Graphene efficient air purifier filter material and preparation method

A high-efficiency air and graphene technology, applied in chemical instruments and methods, botanical equipment and methods, separation methods, etc., can solve the problems that graphene oxide sheets are easy to agglomerate and cannot directly apply air filters, etc., and achieve strong adsorption capacity , the effect of prolonging the service life

Inactive Publication Date: 2018-11-13
JINAN JIAXING TECH
View PDF11 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, graphene oxide sheets are easy to agglomerate and cannot be directly applied to air filters

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A graphene high-efficiency air purifier filter material, comprising modified loofah and graphene materials, 100 parts by mass of modified loofah and 20 parts by mass of graphene.

[0023] Specifically, the filter material also includes 2 parts by mass of nano catalytic material, and the nano catalytic material is TiO 2 .

[0024] Specifically, the graphene material is graphene.

[0025] A method for preparing graphene high-efficiency air purifier filter material, including:

[0026] D1 Preparation of modified loofah

[0027] Select 100g of naturally aged loofah, peel off the outer skin and remove the inner flesh. Shear into multiple round slices with a diameter of 2.5cm and a thickness of 2-5mm. Then put them in boiling water and boil for 30 minutes, then take them out and rinse them with distilled water. Clean, put it in a 30% NaOH solution, add a certain amount of ethanol or propanol to make the mass of ethanol or propanol 20%, basify at room temperature for 72 hours, and then...

Embodiment 2

[0035] A graphene high-efficiency air purifier filter material includes modified loofah and graphene materials, 100 parts by mass of modified loofah and 30 parts by mass of graphene.

[0036] Specifically, the filter material further includes 2 parts by mass of nano catalytic material, and the nano catalytic material is TiO 2 .

[0037] Specifically, the graphene material is a mixture of graphene oxide and graphene.

[0038] A method for preparing graphene high-efficiency air purifier filter material, including:

[0039] D1 Preparation of modified loofah

[0040] Select 100g of naturally aged loofah, peel off the outer skin and remove the inner flesh. Shear into multiple round slices with a diameter of 2.5cm and a thickness of 2-5mm. Then put them in boiling water and boil for 30 minutes, then take them out and rinse them with distilled water. Clean, put it into a 30% NaOH solution, add a certain amount of ethanol or propanol to make the mass of ethanol or propanol 20%, basify at room ...

Embodiment 3

[0048] A graphene high-efficiency air purifier filter material, comprising modified loofah and graphene materials, 100 parts by mass of modified loofah and 23 parts by mass of graphene.

[0049] Specifically, the filter material further includes 4 parts by mass of nano catalytic material, and the nano catalytic material is TiO 2 .

[0050] Specifically, the graphene material is graphene oxide.

[0051] A method for preparing graphene high-efficiency air purifier filter material, including:

[0052] D1 Preparation of modified loofah

[0053] Select 100g of naturally aged loofah, peel off the outer skin and remove the inner flesh. Shear into multiple round slices with a diameter of 2.5cm and a thickness of 2-5mm. Then put them in boiling water and boil for 30 minutes, then take them out and rinse them with distilled water. Clean, put it in a 30% NaOH solution, add a certain amount of ethanol or propanol to make the mass of ethanol or propanol 20%, basify at room temperature for 56 hours,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a graphene efficient air purifier filter material and a preparation method. The graphene efficient air purifier filter material is prepared from 100 parts by mass of modifiedloofah sponge, and 20-30 parts by mass of a graphene material. The filter material is further prepared from 2-5 parts by mass of a nano catalytic material. The preparation method comprises the following steps: preparing the modified loofah sponge, preparing graphene material dispersion liquid, and preparing the graphene filter material. According to the prepared air purifier filter material, a vascular bundle of the used loofah sponge has the elasticity, has a network gap, and is capable of achieving a support function to the graphene material. The graphene material attached to the loofah sponge is self-assembled to form an aerogel structure which can realize the sterilizing anti-bacterial effects. The nano photocatalytic material wrapped in graphene aerogel is capable of degrading organicpollutants of formaldehyde and methyl orange and the like under the photocatalytic effect, and in the case of guaranteeing the filtering effect, effectively prolonging the service life of the filtermaterial.

Description

Technical field [0001] The invention relates to the field of air purification materials, in particular to a graphene high-efficiency air purifier filter material and a preparation method. Background technique [0002] Some existing air filters have at least 3 layers of filters, which are pre-filters, activated carbon filters, and dust-collecting filters (HEPA filters). The pre-filters are newly developed micro-mesh dust filters. Net, the mesh area is smaller than normal, in addition to adsorbing small dust particles, it also effectively removes hair. The surface is cleaned with a fluoxone treatment, and the dust on the surface of the filter screen can be more easily cleaned; activated carbon is a black amorphous granular or fine powder. In air purifier products, they generally exist in the form of particles. Activated carbon particles have a large surface area, and there are abundant micropores all over the body. Its chemical properties determine that it has a strong adsorption...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J20/24B01J20/28B01J20/30B01J31/26B01J31/38B01D53/02B01D53/86B01D53/72A01N59/00A01P3/00A01P1/00
CPCB01D53/02B01D53/8668B01J20/20B01J20/24A01N59/00B01J20/28047B01J31/26B01J31/38B01D2257/7027B01D2257/91B01D2257/70B01J35/39
Inventor 车春玲
Owner JINAN JIAXING TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com