Composite phase change material package and preparation method thereof

A composite phase change material and phase change material technology, applied in the field of composite phase change material package and its preparation, can solve the problems of low heat conduction efficiency and easy leakage, etc., and achieve the effects of reducing environmental pollution, prolonging service life, and being convenient to use

Active Publication Date: 2021-03-02
BEIJING NAT BATTERY TECH
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The first purpose of the present invention is to provide a composite phase change material package to alleviate the technical problems of low heat conduction efficiency and easy liquid leakage after the metal foam and phase change material are combined in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] The present embodiment is a kind of composite phase change material package, which is obtained by vacuum sealing the composite phase change material with an aluminum-plastic film, wherein the composite phase change material is a copper foam layer and a graphene layer alternately arranged in a layered structure, the described The copper foam metal layer contains paraffin, and the outermost layer of the composite phase change material is a graphene layer, that is, both sides of the composite phase change material are provided with graphene layers. Among them, there are 3 layers of copper foam metal layers, and 4 layers of graphene layers. The thickness of each layer of foamed copper metal layer is 0.3cm. The thickness of each graphene metal layer is 0.1 cm. The weight percentage of the phase change material in the foamed copper metal layer is 82%.

Embodiment 2

[0050] The present embodiment is a kind of composite phase change material package, which is obtained by vacuum sealing the composite phase change material with an aluminum-plastic film, wherein the composite phase change material is a copper foam layer and a graphene layer alternately arranged in a layered structure, the described The foamed copper metal layer contains stearic acid, and the outermost layer of the composite phase change material is a graphene layer, that is, both sides of the composite phase change material are provided with graphene layers. Among them, the copper foam metal layer is 4 layers, and the graphene layer is 5 layers. The thickness of each layer of foamed copper metal layer is 0.6cm. The thickness of each graphene metal layer is 0.2 cm. The weight percentage of the phase change material in the foamed copper metal layer is 84%.

Embodiment 3

[0052] The present embodiment is a kind of composite phase change material package, which is obtained by vacuum sealing the composite phase change material with an aluminum-plastic film, wherein the composite phase change material is a copper foam layer and a graphene layer alternately arranged in a layered structure, the described The copper foam metal layer contains lauric acid, and the outermost layer of the composite phase change material is a graphene layer, that is, both sides of the composite phase change material are provided with graphene layers. Among them, the copper foam metal layer is 4 layers, and the graphene layer is 5 layers. The thickness of each layer of foamed copper metal layer is 0.8cm. The thickness of each graphene metal layer is 0.3 cm. The weight percentage of the phase change material in the foamed copper metal layer is 86%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a composite phase-change material package and a preparation method thereof, relating to the field of phase-change materials. The composite phase-change material package is obtained by vacuum-sealing the composite phase-change material with an aluminum-plastic film, and the composite phase-change material includes layers Metal foam layers and graphene layers arranged alternately in the structure, the metal foam layers contain phase change materials. The use of the composite phase change material package can alleviate the technical problems of low heat conduction efficiency and easy liquid leakage after the metal foam and phase change material are combined in the prior art, and achieve the purpose of improving heat conduction efficiency and reducing leakage.

Description

technical field [0001] The invention relates to the technical field of phase change materials, in particular to a composite phase change material package and a preparation method thereof. Background technique [0002] Phase change materials are a general term for substances that use the massive endothermic and exothermic effects of materials during the phase change process for energy storage and temperature regulation. Phase change materials are widely used in building energy saving, road traffic, modern agricultural greenhouses, solar energy utilization, food refrigeration and transportation, medical care, electronic equipment heat dissipation, athletes cooling and warm clothing, special temperature control clothing, aerospace technology, military infrared camouflage, power transfer There are broad application prospects in many fields such as peak filling and valley filling, industrial waste heat storage and utilization, and heat energy recovery. [0003] With the continuo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B15/04C09K5/06B32B15/20B32B15/08B65D30/02C23C16/26
CPCB32B15/043B32B15/08B32B15/20B65D31/00C09K5/063C23C16/26
Inventor 于强罗洪旭孙高峰李卓杨广敏
Owner BEIJING NAT BATTERY TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com