Golden black glaze for jun-porcelain and preparation method of golden black glaze

A technology of black gold and Jun porcelain, applied in the field of black gold glaze for Jun porcelain and its preparation, can solve the problems of insufficient brightness and uneven color of the glaze surface, and achieve the effect of bright color, uniform color and high brightness

Inactive Publication Date: 2018-12-28
杨鹏飞
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Jun porcelain is widely used in various fields because of its smoothness, compactness and many other advantages. In the preparation process of Jun porcelain, various low-temperature colors are applied to the pure bottom glaze, and Wujin glaze becomes a variety of beautiful The high-profile and elegant Jun porcelain glaze can be obtained by the contrast of the color, but the glaze surface of the Wujin glaze in the prior art is not bright enough.
The color is not uniform enough, so it is necessary to design a moist and bright Jun porcelain Wujin glaze on the basis of reproduction technology.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0017] A preparation method of black gold glaze for Jun porcelain, the steps are as follows:

[0018] S1. Accurately weigh the above components by weight and mix them uniformly to form a mixed solid raw material;

[0019] S2, according to the ratio of mixed solid ball stone: raw material: water = 2: 1.2-1.5: 0.9-1.5, respectively counted into the ball mill for mixing and ball milling to form a slurry;

[0020] S3, after ball milling for 12.5-14 hours, detect the fineness of the slurry;

[0021] S4, sieve the slurry whose fineness is qualified to remove iron, and prepare black gold black glaze.

Embodiment 1

[0023] A black gold glaze for Jun porcelain, which consists of 40 parts by weight of feldspar, 16 parts of quartz, 10 parts of calcite, 5 parts of copper ore, 5.5 parts of white feldspar, 6 parts of this medicine, 5 parts of iron ore, manganese 2 parts powder, 2 parts plant ash, 2 parts copper oxide.

[0024] A preparation method of black gold glaze for Jun porcelain, the steps are as follows:

[0025] S1. Accurately weigh the above components by weight and mix them uniformly to form a mixed solid raw material;

[0026] S2, according to the ratio of mixed solid ball stone: raw material: water = 2: 1.2: 0.9, count respectively into ball mill and mix ball mill to form slurry;

[0027] S3, after ball milling for 12.5 hours, detect the fineness of the slurry;

[0028] S4, sieve the slurry whose fineness is qualified to remove iron, and prepare black gold black glaze.

Embodiment 2

[0030] A black gold glaze for Jun porcelain, which consists of 45 parts by weight of feldspar, 15 parts of quartz, 10 parts of calcite, 5 parts of copper ore, 6 parts of white feldspar, 6 parts of this medicine, 5 parts of iron ore, manganese 2 parts powder, 2 parts plant ash, 3 parts copper oxide.

[0031] A preparation method of black gold glaze for Jun porcelain, the steps are as follows:

[0032] S1. Accurately weigh the above components by weight and mix them uniformly to form a mixed solid raw material;

[0033] S2, according to the ratio of mixed solid ball stone: raw material: water = 2: 1.2: 0.9, count respectively into ball mill and mix ball mill to form slurry;

[0034] S3, after ball milling for 12.5 hours, detect the fineness of the slurry;

[0035] S4, sieve the slurry whose fineness is qualified to remove iron, and prepare black gold black glaze.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a golden black glaze for jun-porcelain and a preparation method of the golden black glaze. The golden black glaze for jun-porcelain comprises the following components in parts by weight: 40 to 50 parts of melilite, 15 to 25 parts of quartz, 10 to 20 parts of calcite, 5 to 10 parts of copper ore, 5 to 10 parts of white feldspar, 5 to 10 parts of Benyao, 5 to 10 parts of ironore, 2 to 4 parts of manganese powder, 2 to 5 parts of plant ash and 2 to 5 parts of copper oxide. The components are accurately weighed in parts by weight and mixed uniformly to form a mixed solid raw material; according to the ratio of mixed solid ball stone, a raw material and water are respectively added into a ball mill according to the ratio of 2:(1.2-1.5):(0.9-1.5) for mixing and ball milling to form slurry; the slurry fineness is detected after the ball milling is performed for 12.5 to 14 hours; and the fineness-qualified slurry is sieved to remove iron, and the golden black glaze is obtained. Compared with the prior art, the preparation process provided by the invention is simple, and a prepared golden black glaze jun-porcelain handicraft is moist and bright in glaze, and has theadvantages of easy dispersibility, strong tinting strength, bright color, high brightness, uniform color and the like.

Description

technical field [0001] The invention relates to the technical field of glaze production, in particular to a black gold glaze for Jun porcelain and a preparation method thereof. Background technique [0002] Jun porcelain is widely used in various fields because of its smoothness, compactness and many other advantages. In the preparation process of Jun porcelain, various low-temperature colors are applied to the pure bottom glaze, and Wujin glaze becomes a variety of beautiful The setting off of color can obtain high-profile and elegant Jun porcelain glaze, but its glaze surface of the Wujin glaze of the prior art is not bright enough. The color is not uniform enough, so it is necessary to design a moist and bright Jun porcelain Wujin glaze on the basis of reproduction technology. Contents of the invention [0003] The purpose of the present invention is to solve the problems mentioned in the above-mentioned background technology, and provide a kind of black gold glaze for...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/00C04B41/86
CPCC03C8/00C04B41/5022C04B41/86C04B41/4539
Inventor 杨鹏飞
Owner 杨鹏飞
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com