Polylactide-p-dioxanone composite fiber, preparation method thereof, application and surgical suture

A technology of polydioxanone and polylactide, which is applied in the field of surgical sutures, its preparation, polylactide and polydioxanone composite fibers, can solve the limitations of wide application, short degradation time, Expensive and other problems, to achieve the effect of good operability, easy knotting, and smooth surface

Active Publication Date: 2019-01-18
CHINESE TEXTILE ACAD
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the prior art, most of the synthetic sutures in the domestic market are polyglycolic acid (PGA) and lactide-glycolide copolymer (PGLA), and the polylactide used for biodegradable materials is due to its short degradation time and low strength. , clinically, in many surgical occasions where muscle tissue grows for a long time, therefore, its wide application is limited
However, polydioxanone (PDS) is expensive, which limits its wide application.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polylactide-p-dioxanone composite fiber, preparation method thereof, application and surgical suture
  • Polylactide-p-dioxanone composite fiber, preparation method thereof, application and surgical suture
  • Polylactide-p-dioxanone composite fiber, preparation method thereof, application and surgical suture

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0047] See attached figure 2 , the preparation method of polylactide provided by the invention and polydioxanone (PDS) composite fiber comprises the following steps:

[0048] Step 1: Obtain polylactide slices and polydioxanone (PDS) slices respectively;

[0049] Step 2: Composite spinning for polylactide chips and polydioxanone (PDS) sheets, so that polylactide is in the core layer of the composite fiber, and polydioxanone (PDS) wraps The polylactide is used to form the skin layer of the composite fiber, and the polylactide and polydioxanone (PDS) composite fiber is obtained.

[0050] Among them, the process of composite spinning for polylactide chips and polydioxanone (PDS) chips includes:

[0051] Vacuum drying is carried out under the condition of 80° C. to 100° C., and the vacuum degree of vacuum drying ranges from -0.08 MPa to 0.09 MPa.

[0052] Wherein, in step 1, the method for obtaining polydioxanone (PDS) slices comprises the following steps:

[0053] After vacuu...

Embodiment 1

[0070] The cross-sectional area ratio of the skin layer and the core layer (with PLA as the core of the composite fiber, and polydioxanone (PDS) as the skin of the composite fiber) is 20:80, and the spare PLA / polydioxane The hexanone (PDS) was vacuum-dried separately, the drying temperature was 80°C, and the vacuum degree was -0.09MPa. The composite fiber was spun-stretched in one step, and the draw ratio was 5 times. The monofilament fineness is 2.2dtex (50D / 24f). The spinning process conditions are: the temperature range of the core layer component is 200-220°C, the screw pressure is 9.8MPa, the spinning speed is 220m / min, the temperature range of the skin layer component is 140-170°C, the screw pressure is 8.0MPa, the spinning The filament speed is 220m / min, air cooling, side blowing rate is 3m / min, PLA / polydioxanone (PDS) composite fiber can be obtained.

[0071] The performance parameters of PLA / polydioxanone (PDS) composite fiber are: the tensile strength reaches 4.0CN / ...

Embodiment 2～20

[0073]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polylactide-p-dioxanone composite fiber, a preparation method thereof, application and a surgical suture. In the composite fiber, a polylactide fiber serves as a core layer of the composite fiber, and p-dioxanone serves as a skin layer of the composite fiber. The preparation method comprises the following steps: respectively obtaining a polylactide slice and a p-dioxanoneslice; performing composite spinning on the polylactide slice and the p-dioxanone slice, so that polylactide is located at the core layer of the composite fiber, and the p-dioxanone is used for packaging the polylactide to form the skin layer of the composite fiber, so as to obtain the polylactide-p-dioxanone composite fiber. The composite fiber can be used for the surgical suture. The surgical suture is prepared from the composite fiber. The value range of the tensile strength of the composite fiber is 4.0CN / dtex-5.2CN / dtex, and the value range of the breakage elongation is 20%-30%, so thatthe composite fiber can meet the requirements of the surgical suture and is low in manufacturing cost.

Description

technical field [0001] The invention relates to the technical field of composite fibers, in particular to a composite fiber of polylactide and polydioxanone, its preparation method, application and surgical suture. Background technique [0002] Polylactide, also known as polylactic acid, has a hydroxyl group and a carboxyl group in a single lactic acid molecule, multiple lactic acid molecules are together, -OH is dehydrated and condensed with -COOH of other molecules, and -COOH is dehydrated with -OH of other molecules Condensation, and just like that, they go hand in hand to form a polymer called polylactic acid, or polylactide. Polylactide is a polymer obtained by polymerization of lactic acid as the main raw material. The raw material source is sufficient and can be regenerated. The production process of polylactide is non-polluting, and the product can be biodegraded to realize the cycle in nature, so it is an ideal green polymer material. Polydioxanone (PDS) materials...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F8/14D01D5/34A61L17/06A61L17/10A61L17/12
CPCA61L17/06A61L17/10A61L17/12D01D5/34D01F8/14C08L67/04
Inventor 刘伯林黄庆金剑
Owner CHINESE TEXTILE ACAD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com