Preparation method of a one-pass foaming two-pass frosted surface glove

A matte surface and glove technology, used in household components, household appliances, other household appliances, etc., can solve the problems of insufficient grip, low friction, rigidity, etc., to achieve good protection, improve friction, and good grip. Effect

Pending Publication Date: 2018-11-16
SHANDONG XINGYU GLOVES
View PDF11 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Existing nitrile gloves and latex gloves are widely used in industries such as petrochemical industry, paint printing, agriculture and animal husbandry, and automobile machinery maintenance; When it is used for work in contact with liquids, because the rubber surface is too smooth, there are defects such as low friction, insufficient grip, stiff use, etc., and when the palm is sweaty and airtight when used for a long time, the user feels uncomfortable during use.
Because latex is characterized by softness and wear resistance, it has a wide range of applications, but in terms of the rubber content used for dipping gloves, the latex gloves are very hard to wear due to the addition of calcium carbonate, and the use of gloves is not dexterous and comfortable.
Such as Chinese patent publication number is CN1596786A, discloses a kind of manufacture method of nano-calcium carbonate latex gloves, and it adds and disperses a certain amount of nano-calcium carbonate together with conventional ingredients together in natural latex, and then dips and makes by conventional molding process. Latex gloves containing nano-calcium carbonate are made into latex gloves, and then the finished product is obtained through the processes of flipping, chlorination, foam washing, rinsing, and drying. The active interaction force between nano-calcium carbonate and the polymer makes the polymer particles more tightly packed , but in the process of use, its softness decreases and there is rigidity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of a one-pass foaming two-pass frosted surface glove
  • Preparation method of a one-pass foaming two-pass frosted surface glove
  • Preparation method of a one-pass foaming two-pass frosted surface glove

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A kind of preparation method of the acrylonitrile-butadiene glove that one time foaming fully dips twice frosted surface, concrete steps are as follows:

[0037] (1) Raw materials: pre-vulcanized carboxylated nitrile latex, thickener, potassium ricinoleate, Glauber's salt, KOH, sodium dodecylbenzenesulfonate, etc.;

[0038] (2) Glue adjustment:

[0039] For the first impregnating glue, the mass ratio of the glue is as follows, so that the foaming ratio can reach 1.5 times,

[0040]

[0041] The second dipping glue, the quality ratio of the glue material is as follows

[0042]

[0043] (3) Preheating: put the glove embryo on the hand mold, and preheat the hand mold, soak the coagulant (methanol: calcium nitrate by mass ratio is 100:2), after 30 seconds of uniform solution, the glove embryo is fully immersed for the first time Dipping glue, then dipping in the second coagulant (water: calcium chloride is 100:15 by mass ratio), after 5 minutes of uniform solution, ...

Embodiment 2

[0049] A kind of preparation of the nitrile gloves of once foaming and semi-immersing twice frosted surface, concrete steps are as follows:

[0050] (1) Raw materials: pre-vulcanized carboxylated nitrile latex, thickener, potassium oleate, sodium chloride, KOH, polyoxyethylene alkyl ether, etc.;

[0051] (2) Glue adjustment:

[0052] For the first impregnating glue, the mass ratio of the glue is as follows, so that the foaming ratio can reach 1.1 times,

[0053]

[0054] The second dipping glue, the quality ratio of the glue material is as follows

[0055]

[0056]

[0057] (3) Preheating: put the glove embryo on the hand mold, preheat the hand mold, soak the coagulant (ethanol: calcium nitrate in a mass ratio of 100:3), and soak the palm of the glove embryo after 30 seconds. , the back of the hand is dipped in half of the first dipping glue, and then soaked in the second coagulant (ethanol: calcium chloride is 100:18 by mass ratio), and after 4 minutes of uniform s...

Embodiment 3

[0063] A kind of latex glove preparation that foams once and fully soaks frosted surface twice, concrete steps are as follows:

[0064] (1) Material preparation: pre-vulcanized natural rubber latex, thickener, detergent, Glauber's salt, KOH, sodium dodecylbenzenesulfonate, etc.;

[0065] (2) Glue adjustment:

[0066] The first impregnation glue, its glue material is prepared according to the following mass parts, so that the foaming multiple can reach 1.4 times,

[0067]

[0068] The second impregnating glue, the quality ratio of the glue is as follows

[0069]

[0070] (3) Preheating: put the glove embryo on the hand mold, and preheat the hand mold, soak the first coagulant (methanol: calcium nitrate by mass ratio is 100:3), after 30 seconds, the glove embryo is fully immersed The first dipping glue, and then dipping the second coagulant (methanol: calcium chloride is 100:5 by mass ratio), and after 5 minutes of uniform solution, the glove palm is soaked in the second...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
quality scoreaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of a one-pass foaming two-pass frosted surface glove. The preparation method comprises the following steps of S1, sleeving the glove blank on the hand mold, preheating the hand mold and soaking the coagulator, dipping the first impregnating adhesive and then dipping the coagulating agent, and then dipping the second impregnating adhesive, wherein the first impregnating adhesive is a foaming adhesive added with a physical foaming agent, and the second impregnating adhesive contains a surfactant; S2, spraying frosted particles; S3, pre-drying; S4, washing the glove with water; and S5, vulcanizing to obtain a one-pass foamed two-pass frosted surface glove. The glove prepared by the method is light, sensitive, soft and comfortable, provides good protection, and has the advantages of being breathable, excellent in grabbing force and the like, the safety of a user in the working process can be better protected.

Description

technical field [0001] The invention relates to a method for preparing gloves with a frosted surface foamed once and twice, and belongs to the technical field of labor protection products. Background technique [0002] Make gloves with cloth or yarn, soak the gloves in the prepared glue (such as nitrile, natural latex, etc.) for a moment, take them out and dry them to form rubber gloves, also known as dipped gloves , Hanging gloves, rubber gloves. [0003] Existing nitrile gloves and latex gloves are widely used in industries such as petrochemical industry, paint printing, agriculture and animal husbandry, and automobile machinery maintenance; When it is used for work in contact with liquids, because the rubber surface is too smooth, there are defects such as low friction, insufficient grip, stiff use, etc., and when the palm is sweaty and airtight when used for a long time, the user feels uncomfortable during use. . Because the characteristics of latex are soft and wear-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B29C41/20B29C41/34B29C44/02B29L31/48
CPCB29C41/20B29C41/34B29C44/02B29L2031/4864
Inventor 周星余王垂文
Owner SHANDONG XINGYU GLOVES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap