Preparation method for antiskid and anti-wear easily-cleaned ceramic tiles

A kind of ceramic brick, anti-slip technology, applied in the field of architectural ceramics, can solve the problems of insufficient surface wear resistance, low anti-slip coefficient, easy to scratch, etc., to achieve the effect of not easy to wear, high anti-slip coefficient, and difficult to hide dirt

Active Publication Date: 2017-10-20
GUANGDONG KITO CERAMICS GROUP CO LTD +2
View PDF5 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a non-slip, wear-resistant and easy-to-clean ceramic brick to alleviate the common problems of ceramic antique bricks on the market that the surface wear resistance is not enough, easy to scratch, easy to wear, and the product has a low anti-skid coefficient. There are technical problems such as difficult cleaning, dirt accumulation, and product turning black after a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for antiskid and anti-wear easily-cleaned ceramic tiles

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] The preparation method of the anti-slip, wear-resistant and easy-to-clean ceramic tile provided by the present invention comprises the following steps:

[0026] (a) preparing a green body layer from a blank;

[0027] (b) applying top glaze on the body layer to form a top glaze layer;

[0028] (c) preparing a decorative layer by inkjet printing on the glaze layer;

[0029] (d) Printing anti-slip and wear-resistant glaze on the decorative layer to form an anti-slip and wear-resistant layer. The anti-slip and wear-resistant glaze is mainly prepared from anti-slip and wear-resistant particles, and the anti-slip and wear-resistant particles are mainly composed of the following components in parts by mass: Composition: SiO 2 60-70 parts, Al 2 o 3 20-30 parts, Fe 2 o 3 0.01~0.1 parts, TiO 2 0.1~2 parts, Na 2 O 1~5 parts, K 2 1-10 parts of O, 0.1-1 parts of MgO, 0.1-5 parts of CaO and 0.1-2 parts of loss on ignition;

[0030] (e) Applying an easy-clean protective ...

Embodiment 1

[0084] The present embodiment provides a kind of preparation method of antiskid wear-resisting easy-to-clean ceramic brick, carries out according to following steps:

[0085] (a) The billet is firstly wet ball milled to make a moisture content of 6.3%, particle gradation of 1% above 20 mesh, 45% of -20~40 mesh, 80% of -20~60 mesh, and below 100 mesh 3%, the balance is -60 to 100 mesh slurry; then the slurry is pressed through a concave-convex mold to form a green body layer with a concave-convex effect; wherein, the blank is composed of the following components in parts by mass: 20 parts of quartz sand, potassium 15 parts of sodium sand, 18 parts of washed clay, 44 parts of white clay, 31 parts of potassium sand, 1 part of bentonite and 2.5 parts of black talc;

[0086] (s) Put the green body layer into a drying kiln for drying once, the drying temperature is 130°C, and the drying cycle is 60 minutes;

[0087] (b) On the once-dried green body layer, the surface glaze is appli...

Embodiment 2

[0095] This embodiment provides a kind of preparation method of anti-skid wear-resistant easy-clean ceramic brick, and the difference between this embodiment and embodiment 1 is that anti-skid wear-resistant particle is made up of the following components in parts by mass: SiO 2 70 parts, Al 2 o 3 20 parts, Fe 2 o 3 0.1 parts, TiO 2 2 parts, Na 2 O 1 part, K 2 5 parts of O, 1 part of MgO, 0.8 parts of CaO and 0.1 part of loss on ignition.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Meshaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method for antiskid and anti-wear easily-cleaned ceramic tiles, and relates to the technical field of building ceramics. The antiskid and anti-wear easily-cleaned ceramic tiles are prepared from the following successive steps: preparing a green body layer by pressing, spreading an overglaze layer, preparing a decoration layer by ink jet printing, printing an antiskid and anti-wear layer, preparing an easily-cleaned dry layers, conducting burning, conducting burnishing and polishing edges. Technical problems commonly existing in ceramic archaized tiles in present markets that surface anti-wear strength is not enough, wearing is easy, the antiskid factor is low, cleaning is difficult, dirt hiding is easy and the like are relieved, and technical effects that the prepared antiskid and anti-wear easily-cleaned ceramic tiles have high anti-wear strength, uneasiness to wear and a high antiskid factor, people are effectively prevented from falling, the security of the tiles is improved, meanwhile, the contamination resistance is excellent, dirt is not easy to hide, cleaning is easy, and convenience is provided for daily cleaning are achieved.

Description

technical field [0001] The invention relates to the technical field of architectural ceramics, in particular to a method for preparing anti-slip, wear-resistant and easy-to-clean ceramic tiles. Background technique [0002] Ceramic antique brick is a kind of building decoration material that has become popular in recent years. It has both the magnificence of polished brick and the rich and colorful patterns of porcelain tiles. It has many advantages such as modern or retro charm and individuality. It is popular in the market and consumed reader's favorite. [0003] With the continuous improvement of people's living standards, consumers have more and more demands on the functions of ceramic antique bricks. The beauty and grade of the product are improved, and the anti-skid coefficient of the product is low, especially when there is water on the surface of the product, it is easy to cause people to fall. At the same time, there are defects such as difficulty in cleaning, dirt...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/00C04B41/89C04B35/64E04F15/08B28B11/04B28B11/24
Inventor 喻劲军李德英戴永刚钟礼丰
Owner GUANGDONG KITO CERAMICS GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com