Low-odor polypropylene composite material and preparation method thereof

A composite material and polypropylene technology, which is applied in the field of low-odor polypropylene composite material and its preparation, and achieves the effects of good market prospect and low production cost

Active Publication Date: 2018-01-26
大韩道恩高分子材料(上海)有限公司
View PDF13 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above-mentioned various methods all focus on improving a certain aspect, and cannot solve the problem of odor generation in all aspects.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-odor polypropylene composite material and preparation method thereof
  • Low-odor polypropylene composite material and preparation method thereof
  • Low-odor polypropylene composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] (1) By weight percentage, accurately weigh 79wt% of 1215C, 18wt% of talcum powder BHS-818A, 1wt% of molecular sieve, 1wt% of jellyfish particles LDV 1040, 0.3wt% of erucamide, 0.2wt% of Antioxidant 1010, 0.2wt% antioxidant 168, 0.3% TAF;

[0039] (2) Put the above materials into a high-speed mixer and dry mix for 1-4 minutes, then put the mixed materials into a twin-screw extruder, melt and extrude through the twin-screw extruder, cool, dry, and pelletize to obtain the finished product.

Embodiment 2

[0041] (1) By weight percentage, accurately weigh 78wt% of 1215C, 18wt% of talcum powder BHS-818A, 1wt% of molecular sieve, 2wt% of jellyfish particles LDV 1040, 0.3wt% of erucamide, 0.2wt% of Antioxidant 1010, 0.2wt% antioxidant 168 and 0.3% TAF;

[0042](2) Put the above materials into a high-speed mixer and dry mix for 1-4 minutes, then put the mixed materials into a twin-screw extruder, melt and extrude through the twin-screw extruder, cool, dry, and pelletize to obtain the finished product.

Embodiment 3

[0044] (1) By weight percentage, accurately weigh 78wt% of 1215C, 18wt% of talcum powder BHS-818A, 2wt% of molecular sieves, 1wt% of jellyfish particles LDV 1040, 0.3wt% of erucamide, 0.2wt% of Antioxidant 1010, 0.2wt% antioxidant 168 and 0.3% TAF;

[0045] (2) Put the above materials into a high-speed mixer and dry mix for 1-4 minutes, then put the mixed materials into a twin-screw extruder, melt and extrude through the twin-screw extruder, cool, dry, and pelletize to obtain the finished product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to the technical field of polymer composite materials, particularly to a low-odor polypropylene composite material and a preparation method thereof, wherein the low-odorpolypropylene composite material is prepared from the following components by weight, 55-99 wt% of polypropylene, 0.1-2 wt% of an odor adsorbent, 0.1-3 wt% of a small molecular deodorant, 0.05-0.5 wt%of a scratch-resistant agent, 0-40 wt% of talc powder, 0.1-1 wt% of a main antioxidant, 0.1-1 wt% of an auxiliary antioxidant, and 0.1-1 wt% of a lubricant. According to the present invention, with the technical scheme, the production cost is low, the market prospect is good, and the obtained low-odor polypropylene composite material can be used in the vehicle field such as vehicle instrument panels, door protection plates, sub-instrument panels and other vehicle interior and exterior decoration parts, and the household appliance field such as refrigerators and small household appliances.

Description

technical field [0001] The invention relates to the technical field of polymer composite materials, in particular to a low-odor polypropylene composite material and a preparation method thereof. Background technique [0002] There are many reasons for the odor of PP plastics, mainly including: low molecular substances remaining in PP resin; added additives migrate to the surface of the polymer or volatilize on the surface of the polymer; After the chain is oxidized, volatile substances such as aldehydes and ketones will be produced. [0003] CN1727389 relates to a polypropylene composite material with low odor and low volatile content. The odor of the material is adsorbed through fine-pore silica gel. [0004] CN1727390 relates to a low-odor polypropylene composite material and its preparation method, in particular to a product obtained by adding an odor suppressor that can effectively suppress the unpleasant smell in the polypropylene composite material. The adsorbent is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/14C08L23/12C08K13/02C08K5/20C08K3/34C08K5/134C08K5/526C08J3/22
Inventor 文宏薛晗崔乘俊于晓宁
Owner 大韩道恩高分子材料(上海)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com