Silicon amorphous refractory hot patching material

A refractory material and heat repair technology, which is used in the maintenance of the melting damaged parts of silica brick refractory brick materials and the internal field of high-temperature kilns, can solve the problems of jumping fire, kiln combustion heat loss, bursting defects of refractory bricks, etc., and achieves the operation steps. Simple and convenient, save energy loss, good thermal shock stability

Inactive Publication Date: 2018-07-03
武汉重远炉窑工程技术服务有限公司
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Many parts of the high-temperature kiln are made of silica bricks, and in high-temperature production, the refractory bricks inside the kiln are due to various reasons during the production process of the kiln (such as misuse of the kiln by the operator of the company, kiln Due to the erosion and erosion of the burning flame in the furnace, the sudden cooling and rapid heating of the internal temperature of the kiln after the cessation of fire and cooling, the rapid cooling and rapid heating of the internal temperature, and the erosion of the internal acid-base gas formed in the raw material process of the production of products, etc., the refractory bricks built by the kiln will all appear. Different degrees of melting loss, bursting defects, etc.), the damage of refractory bricks inside the kiln gradually evolves, which will affect the overall service life of the kiln in the later stage
[0004] After the above conditions occur, the refractory bricks inside the kiln will burst into flames after being damaged. After this phenomenon occurs, the internal temperature of the kiln will radiate to the outside, which will not only cause the loss of burning heat of the kiln, but also affect the external operation of the kiln. The working environment of personnel has also become worse. More importantly, the fire on the outer wall of the kiln will cause safety hazards to the steel structure, columns and other supports outside the kiln.
If left untreated it will burn out the external steel structure

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] The technical solutions in the embodiments of the present invention will be clearly and completely described below. Obviously, the described embodiments are only some of the embodiments of the present invention, but not all of them. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0029] An embodiment of the present invention provides a hot-filling material for a siliceous amorphous refractory material. The hot-filling material for a siliceous amorphous refractory material is formed by mixing fused silica particles and a silica sol liquid. In this preferred embodiment, the mass concentration of silica sol in the silica sol liquid is 40%.

[0030] Among them, the fused silica particles are composed of the following components according to the mass ratio:

[0031] Fused silica sand with particle size of 0.3~...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a silicon amorphous refractory hot patching material. The silicon amorphous refractory hot patching material is prepared by mixing fused quartz particles with silica sol liquid, wherein the fused quartz particles contains the following components in percentage by weight: 4%-6% of fused quartz sand with a particle size of 0.2mm-0.3mm, 18%-22% of fused quartz powder with theparticle size of 0.065mm-0.075mm and 72%-78% of fused quartz powder with the particle size of 0.035mm-0.04mm. Damaged parts with all kinds of shapes and specification of a kiln and fused parts in allsizes can be patched by virtue of the silicon amorphous refractory hot patching material from, and the damaged parts and the fused parts are firm and compact after being patched.

Description

technical field [0001] The invention relates to a silicon amorphous refractory hot-filling material, which is applied to the maintenance of the interior of a high-temperature kiln and the melted part of a silica brick refractory material. Background technique [0002] At present, in the production process of high-temperature kilns built with refractory bricks, silicon refractory bricks are widely used due to their economical applicability. [0003] Many parts of the high-temperature kiln are made of silica bricks, and in high-temperature production, the refractory bricks inside the kiln are due to various reasons during the production process of the kiln (such as misuse of the kiln by the operator of the company, kiln Due to the erosion and erosion of the burning flame in the furnace, the sudden cooling and rapid heating of the internal temperature of the kiln after the cessation of fire and cooling, the rapid cooling and rapid heating of the internal temperature, and the er...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/66
CPCC04B35/66
Inventor 任重李乐华刘磊
Owner 武汉重远炉窑工程技术服务有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products