Online minor repair method for 300/380KA large-scale prebake cells

A 380KA, pre-baked tank technology, applied in the electrolysis process, electrolysis components, etc., can solve the problems of chemical and electrochemical corrosion, damage of cathode carbon lining, damage of cathode carbon lining, etc., to protect the environment and prolong the service life , The effect of saving repair costs

Inactive Publication Date: 2018-07-20
张帝
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the production process of aluminum electrolysis, there are many reasons for the damage of the lining of the electrolytic cell. For example, the temperature gradient is too large during the firing start-up and operation of the aluminum electrolytic cell, and the tank temperature is unstable, which causes the internal stress of the cathode lining to locally generate cracks and fall off. The thermal expansion and contraction of the cathode carbon block do not match the expansion after heating; the current distribution is uneven; the metal sodium forms a stable intercalation compound with the cathode carbon lining through the interface reaction, because its lattice is larger than the carbon lattice size. The local expansion of the lining generates internal stress, which leads to damage to the carbon lining of the cathode; at high temperature, metal aluminum and carbon are formed by the interaction, resulting in chemical and electrochemical corrosion, which damages the carbon lining of the cathode, etc. But the shutdown repair is too big a loss for the enterprise

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Online minor repair method for 300/380KA large-scale prebake cells
  • Online minor repair method for 300/380KA large-scale prebake cells

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Example 1: The foundation of an aluminum electrolysis work area has unbalanced settlement, and the settlement of the side B of the aluminum outlet end of the 2139# prebaking tank is more serious. The corner block and the adjustment block cause the insulation failure of the pre-baked tank body, the corner block is connected to the shell of the pre-baked tank for conduction, and the corner side block breaks down (from the cleaning site, the shell of the pre-baked tank comes out of the aluminum end B There are three vertical electric shock holes on the contact surface of the side corners, with a diameter of about 10mm. The side blocks at the breakdown site are all graphite side blocks, which have good electrical conductivity) and are damaged, resulting in damage to the tank shell.

[0023] In order to quickly repair the prebaked tank, the method adopted includes the following steps:

[0024] 1) When it is found that the side of the pre-baking tank has a red furnace or a fu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an online minor repair method for 300 / 380KA large-scale prebake cells. The method comprises the following steps of: when lining damage or red furnace or furnace leakage occursat the side part of a prebake cell, pulling out an anode carbon block at a leakage point in time without stopping the cell; encircling the periphery of the leakage point by molten aluminum and liquidelectrolyte through a mixture of electrolyte and aluminum oxide; cooling the outer side of the cell shell leakage point of the prebake cell via blowing by using compressed air; when the temperature islower than 150 DEG C, starting to clean the inner side of the leakage point to ensure that the bottom is flat and the vertical face is straight; cleaning the residual materials, cooling via blowing by using compressed air, when the temperature is reduced to 100 DEG C, paving a thickener and carrying out compaction, constructing an anode carbon block at the top of the thickener, and tamping aluminum oxide between the lateral anode carbon block and the cell shell; after the repair, carrying out baking for 24, and mounting the pulled anode carbon block. According to the method, rapid repair is carried out in a shortest time without stopping the cell, so that large-area molten aluminum leakage caused by untimely processing is prevented from thrusting buses around the cell and then influencingthe safe operation of electrolytic series.

Description

technical field [0001] The invention relates to a maintenance method for an aluminum electrolysis electrolytic cell, in particular to an online minor repair method for a 300 / 380KA large prebaked cell. Background technique [0002] In the production process of aluminum electrolysis, there are many reasons for the damage of the lining of the electrolytic cell. For example, the temperature gradient is too large during the firing start-up and operation of the aluminum electrolytic cell, and the tank temperature is unstable, which causes the internal stress of the cathode lining to locally generate cracks and fall off. The thermal expansion and contraction of the cathode carbon block do not match the expansion after heating; the current distribution is uneven; the metal sodium forms a stable intercalation compound with the cathode carbon lining through the interface reaction, because its lattice is larger than the carbon lattice size. The local expansion of the lining generates i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C25C7/06C25C3/08
CPCC25C7/06C25C3/08
Inventor 张帝
Owner 张帝
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products