[0006] The purpose of the present invention is to provide a concrete internal and external moisture migration inhibitor for the problem of concrete moisture migration in the plastic stage, hardening stage and post-hardening stage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of moisture migration inhibitor inside and outside concrete
  • A kind of moisture migration inhibitor inside and outside concrete

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The moisture migration inhibitor inside and outside the concrete of the present invention is prepared by the following method from raw materials muscovite powder, mordenite and kaolin:

[0023] (1) Substrate preparation: Grind the commercially available muscovite powder to 400 mesh, dry it for later use; grind the commercially available natural mordenite to 300 mesh, and the ammonium absorption value is not less than 130mmol / 100g; commercially available Kaolin is calcined at 750°C~800°C and ground to a fineness of 500 mesh, of which SiO 2 The content is not less than 50%, Al 2 o 3 The content is not less than 40%, and the specific surface area is not less than 15000m2 2 / kg. Take 60g of mica powder, 10g of zeolite powder, and 30g of kaolin powder after the above-mentioned treatment, and mix them uniformly in a high-speed powder mixer to prepare a base material;

[0024] (2) Ultrasonic treatment: Take 50g of the base material, add it into the mixture of isopropanol a...

Embodiment 2

[0029] The moisture migration inhibitor inside and outside the concrete of the present invention is prepared by the following method from raw material muscovite powder and mordenite:

[0030] (1) Substrate preparation: commercially available muscovite powder is ground to 400 mesh, dried for later use; commercially available natural mordenite is ground to 300 mesh, and the ammonium absorption value is not less than 130mmol / 100g. Take 70g of treated mica powder and 30g of zeolite powder, mix them evenly in a high-speed powder mixer, and prepare them as substrates;

[0031] (2) Ultrasonic treatment: Take 50g of the base material, add it into the mixture of isopropanol and n-butanol (volume ratio 1:1), ultrasonically treat for 10min, and then magnetically stir for 10min;

[0032] (3) Modification treatment: Slowly add 4ml of KH-550 silane coupling agent with a pipette gun under the state of magnetic stirring, and continue to stir for 30 minutes; appropriately increase the speed of...

Embodiment 3

[0036]The moisture migration inhibitor inside and outside the concrete of the present invention is prepared by the following method from raw material muscovite powder and commercially available kaolin:

[0037] (1) Substrate preparation: commercially available muscovite powder, ground to 1000 mesh, dried for later use; commercially available kaolin was calcined at 750°C to 800°C, and ground to a fineness of 500 mesh, of which SiO 2 The content is not less than 50%, Al 2 o 3 The content is not less than 40%, and the specific surface area is not less than 15000m2 2 / kg. Take 50g of mica powder and 50g of kaolin powder after the above treatment, and mix them uniformly in a high-speed powder mixer to prepare a base material;

[0038] (2) Ultrasonic treatment: Take 50g of the base material, add it into the mixture of isopropanol and n-butanol (volume ratio 1:1), ultrasonically treat for 10min, and then magnetically stir for 10min;

[0039] (3) Modification treatment: Slowly add...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
porosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an inhibitor of moisture migration inside and outside concrete. The preparation method comprises the following steps: firstly subjecting phlogopite powder / muscovite powder, clinoptilolite / mordenite powder and kaolin powder to special treatment; The ratio of ~30:0~50 is mixed evenly, and the mixture of isopropanol and n-butanol is added for ultrasonic treatment; under magnetic stirring, an appropriate amount of silane coupling agent is added, and an appropriate amount of distilled water is slowly added below the liquid surface of the solution, and formazan is added slowly and uniformly. base silicone oil modifier, magnetically stirred for 1 hour; dry, grind and sieve the slurry to obtain the finished product of moisture migration inhibitor. The water migration inhibitor prepared by the invention has low cost of raw materials, simple preparation method and outstanding water blocking effect.

Description

technical field [0001] The invention relates to a concrete admixture, in particular to an inhibitor of moisture migration inside and outside concrete in the plastic stage, hardening stage and post-hardening stage. Background technique [0002] During the construction process, the process of concrete from adding water to mixing can be divided into three stages: plastic stage, hardening stage and post-hardening stage. The concrete in the plastic stage must meet the workability requirements, the concrete in the hardening stage must meet the requirements of continuous strength growth and crack resistance, and the concrete in the hardened stage must meet the requirements of strength and durability. Therefore, the improvement of concrete performance should be considered around the whole life process of concrete. [0003] After concrete is poured, due to bleeding and poor humidity, the internal moisture evaporates into the air. If the moisture volatilization rate of the concrete ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B24/42
CPCC04B40/0042C04B14/20C04B14/047C04B14/106C04B24/026C04B24/42C04B2103/0083C04B2103/65C04B2111/00275C04B2111/27C04B24/02C04B20/023C04B20/04C04B14/041C04B14/042C04B14/045C04B40/0046
Inventor 张金良苏茂林尚宏琦吴法辰景来红毛文然杨林陈学理
Owner YELLOW RIVER ENG CONSULTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com