Brick breakage-free waterproof coating composition and ceramic tile waterproofing construction method

A waterproof coating and composition technology, which is applied in cement coatings, coatings, building structures, etc., can solve problems such as failure of waterproof materials, and achieve the effects of long plugging life, not easy to lose water, and excellent water absorption and swelling effect.

Active Publication Date: 2017-10-13
广州艾偲尼建材科技有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] But no matter how good the waterproof material is, it will always face the problem of failure after several years of use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The base surface of a household's toilet has seepage after pasting tiles; in order to solve the seepage problem, the following steps are used for construction:

[0032] Step 1: Evenly disperse 1 weight part of the base coating into 15 weight parts of water; the base coating includes: sodium acrylate, sodium silicate, lithium carbonate catalyst, methylethylenediamine curing agent; wherein, sodium acrylate, silicon The weight ratio of sodium carbonate, lithium carbonate catalyst, and methylethylenediamine curing agent is 0.6:0.3:0.4:16.

[0033] Step 2: Sprinkle the solution obtained in step 1 on the surface of the tiles, allowing it to immerse into the gaps in the tiles; wait for 5-20 minutes, and wait for the solution in step 1 to completely soak into the gaps in the tiles and fully cross-link and solidify.

[0034] Step 3: Evenly disperse 10 parts by weight of the intermediate coating into 1 part by weight of water to obtain an intermediate coating mixture, and then ap...

Embodiment 2

[0037] The base surface of a household's toilet has seepage after pasting tiles; in order to solve the seepage problem, the following steps are used for construction:

[0038] Step 1: Evenly disperse 1 weight part of the base coating into 15 weight parts of water; the base coating includes: sodium acrylate, sodium silicate, lithium carbonate catalyst, methylethylenediamine curing agent; wherein, sodium acrylate, silicon The weight ratio of sodium carbonate, lithium carbonate catalyst, and methylethylenediamine curing agent is 0.8:0.1:0.6:14.

[0039] Step 2: Sprinkle the solution obtained in step 1 on the surface of the tiles, allowing it to immerse into the gaps in the tiles; wait for 5-20 minutes, and wait for the solution in step 1 to completely soak into the gaps in the tiles and fully cross-link and solidify.

[0040] Step 3: Evenly disperse 10 parts by weight of the intermediate coating into 1 part by weight of water to obtain an intermediate coating mixture, and then ap...

Embodiment 3

[0043] The base surface of a resident's kitchen has seepage after pasting tiles; in order to solve the seepage problem, the following steps are used for construction:

[0044] Step 1: Evenly disperse 1 weight part of the base coating into 15 weight parts of water; the base coating includes: sodium acrylate, sodium silicate, lithium carbonate catalyst, methylethylenediamine curing agent; wherein, sodium acrylate, silicon The weight ratio of sodium carbonate, lithium carbonate catalyst, and methylethylenediamine curing agent is 0.7:0.2:0.5:15.

[0045] Step 2: Sprinkle the solution obtained in step 1 on the surface of the tiles, allowing it to immerse into the gaps in the tiles; wait for 5-20 minutes, and wait for the solution in step 1 to completely soak into the gaps in the tiles and fully cross-link and solidify.

[0046] Step 3: Evenly disperse 10 parts by weight of the intermediate coating into 1 part by weight of water to obtain an intermediate coating mixture, and then appl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of waterproof materials, in particular to a brick breakage-free waterproof coating composition. The brick breakage-free waterproof coating composition is prepared from a base layer coating, a middle layer coating and a surface layer coating, wherein the base layer coating is prepared from 0.6 to 0.8 weight part of sodium acrylate, 0.1 to 0.3 weight part of sodium silicate, 0.4 to 0.6 weight part of a lithium carbonate catalyst and 14 to 16 weight parts of a methyl ethidene diamine curing agent. The brick breakage-free waterproof coating composition has the beneficial effects of good waterproofing effect, long service life and external impact resistance.

Description

technical field [0001] The invention relates to the field of waterproof materials, in particular to a brick-shatter-free waterproof coating composition and a ceramic tile waterproof construction method. Background technique [0002] The waterproofing of toilets and kitchens is generally very difficult to deal with. The usual method is to lay a layer of waterproof material on the base of the building, and then fill it with building materials to achieve the waterproof effect. [0003] But no matter how good the waterproof material is, it will always face the problem of failure after several years of use. [0004] In order to solve this problem, those skilled in the art have reasons and motivations to develop a waterproof material and waterproof construction method that do not require building construction. Contents of the invention [0005] The invention aims to provide a brick-shatter-free waterproof coating composition and a ceramic tile waterproof construction method. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D4/02C09D7/12C09D1/08C09D133/04E04F13/02
CPCC09D1/08C09D4/00C09D143/04E04F13/02C08F220/06
Inventor 张敬
Owner 广州艾偲尼建材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com