed according to the above ratio and added to the mixture in step 1, keeping the temperature in step 1 at 90°C, and stirring until the solids were completely dissolved;

[0041] 3) cooling the mixture obtained in step 2 to a temperature of 60°...

Embodiment 3

[0045] A kind of steel strip cold rolling rolling oil composition, comprises following composition according to mass percentage:

[0046] Trimethylolpropane Oleate 50%, Lard 20%, Mineral Oil 350SN 10%, Dioctyldiphenylamine 1%, Benzotriazole 2%, Sulfurized Lard 5%, Sulfurized Olefin 2%, 6721%, Doverlube NCL-21%, HypermerA 704% and GENAPOL X 0804%.

[0047] The preparation method of strip steel cold rolling rolling oil composition comprises the steps in the present embodiment:

[0048] 1) Weigh trimethylolpropane oleate, palm oil, lard, and mineral oil 150SN according to the above proportions and add them to the reaction tank, and heat to 85°C while stirring;

[0049] 2) Dioctyldiphenylamine and benzotriazole were weighed according to the above ratio and added to the mixture in step 1, keeping the temperature in step 1 at 85°C, and stirring until the solids were completely dissolved;

[0050] 3) cooling the mixture obtained in step 2 to a temperature of 55°C;

[0051] 4) Sul...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a strip steel cold rolling oil composition and a preparation method thereof, which comprises the following components according to mass percentage: 70-90% of base oil, 0.1-2% of antioxidant, 0.5-4% of slow-release agent, Extreme pressure lubricant 2-10%, emulsifier 1-20%, the preparation method includes: adding base oil into the reaction tank in proportion, heating to the specified temperature range while stirring; adding antioxidant and slow-release agent in proportion Add to the mixture in step 1, keep the temperature range, and stir until the solid is completely dissolved; cool the obtained mixture; add the extreme pressure lubricant and emulsifier into the mixture in proportion, keep the temperature range after cooling, and stir Until the mixture is completely homogeneous and transparent, the finished composition is obtained. Compared with the prior art, in the present invention, the lubricity and stability of the cold-rolling oil are balanced overall, which not only ensures good lubricating performance of the cold-rolling oil, but also reduces the difficulty of maintenance and management.

Description

technical field [0001] The invention belongs to the technical field of rolling oil, and in particular relates to a strip steel cold rolling rolling oil composition and a preparation method thereof. Background technique [0002] Rolling liquid is an essential oil product in the cold rolling process of strip steel, which plays the roles of lubrication, cooling, cleaning and rust prevention. When used on site, the rolling liquid is usually mixed with a certain proportion of water (usually the water content is 95-98%), and then it is used as an emulsion after stirring. The lubricity and stability of the emulsion are very important for the use of rolling liquid. Performance matters. [0003] Good lubricity, low rolling force, good shape and high surface quality after rolling. Stable emulsions have good cleanliness and less oil slick, which is convenient for maintenance and management, but their lubricity and cleanliness will be affected; unstable emulsions have good lubricity, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10M169/04C10N40/24C10N30/06
CPCC10M169/045C10M2203/1025C10M2207/2835C10M2207/401C10M2215/064C10M2215/223C10M2219/022C10M2219/024C10N2030/06C10N2040/24C10N2040/243C10N2020/02
Inventor 许春栋蒋华良许群益杨佳田祖胜
Owner JIANGSU ZHONGSHENG GAOKE ENVIRONMENTAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com