A kind of controllable preparation method of monodisperse copper oxalate powder

A copper oxalate, monodisperse technology, applied in the preparation of carboxylates, carboxylates, chemical instruments and methods, etc., can solve the problems of easy agglomeration of amorphous precipitated particles, difficult to control the shape well, and difficult to disperse.

Active Publication Date: 2020-11-17
UNIV OF SCI & TECH BEIJING
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, copper oxalate is a crystalline substance, and its precipitated crystal morphology is easy to control, while copper hydroxide and basic copper carbonate are mostly amorphous, and the shape is difficult to control well. What is more fatal is that amorphous precipitated particles are easier to agglomerate and difficult to control. separate, separate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of controllable preparation method of monodisperse copper oxalate powder
  • A kind of controllable preparation method of monodisperse copper oxalate powder
  • A kind of controllable preparation method of monodisperse copper oxalate powder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Take 1.6 liters of deionized water without adding EDTA, stir to dissolve it completely, and control its pH to 5; then add 200ml of copper salt solution with a concentration of 0.1mol / l, stir for 5-30 minutes, and then add 200ml with a concentration of 0.1 mol / l oxalate solution, stirred for 5 minutes, then allowed to stand at room temperature for 1 hour; sampled and filtered, washed repeatedly to remove impurity ions, and collected solid copper oxalate powder with an average particle size of 2.3 microns. Its typical morphology features are as figure 1 shown.

Embodiment 2

[0032] Take 1.6 liters of deionized water, add 4g of EDTA, stir to dissolve completely, and control its pH to 7; then add 200ml of copper salt solution with a concentration of 0.1mol / l, and stir for 5-10 minutes; then add 200ml with a concentration of 0.1 mol / l oxalate solution, stirred for 5 minutes; stood at room temperature for 1 hour; then sampled and filtered at 10 minutes and 1 hour respectively, after repeated cleaning to remove impurity ions, collected solid copper oxalate powder, sampled and filtered at 10 minutes The average particle diameter of the solid copper oxalate powder is 2.1 microns, and the average particle diameter of the solid copper oxalate powder that is sampled and filtered in 1 hour is 3.1 microns. Its typical morphology features are as follows figure 2 and image 3 shown.

Embodiment 3

[0034] Take 1.6 liters of deionized water, add 4g of EDTA, stir to dissolve it completely, and control its pH to 7; then add 200ml of copper salt solution with a concentration of 0.1mol / l, and stir for 5-30 minutes; then add 200ml with a concentration of 0.1 mol / l oxalate solution, stirred for 2 minutes; stood at room temperature for 1 hour; then sampled and filtered at 10 minutes and 1 hour respectively, after repeated cleaning to remove impurity ions, collected solid copper oxalate powder, sampled and filtered at 10 minutes The average particle diameter of the solid copper oxalate powder is 2.1 microns, and the average particle diameter of the solid copper oxalate powder that is sampled and filtered in 1 hour is 3.1 microns. Its typical morphology features are as follows Figure 4 and Figure 5 shown.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of preparation of a monodisperse powder material, and provides a controllable preparation method of monodisperse copper oxalate powder. The method comprises the following steps: uniformly mixing a soluble copper salt solution, a soluble oxalate solution and an ethylenediamine tetraacetic acid (EDTA) solution in a molar ratio of 1:1:(0-1):1:5; standing in certain temperature condition; filtering, washing and drying to obtain the monodisperse copper oxalate powder. The method provided by the invention has the following beneficial effects: operation iseasy, monodispersity of copper oxalate is high, large-scale preparation is easy to implement, and preparation can be performed at room temperature; accurate control on the size of copper oxalate particles is realized, and the size can be controlled to 2-4 microns; the monodisperse copper oxalate powder can serve as a precursor and can be subjected to thermal decomposition to obtain copper oxide,cuprous oxide and metal copper powder.

Description

technical field [0001] The invention relates to the technical field of preparation of monodisperse powder materials, in particular to a controllable preparation method of monodisperse copper oxalate powder. Background technique [0002] The controllable preparation of nano- and micro-powder materials is very critical for the properties of various macro-sized and structured materials made from them. The fine powder materials with uniform basic characteristics such as particle size, shape and composition, and good dispersibility, the so-called monodisperse granular materials, are especially favored by the industry. First, the properties of monodisperse powder materials are uniform and consistent, which is conducive to fine, stable, and consistent processing into functional material products; second, the preparation process of monodisperse powder materials is demanding, so its preparation costs are particularly large-scale The preparation cost is relatively high. In addition t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C07C51/41C07C55/07
CPCC07C51/412C07C55/07
Inventor 黄凯陈兴王成彦
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap