Preparation method of waterproof and moldproof paint for cupboard

A waterproof and mildew-proof, cabinet technology, applied in the field of cabinets, can solve the problems of flame retardant performance, waterproof and anti-corrosion performance of coatings, etc., and achieve good flame retardant and self-cleaning performance, fast drying speed, good waterproof and anti-corrosion performance. Effect

Inactive Publication Date: 2019-02-12
合肥永泰新型建材有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the coating of the present invention is applied on the product, the paint surface is flat and smooth; it has good adhesion, fast drying speed, and self-cleaning property of oil stains, but the flame retardancy, waterproof and anti-corrosion properties of the coating need to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041]This embodiment relates to a preparation method of waterproof and mildew-proof paint for cabinets;

[0042] The preparation method of described cabinet waterproof mold proof paint, comprises the steps:

[0043] (1) Prepare the following components by weight according to the following ratio:

[0044] 32 parts of silicone modified polyacrylamide, 15 parts of polyketone resin, 13 parts of polyether resin, 16 parts of graphene modified polyvinyl alcohol, 9 parts of nano titanium dioxide, 11 parts of antimony trioxide, 16 parts of chlorinated paraffin, 7 parts of nano-magnesium hydroxide, 6 parts of ultra-fine mica powder, 5 parts of white carbon black, 8 parts of nano-silica, 12 parts of high-viscosity attapulgite clay, 6 parts of diatomaceous earth, 8 parts of anti-mildew additive, coloring material 3 parts, 3 parts of defoamer;

[0045] (2) Weigh the proportioned amount of anti-mold additive, add water to fully dissolve it, then place it under ultrasonic conditions, add ...

Embodiment 2

[0063] This embodiment relates to a preparation method of waterproof and mildew-proof paint for cabinets;

[0064] The preparation method of described cabinet waterproof mold proof paint, comprises the steps:

[0065] (1) Prepare the following components by weight according to the following ratio:

[0066] 30 parts of silicone modified polyacrylamide, 12 parts of polyketone resin, 9 parts of polyether resin, 10 parts of graphene modified polyvinyl alcohol, 6 parts of nano titanium dioxide, 6 parts of antimony trioxide, 10 parts of chlorinated paraffin, 4 parts of nano-magnesium hydroxide, 5 parts of superfine mica powder, 3 parts of white carbon black, 5 parts of nano-silica, 8 parts of high-viscosity attapulgite clay, 3 parts of diatomaceous earth, 5 parts of anti-mildew additive, coloring material 1 part, 2 parts of defoamer;

[0067] (2) Weigh the proportioned amount of anti-mildew additive, add water to fully dissolve it, then place it under ultrasonic conditions, add hi...

Embodiment 3

[0085] This embodiment relates to a preparation method of waterproof and mildew-proof paint for cabinets;

[0086] The preparation method of described cabinet waterproof mold proof paint, comprises the steps:

[0087] (1) Prepare the following components by weight according to the following ratio:

[0088] 36 parts of silicone modified polyacrylamide, 17 parts of polyketone resin, 16 parts of polyether resin, 18 parts of graphene modified polyvinyl alcohol, 13 parts of nano titanium dioxide, 15 parts of antimony trioxide, 18 parts of chlorinated paraffin, 9 parts of nano-magnesium hydroxide, 10 parts of superfine mica powder, 7 parts of white carbon black, 11 parts of nano-silica, 16 parts of high-viscosity attapulgite clay, 7 parts of diatomaceous earth, 10 parts of anti-mildew additive, coloring material 4 parts, 6 parts of defoamer;

[0089] (2) Weigh the proportioned amount of anti-mold additive, add water to fully dissolve it, then place it under ultrasonic conditions, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of waterproof and moldproof paint for a cupboard. The preparation method comprises the following steps of weighing the following raw materials including organosilicone modified polyacrylamide, polyketone resin, polyether resin, graphene modified polyvinyl alcohol, nanometer titanium dioxide, antimonous oxide, chlorinated paraffin, nanometer magnesium hydroxide, superfine mica powder, white carbon black, nanometer silicon dioxide, high viscosity attapulgite clay, diatomite, an moldproof additive, a pigment and a defoamer, respectively crushing the rawmaterials, and performing uniform mixing to obtain a paint film. The preparation method of the waterproof and moldproof paint for the cupboard is simple in process and convenient to operate; and theprepared paint is applied to the cupboard, has the characteristics of rapid drying speed, good waterproof performance, good corrosion resistant performance and strong adhesion force, also has better flame retardant performance and self-cleaning performance, effectively inhibits breeding of molds and provides guarantee to safe and long-term use of the cupboard.

Description

technical field [0001] The invention relates to the technical field of cabinets, in particular to a method for preparing a waterproof and mildew-proof paint for cabinets. Background technique [0002] Paint is a chemical mixture coating that can firmly cover the surface of objects for protection, decoration, marking and other special purposes. The relatively authoritative book "Painting Technology" in the Chinese coatings industry defines it as follows: "Painting is a material that can be coated on the surface of an object by different construction techniques to form a firm adhesion, a certain strength, and a continuous coating. Solid film. The film formed in this way is commonly called coating film, also known as paint film or coating.” It belongs to organic chemical polymer materials, and the formed coating film belongs to the type of polymer compound. According to the classification of modern chemical products, coatings belong to fine chemical products. Modern coatings ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/14C09D133/26C09D173/00C09D171/00C09D7/61C09D7/65C09D5/08C09D5/18
CPCC09D5/14C08K2003/2224C08K2003/2241C08K2201/011C08L2205/035C09D5/08C09D5/18C09D7/61C09D7/65C09D7/70C09D143/04C08L73/00C08L71/00C08L29/04C08L91/06C08K13/04C08K7/26C08K3/22C08K3/042C08K3/2279C08K3/34C08K3/36C08K3/346C08K5/0058
Inventor 伍志远
Owner 合肥永泰新型建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com