A kind of uv-led packaging glue and preparation method thereof

A UV-LED, encapsulating adhesive technology, applied in adhesives, non-polymer adhesive additives, adhesive additives, etc., can solve the problems of low refractive index, easy yellowing, poor anti-vulcanization performance, etc., and achieve high refractive index. rate, good vulcanization resistance, and excellent UV resistance

Active Publication Date: 2021-02-09
广州惠利电子材料有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Traditional silicone packaging materials mainly include methyl silicone and phenyl silicone. Methyl silicone has good heat resistance and UV resistance, but its refractive index is low, and the light extraction efficiency of LED is low. Due to its low hardness, it is resistant to vulcanization Poor performance; phenyl silica gel has high refractive index and high hardness, and has good light extraction efficiency and anti-vulcanization performance, but its temperature resistance and ultraviolet resistance are poor, it is prone to yellowing, and the light decays when it is lit for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of uv-led packaging glue and preparation method thereof
  • A kind of uv-led packaging glue and preparation method thereof
  • A kind of uv-led packaging glue and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] A UV-LED encapsulant, which is made by mixing component A and component B at a mass ratio of 1:1;

[0054] Component A includes the following ingredients:

[0055]

[0056] Component A includes the following ingredients:

[0057] 30g of adamantyl-containing methyl vinyl silicone resin;

[0058] 69.99g of adamantyl-containing methyl hydrogen silicone oil;

[0059] Methylbutynol 0.01g;

[0060] The preparation method of UV-LED encapsulation adhesive in this embodiment comprises the following steps:

[0061] a) Weigh 90g of adamantyl-containing methyl vinyl silicone resin, 5g of polysiloxane-modified nano-cerium oxide (Dongguan Luyue AHR-3), 4.99g of silane coupling agent KH-560 and 0.01g of platinum -Vinylsilane complex catalyst (platinum content: 5000ppm), sequentially added to the vacuum mixer, mixed evenly to obtain A component;

[0062] b) Weigh 30g of adamantyl-containing methyl vinyl silicone resin, 69.99g of adamantyl-containing methyl hydrogen-containing s...

Embodiment 2

[0065] A UV-LED encapsulant, which is made by mixing component A and component B at a mass ratio of 1:1;

[0066] Component A includes the following ingredients:

[0067]

[0068] Component A includes the following ingredients:

[0069] 49.5g of adamantyl-containing methyl vinyl silicone resin;

[0070] 50g of adamantyl-containing methyl hydrogen silicone oil;

[0071] Phenylbutynol 0.5g;

[0072] The preparation method of UV-LED encapsulation adhesive in this embodiment comprises the following steps:

[0073] a) Weigh 97.5g of adamantyl-containing methyl vinyl silicone resin, 1g of polysiloxane-modified nano-cerium oxide (Dongguan Luyue AHR-3), 1g of silane coupling agent KH-561 and 0.5g of platinum -Vinylsilane complex catalyst (platinum content: 5000ppm), sequentially added to the vacuum mixer, mixed evenly to obtain A component;

[0074] b) Weigh 49.5g of adamantyl-containing methyl vinyl silicone resin, 50g of adamantyl-containing methyl hydrogen-containing silicone...

Embodiment 3

[0077] A UV-LED encapsulant, which is made by mixing component A and component B at a mass ratio of 1:1;

[0078] Component A includes the following ingredients:

[0079]

[0080] Component A includes the following ingredients:

[0081] 50g of adamantyl-containing methyl vinyl silicone resin;

[0082] 49.5g of adamantyl-containing methyl hydrogen silicone oil;

[0083] Ethynylcyclohexanol 0.5g;

[0084] The preparation method of UV-LED encapsulation adhesive in this embodiment comprises the following steps:

[0085] a) Weigh 90g of adamantyl-containing methyl vinyl silicone resin, 4.5g of polysiloxane-modified nano-cerium oxide (Dongguan Luyue AHR-3), 5g of silane coupling agent KH-561 and 0.5g of platinum -Vinylsilane complex catalyst (platinum content: 5000ppm), sequentially added to the vacuum mixer, mixed evenly to obtain A component;

[0086] b) Weigh 50g of adamantyl-containing methyl vinyl silicone resin, 49.5g of adamantyl-containing methyl hydrogen-containing ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a UV-LED encapsulant, which is formed by mixing component A and component B at a mass ratio of 1:1; component A includes the following components in parts by mass: adamantyl-containing methyl vinyl 90-98 parts of silicone resin; 0.01-0.5 parts of platinum catalyst; component B includes the following components in parts by mass: 30-50 parts of adamantyl-containing methyl vinyl silicone resin; adamantyl-containing methyl hydrogen-containing silicone oil 50-70 copies. Select specific average molecular formula of adamantane-containing methyl vinyl silicone resin and adamantyl-containing methyl hydrogen-containing silicone oil as base glue, and react under the catalysis of platinum catalyst to obtain encapsulation glue. Compared with the prior art , The encapsulation adhesive of the present invention has a relatively high refractive index, good anti-vulcanization performance, and excellent ultraviolet resistance performance.

Description

technical field [0001] The invention belongs to the field of LED packaging, and in particular relates to a UV-LED packaging glue and a preparation method thereof. Background technique [0002] UV-LED is a kind of LED, which emits invisible light of a single wavelength, generally below 400nm. Compared with traditional mercury lamps, UV-LED has the characteristics of energy saving, less heat loss, long life, and concentrated wavelength. It is a new type of environmentally friendly light source and is widely favored by the market. At present, the packaging of UV-LEDs mainly follows the packaging method of white LEDs, and silicone resin is still used as the packaging material. However, due to the shorter wavelength and higher radiation energy of UV-LEDs, there are higher requirements for the performance of packaging materials. . [0003] Traditional silicone packaging materials mainly include methyl silicone and phenyl silicone. Methyl silicone has good heat resistance and UV ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J183/07C09J183/05C09J11/04
CPCC08K2003/2213C08K2201/011C08L2201/08C08L2203/206C08L2205/025C09J11/04C09J183/04C08L83/04C08K9/08C08K3/22
Inventor 韩小兵谢继鹏郑长利黄仁杰
Owner 广州惠利电子材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com