Sn/Sb-Mn-GAC particles and application thereof in treatment of 4-chlorophenol through three-dimensional electrochemical reaction

A technology of chemical reaction and three-dimensional electricity, applied in water/sewage treatment, oxidized water/sewage treatment, water/sludge/sewage treatment, etc., can solve the problems of limited removal rate, difficult removal, high removal cost, etc., and achieve degradation Thorough, good adsorption effect, and the effect of improving catalytic oxidation performance

Active Publication Date: 2018-02-16
GUANGXI UNIV FOR NATITIES
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention aims at the problems of difficult removal, limited removal rate, high removal cost and complicated operation in the traditional treatment method of phenol-containing industrial wastewater in the prior art, and provides a preparation of Sn / Sb-Mn-GAC particles and its application in Application of Three-dimensional Electrochemical Reaction in Treatment of 4-Chlorophenol Wastewater

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sn/Sb-Mn-GAC particles and application thereof in treatment of 4-chlorophenol through three-dimensional electrochemical reaction
  • Sn/Sb-Mn-GAC particles and application thereof in treatment of 4-chlorophenol through three-dimensional electrochemical reaction
  • Sn/Sb-Mn-GAC particles and application thereof in treatment of 4-chlorophenol through three-dimensional electrochemical reaction

Examples

Experimental program
Comparison scheme
Effect test

preparation Embodiment 2

[0032] (1) Pretreatment of granular activated carbon: boil the granular activated carbon with a large amount of deionized water, dry it, and set aside.

[0033] (2) Weigh SnCl according to the mass ratio: 10:2:1:65 4 ·5H 2 O, Mn(NO 3 ) 2 , SbCl 3 and the GAC.

[0034] (3) SnCl 4 ·5H 2 O, Mn(NO 3 ) 2 , SbCl 3 Dissolve in an organic alcohol solvent to obtain a mixed solution, then soak GAC in the mixed solution, and shake on a shaking table at 160r / min for 4 hours to obtain the crude product of loaded Sn / Sb-Mn-GAC particles, then dry and bake at 350°C The supported Sn / Sb-Mn-GAC particles were obtained.

preparation Embodiment 3

[0036] (1) Pretreatment of granular activated carbon: boil the granular activated carbon with a large amount of deionized water, dry it, and set aside.

[0037] (2) Weigh SnCl according to the mass ratio: 12:3:1.5:70 4 ·5H 2 O, Mn(NO 3 ) 2 , SbCl 3 and the GAC.

[0038] (3) SnCl 4 ·5H 2 O, Mn(NO 3 ) 2 , SbCl 3 Dissolve in an organic alcohol solvent to obtain a mixed solution, then soak GAC in the mixed solution, and shake it on a shaking table at 170r / min for 3 hours to obtain the crude product of loaded Sn / Sb-Mn-GAC particles, then dry it and bake it at 400°C The supported Sn / Sb-Mn-GAC particles were obtained.

preparation Embodiment 4

[0040] (1) Pretreatment of granular activated carbon: boil the granular activated carbon with a large amount of deionized water, dry it, and set aside.

[0041] (2) Weigh SnCl according to the mass ratio: 14:4:42:75 4 ·5H 2 O, Mn(NO 3 ) 2 , SbCl 3 and the GAC.

[0042] (3) SnCl 4 ·5H 2 O, Mn(NO 3 ) 2 , SbCl 3 Dissolve in an organic alcohol solvent to obtain a mixed solution, then soak GAC in the mixed solution, and shake on a shaking table at 180r / min for 6 hours to obtain the crude product of loaded Sn / Sb-Mn-GAC particles, then dry and bake at 450°C The supported Sn / Sb-Mn-GAC particles were obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
electric potential / voltageaaaaaaaaaa
clearance rateaaaaaaaaaa
decolorization rateaaaaaaaaaa
Login to View More

Abstract

The invention discloses Sn / Sb-Mn-GAC particles. The particles are supported Sn / Sb-Mn-GAC particles prepared by supporting modified granular activated carbon onto metal ions such as Sn, Sb and Mn through an impregnation method. The method comprises the following steps: taking the supported Sn / Sb-Mn-GAC particles as a particle electrode, taking a dimensionally stable anode DSA as an anode, taking atitanium plate as a cathode, constructing a bipolar type three-dimensional electrochemical reactor, carrying out a three-dimensional electrochemical reaction under an electrochemical oxidation effect,and finally degrading 4-chlorophenol into carbon dioxide and water. The 4-chlorophenol wastewater is treated by using the Sn / Sb-Mn-GAC particles, so that the removal rate of the 4-chlorophenol can reach 99% or higher. Meanwhile, the particle preparation process is simple, the particles can be repeatedly used, the treatment cost of the 4-chlorophenol wastewater is greatly reduced, and the treatment efficiency of the 4-chlorophenol wastewater is improved.

Description

technical field [0001] The invention belongs to the technical field of sewage treatment, in particular to the preparation of Sn / Sb-Mn-GAC particles and its application in three-dimensional electrochemical reaction treatment of 4-chlorophenol wastewater. Background technique [0002] With the rapid development of petrochemical, plastic, synthetic fiber and other industries, phenolic wastewater generated in production is discharged into nature, causing water pollution and affecting the growth and reproduction of aquatic organisms. Phenol-containing wastewater is a refractory toxic organic substance, and it is also a difficult point in environmental governance. The discharge of phenolic substances is strictly controlled at home and abroad. [0003] The treatment of phenolic industrial wastewater has also become one of the hot research topics. At present, the adsorption method can generally be used for the treatment of wastewater containing phenolic substances, and the adsorben...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C02F1/461C02F1/72
CPCC02F1/46109C02F1/4672C02F2001/46133C02F2101/36
Inventor 李媚廖安平覃琴陈熠嘉蓝平谢树明谢涛
Owner GUANGXI UNIV FOR NATITIES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products