A method for preparing sodium metatitanate-potassium tetratitanate composite catalytic material by molten salt method

A technology of potassium tetratitanate and sodium metatitanate, applied in chemical instruments and methods, heterogeneous catalyst chemical elements, physical/chemical process catalysts, etc., can solve problems such as high yield, high cost, and danger , to achieve the effect of excellent catalytic performance, low cost and high product yield

Inactive Publication Date: 2020-10-09
CHINA UNIV OF GEOSCIENCES (BEIJING)
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method has a high yield and can obtain whiskers with relatively large diameter lengths, but it needs to strictly control parameters such as temperature, alkalinity, and reaction time, and is costly and dangerous.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for preparing sodium metatitanate-potassium tetratitanate composite catalytic material by molten salt method
  • A method for preparing sodium metatitanate-potassium tetratitanate composite catalytic material by molten salt method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0039] Example: Slowly mix 5ml of acetic acid solution with 2ml of tetrabutyl titanate under stirring, continue to stir for 30 minutes, carry out hydrothermal reaction at 150°C for 24h, and vacuum-dry the sample after centrifugation at 60°C to obtain TiO 2 Precursor samples.

[0040] Then TiO2 Precursor sample, NaNO 3 and KNO 3 Mix evenly at a mass ratio of 5:1:1, calcinate at 350°C for 4 hours, wash and dry thoroughly, and then the composite catalytic material of sodium metatitanate-potassium tetratitanate can be obtained.

[0041] Prepared sodium metatitanate-potassium tetratitanate composite catalytic material (see figure 1 ), which is nanoribbon-shaped, with smooth surface and clear edges and corners, with a length of about 6-13 microns and a width of about 200 nanometers (see figure 2 ).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
widthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing sodium metatitanate-potassium tetratitanate composite catalytic material using a molten salt method using mixed nitrate as a co-solvent, and belongs to the technical field of material preparation. The present invention uses tetrabutyl titanate as raw material and prepares TiO by hydrothermal method. 2 The material precursor is then added with mixed nitrate as a cosolvent, and the sodium metatitanate-potassium tetratitanate composite catalytic material is prepared through the nitrate molten salt method. This method has the advantages of simple and controllable preparation conditions, simple equipment and process, large output, and low cost. The obtained product is a nanoribbon with a length of 6-13 microns and a width of about 200 nanometers. It has broad application prospects in photocatalytic degradation of pollutants and photocatalytic hydrogen production.

Description

technical field [0001] The invention relates to a method for preparing a sodium metatitanate-potassium tetratitanate composite catalytic material by a melting method, and belongs to the technical field of material preparation. Background technique [0002] Titanate is a kind of semiconductor layered metal compound with high photocatalytic activity discovered so far. It has attracted extensive research attention because of its good photocorrosion resistance and high activity. The laminate framework of layered titanates is composed of octahedral TiO 6 They are connected to each other in a way of sharing edges or corners, and spread to form a negatively charged two-dimensional layered oxide, and the negatively charged layers contain alkali metal cations. Alkali metal cations have interlayer ion exchange performance, excellent adsorption performance and high chemical activity. In addition, the layered structure can maintain good stability during ion exchange, and can absorb ha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/04
CPCB01J23/002B01J23/04B01J2523/00B01J35/39B01J35/40B01J2523/12B01J2523/13B01J2523/47
Inventor 赵增迎李晨曦彭志坚
Owner CHINA UNIV OF GEOSCIENCES (BEIJING)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com