Preparation method and application of polyvinyl alcohol nonwoven fabric finishing agent

A polyvinyl alcohol, non-woven technology, applied in fiber processing, textiles and papermaking, improved hand-feeling fibers, etc., can solve certain limitations in the application field, low efficiency of polyvinyl alcohol non-woven fabrics, and poor heat sealing. performance and other issues, to achieve the effect of improving mechanical properties, strengthening overall performance, and improving elongation at break

Active Publication Date: 2019-02-01
SHENGZHEN SAILONG FIBERGLASS CO LTD
View PDF5 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It cannot have excellent heat sealing properties like non-woven fabrics prepared by other commonly used plastic synthetic resins, so it is subject to certain restrictions in the application field, such as the second processing of non-woven fabrics: edge sealing, sealing, bag making, etc. etc., only traditional manual stitching can be performed instead of the process of automatic heat-sealing processing machinery
This leads to inefficiency in the product processing process of polyvinyl alcohol non-woven fabrics and high processing costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and application of polyvinyl alcohol nonwoven fabric finishing agent
  • Preparation method and application of polyvinyl alcohol nonwoven fabric finishing agent
  • Preparation method and application of polyvinyl alcohol nonwoven fabric finishing agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] The padding finishing of polyvinyl alcohol nonwoven fabric specifically comprises the following steps:

[0041] (1) The impregnating finishing agent for finishing includes the following components in parts by weight (see Table 1):

[0042] Table 1

[0043]

[0044]

[0045] After measuring the materials in the above components, add them to a dissolution vessel with a heating jacket, raise the temperature to 95°C under stirring (50 rpm), mix and dissolve for 4 hours, and keep warm at 90°C for 30 minutes, then cool down to room temperature Discharge is standby, is the finishing agent of a kind of polyvinyl alcohol non-woven fabric of the present invention;

[0046] (2) Specification of polyvinyl alcohol non-woven fabric for finishing: 28g / m 2 ;

[0047] (3) padding finishing process (see figure 1 ): release the polyvinyl alcohol non-woven fabric by the unwinding roller 1-1, enter the impregnation tank 1-2 filled with the finishing agent of embodiment 1 through t...

Embodiment 2

[0053] The padding finishing of polyvinyl alcohol nonwoven fabric specifically comprises the following steps:

[0054] (1) The impregnating finishing agent for finishing includes the following components in parts by weight (see Table 3):

[0055] table 3

[0056]

[0057] After measuring the materials in the above components, add them to the dissolution container with a heating jacket, raise the temperature to 95°C under stirring (50 rpm), mix and dissolve for 2 hours, and keep warm at 90°C for 30 minutes, then cool down to room temperature The material is ready for use. It is a finishing agent for polyvinyl alcohol non-woven fabrics of the present invention;

[0058] (2) Specification of polyvinyl alcohol non-woven fabric for finishing: 15g / m2;

[0059] (3) padding finishing process (see figure 1 ): release the polyvinyl alcohol non-woven fabric by the unwinding roller 1-1, enter the impregnation tank 1-2 that the finishing agent of embodiment 2 has been adorned throug...

Embodiment 3

[0066] The padding finishing of polyvinyl alcohol nonwoven fabric specifically comprises the following steps:

[0067] (1) The impregnation finishing agent for finishing includes the following components in parts by weight (see Table 5):

[0068] table 5

[0069]

[0070] After measuring the materials in the above components, add them into the dissolution container with a heating jacket, heat up to 95°C under stirring (50 rpm), mix and dissolve for 3 hours, and keep warm at 90°C for 30 minutes, then cool down to room temperature The material is ready for use. It is a finishing agent for polyvinyl alcohol non-woven fabrics of the present invention;

[0071] (2) Specification of polyvinyl alcohol non-woven fabric for finishing: 10g / m2;

[0072] (3) padding finishing process (see figure 1 ): release the polyvinyl alcohol non-woven fabric by the unwinding roller 1-1, enter the impregnation tank 1-2 filled with the finishing agent of embodiment 3 through the guide roller, fu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method and an application of a polyvinyl alcohol nonwoven fabric finishing agent. The finishing agent comprises, by weight, 10-20 parts of polyvinyl alcohol, 3-8parts of hydroxypropyl cellulose (HPC), 5-20 parts of amide modified polyol, 3-15 parts of alkyl glycosides, 5-10 parts of an inorganic filler, 1-5 parts of hydroxyethyl urea, 0.3-1.0 part of a penetrant, 0.3-1.0 part of imidazolidinyl urea, 0.1-0.3 part of p-hydroxybenzoate and 100 parts of water. The raw materials are mixed and heated to obtain the finishing agent. The finishing agent is suitable for the processes of padding finishing, sizing finishing, coating finishing and the like of a polyvinyl alcohol nonwoven fabric; and the polyvinyl alcohol nonwoven fabric is dipped in or coated withthe finishing agent, and then is dried, set and embossed. The nonwoven fabric finished with the finishing agent has improved heat-sealing performance and enhanced mechanical properties, so the hand feeling of the finished nonwoven fabric is also improved.

Description

technical field [0001] The invention relates to the field of post-treatment of non-woven fabrics, in particular to a preparation method and application of a polyvinyl alcohol non-woven fabric finishing agent. Background technique [0002] As an environmentally friendly material, polyvinyl alcohol (PVA) has been rapidly developed and applied in many fields in recent years. As a country with a large production capacity of vinylon, China has abundant sources of raw materials and application markets. In the pre-production process of vinylon, the polyvinyl alcohol (PVA) fiber formed by wet spinning coagulation bath is directly processed without acetal treatment. It is used to produce polyvinyl alcohol non-woven fabrics, and it has also developed rapidly in recent years. Due to the water-soluble and environmentally friendly properties of polyvinyl alcohol non-woven fabrics, it has begun to replace non-woven fabrics made of plastic synthetic resins in many fields, such as shoemaki...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M15/333D06M15/09D06M13/432D06M13/224D06M11/79D06M101/24
CPCD06M11/79D06M13/224D06M13/432D06M15/09D06M15/333D06M2101/24D06M2200/50
Inventor 崔跃飞
Owner SHENGZHEN SAILONG FIBERGLASS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com