Kaolinite archaized brick and method thereof

A technology of kaolinite and antique bricks, applied in the field of restoration of ancient buildings, can solve the problems of high density of unburned bricks, and achieve the effects of realistic antique effect, reducing density and avoiding cumbersome production process.

Pending Publication Date: 2019-02-15
HENAN BESTBUILDER NETWORK TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies in the above-mentioned technologies, the present invention provides a kaolinite antique brick and its method to solve the problem of excessive density of existing kaolinite unburned bricks

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Kaolinite archaized brick and method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] This embodiment provides a kaolinite antique brick, which is prepared from the following raw materials in parts by weight: 50 parts of kaolin slag, 8 parts of coal gangue, 8 parts of corn straw, 8 parts of fine sand, and 22 parts of sludge. Parts, 6 parts of salt gypsum, 6 parts of white cement, 1 part of silica fume, 0.7 parts of calcium chloride, 0.8 parts of calcium oxide, 0.8 parts of disodium EDTA.

[0026] The preparation method of kaolinite antique brick in this embodiment includes the following steps:

[0027] (1) Feed the corn stalks into the crusher, and then crush them for later use;

[0028] (2) After the coal gangue is screened and removed, it is sent to a crusher to be crushed, washed with water to remove debris and floating objects, and then reserved;

[0029] (3) Add the sludge to a forced mixer, and then add disodium EDTA. After forced stirring for 8 minutes, let it stand for 45 minutes; then weigh the kaolin slag, coal gangue, corn stalks, fine sand, and salt ...

Embodiment 2

[0033] This embodiment provides a kaolinite antique brick, which is prepared from the following raw materials in parts by weight: 45 parts of kaolin slag, 10 parts of coal gangue, 5 parts of corn stalks, 10 parts of fine sand, and 20 parts of sludge. Parts, 8 parts salt gypsum, 5 parts white cement, 2 parts silica fume, 0.5 parts calcium chloride, 1.0 parts calcium oxide, 0.5 parts disodium EDTA.

[0034] The preparation method of kaolinite antique brick in this embodiment includes the following steps:

[0035] (1) Feed the corn stalks into the crusher, and then crush them for later use;

[0036] (2) After the coal gangue is screened and removed, it is sent to a crusher to be crushed, washed with water to remove debris and floating objects, and then reserved;

[0037] (3) Add the sludge to a forced mixer, then add disodium EDTA, and after forced stirring for 5 minutes, let it stand for 60 minutes; then weigh kaolin slag, coal gangue, corn stalks, fine sand, and salt gypsum according t...

Embodiment 3

[0041] This embodiment provides a kaolinite antique brick, which is prepared from the following raw materials in parts by weight: 55 parts of kaolin slag, 5 parts of coal gangue, 10 parts of corn stalks, 5 parts of fine sand, and 25 parts of sludge. Parts, 5 parts of salt gypsum, 8 parts of white cement, 1.0 part of calcium chloride, 0.5 part of calcium oxide, 1.0 part of disodium EDTA.

[0042] The preparation method of kaolinite antique brick in this embodiment includes the following steps:

[0043] (1) Feed the corn stalks into the crusher, and then crush them for later use;

[0044] (2) After the coal gangue is screened and removed, it is sent to a crusher to be crushed, washed with water to remove debris and floating objects, and then reserved;

[0045] (3) Add the sludge to a forced mixer, then add disodium EDTA, and after forced stirring for 10 minutes, let it stand for 30 minutes; then weigh the kaolin slag, coal gangue, corn stalks, fine sand, and salt gypsum according to the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a kaolinite archaized brick and a preparation method thereof, and belongs to the technical field of restoration of ancient buildings. The kaolinite archaized brick is preparedfrom the following raw materials in parts by weight: 45-55 parts of kaolinite slag, 5-10 parts of coal gangue, 5-10 parts of corn straws, 5-10 parts of fine sand, 20-25 parts of sludge, 5-8 parts of salt gypsum, 5-8 parts of white cement, 0-2 parts of a silicon powder, 0.5-1.0 part of calcium chloride, 0.5-1.0 part of calcium oxide, and 0.5-1.0 part of EDTA disodium. The corn straw pulverized by apulverizer is added to the kaolinite slag and the coal gangue to increase the strength of the archaized brick, reduce the density of the archaized brick and reduce the weight; and the silicon powderadded not only improves the strength of the archaized bricks, but also causes the archaized brick to be blue gray with a vivid antique effect; and the sludge added reduces the cost of the archaized brick, and the sludge can be recycled to save natural resources such as sand and clay.

Description

Technical field [0001] The invention relates to the technical field of ancient building restoration, in particular to a kaolinite antique brick and a preparation method thereof. Background technique [0002] Kaolinite is also known as "kaolin" and "china clay". A clay mineral. It was named after it was first discovered in Gaoling Village near Jingdezhen, Jiangxi. Aluminosilicate minerals such as feldspar and pyroxene are formed during weathering. It is earthy or massive, with low hardness, plasticity, adhesion and volume expansion when wet, especially microcrystalline kaolinite (also known as "montmorillonite", "jiaolinite") has greater expansion (can be Up to several times to ten times). The main components of microcrystalline kaolinite and belayite are called bentonite. In addition to being used as ceramic raw materials, papermaking raw materials, rubber and plastic fillers, refractory materials, etc., kaolinite clay can also be used to synthesize zeolite molecular sieves ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B111/20C04B111/82
CPCC04B28/142C04B2111/00017C04B2111/20C04B2111/82C04B2201/50C04B14/106C04B18/12C04B18/248C04B14/06C04B18/0436C04B7/02C04B18/146C04B22/124C04B22/064C04B24/123
Inventor 王铁成
Owner HENAN BESTBUILDER NETWORK TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com