Water-based resin sand for stone-like coating and preparation method of water-based resin sand

A technology of water-based resin and real stone paint, applied in the direction of coating, can solve the problems of water-based resin sand preparation method of real stone paint, lack of acid and alkali resistance, etc., to reduce the surface energy of the coating, the product is beautiful, and the implementation cost is low. Effect

Pending Publication Date: 2018-07-27
HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] At present, there is a lack of a kind of water-based resin sand and preparation method thereof for acid and alkali-resistant good real stone paint

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based resin sand for stone-like coating and preparation method of water-based resin sand
  • Water-based resin sand for stone-like coating and preparation method of water-based resin sand
  • Water-based resin sand for stone-like coating and preparation method of water-based resin sand

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of water-based resin sand for real stone paint of the present invention, said water-based resin sand for real stone paint comprises the following components in parts by mass:

[0028]

[0029]

[0030] The water-based hydroxyacrylic resin is the high-gloss hydroxyacrylic dispersion A2033 of Wanhua Chemical.

[0031] Described waterborne amino resin is Cytec 303. The silane coupling agent is an aqueous silane coupling agent. The described water-based silane coupling agent is A-1100 American United Carbon. The water-based inorganic color paste is Clariant's color paste series.

[0032] The preparation method of water-based resin sand for genuine stone paint of the present invention comprises the following steps:

[0033] (1) Each component is weighed according to the stated parts by mass, the water-based hydroxyacrylic resin and the water-based amino resin are mixed first, then water is added, and stirred for 5 minutes at a speed of 500r / min;

[0034] (2)...

Embodiment 2

[0038] The difference between embodiment 2 and embodiment 1 is:

[0039] A kind of water-based resin sand for real stone paint of the present invention, said water-based resin sand for real stone paint comprises the following components in parts by mass:

[0040]

[0041]

[0042] The water-based hydroxyacrylic resin is the high-gloss hydroxyacrylic dispersion A2033 of Wanhua Chemical.

[0043] The water-based amino resin is a combination of fully etherified amino resin Taiwan Changchun MR603 and Cytec 303.

[0044] The preparation method of water-based resin sand for genuine stone paint of the present invention comprises the following steps:

[0045] (1) Each component is weighed according to the stated parts by mass, the water-based hydroxyacrylic resin and the water-based amino resin are mixed first, then water is added, and stirred for 5 minutes at a speed of 500r / min;

[0046] (2) The silane coupling agent is added to the mixed solution of step (1), and stirred at...

Embodiment 3

[0050] The difference between embodiment 3 and embodiment 1 is:

[0051] A kind of water-based resin sand for real stone paint of the present invention, said water-based resin sand for real stone paint comprises the following components in parts by mass:

[0052]

[0053]

[0054] The water-based amino resin is fully etherified amino resin Taiwan Changchun MR603.

[0055] The preparation method of water-based resin sand for genuine stone paint of the present invention comprises the following steps:

[0056] (1) Each component is weighed according to the stated parts by mass, the water-based hydroxyacrylic resin and the water-based amino resin are mixed first, then water is added, and stirred for 5 minutes at a speed of 500r / min;

[0057] (2) The silane coupling agent is added to the mixed solution of step (1), and stirred at a speed of 500r / min for 3 minutes for subsequent use;

[0058] (3) Stir the quartz sand at a rate of 200r / min, then add the mixed solution prepare...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses water-based resin sand for a stone-like coating and a preparation method of the water-based resin sand. The water-based resin sand for the stone-like coating is prepared from components in parts by mass as follows: 90-97 parts of quartz sand, 1-3 parts of water-based inorganic color paste, 1-2 parts of water, 2-2.5 parts of a water-based curing agent, 0.2-0.5 parts of a silane coupling agent, 3-4 parts of water-based hydroxyl acrylic resin and 0.5-0.8 parts of water-based amino resin. The water-based resin sand is simple, attractive, good in acid and alkali resistance,good in weatherability, low in implementation cost, energy-saving, environmentally friendly and good in solvent resistance and friction resistance.

Description

technical field [0001] The invention relates to the field of coatings, in particular to water-based resin sand for real stone paint and a preparation method thereof. Background technique [0002] Environmental pollution refers to natural or man-made destruction, adding certain substances to the environment and exceeding the self-purification ability of the environment to cause harm. Or due to human factors, the environment is polluted by harmful substances, which will adversely affect the growth and reproduction of organisms and the normal life of human beings. Due to human factors, the composition or state of the environment changes, and the quality of the environment declines, thereby disturbing and destroying the normal production and living conditions of the ecological system and human beings. [0003] Particulate pollutants in the air are large in number and complex in composition, and they can be carriers of toxic substances or other pollutants. It mainly comes from ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D7/61C09D7/65C09D7/63
Inventor 戴国军胡中源董立志
Owner HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap