A kind of surface modified polyvinyl chloride resin of ethylene-vinyl acetate copolymer emulsion and its surface modification method

A polyvinyl chloride resin and vinyl acetate copolymerization technology, applied in the direction of coating, can solve the problems of complicated coupling agent treatment process, little effect of performance improvement, and materials are not easy to disperse evenly, so as to improve the interface compatibility and effect. Enhance and enhance the effect of plasticizing performance

Active Publication Date: 2020-10-09
YUNNAN ZHENGBANG TECH CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] (1) The viscosity of the coupling agent is high, the material is not easy to disperse evenly, and has little effect on performance improvement;
[0006] (2) The consumption of coupling agent is large and the cost is high;
[0007] (3) The coupling agent treatment process is complicated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of surface modified polyvinyl chloride resin of ethylene-vinyl acetate copolymer emulsion and its surface modification method
  • A kind of surface modified polyvinyl chloride resin of ethylene-vinyl acetate copolymer emulsion and its surface modification method
  • A kind of surface modified polyvinyl chloride resin of ethylene-vinyl acetate copolymer emulsion and its surface modification method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A kind of ethylene-vinyl acetate copolymer latex surface modified polyvinyl chloride resin, its surface modification method comprises:

[0027] 1) In the polyvinyl chloride resin polymerization process, after the material enters the slurry tank, add 1% ethylene-vinyl acetate copolymer emulsion (40% vinyl acetate content) and mix evenly. The mixing time is: 10min;

[0028] 2) Then filter out excess water, transfer the material to a cyclone drying bed and dry at 40°C to obtain a polyvinyl chloride resin modified by ethylene-vinyl acetate copolymer emulsion.

Embodiment 2

[0030] A polyvinyl chloride resin surface-modified by an ethylene-vinyl acetate copolymer emulsion. The surface modification method is the same as in Example 1, except that the amount of ethylene-vinyl acetate copolymer emulsion used is changed to 20%.

Embodiment 3

[0032] A polyvinyl chloride resin surface-modified by an ethylene-vinyl acetate copolymer emulsion, the surface modification method of which is the same as in Example 1, except that the amount of ethylene-vinyl acetate copolymer emulsion used is changed to 40%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses and provides ethylene-vinyl acetate copolymerized emulsion surface modified polyvinyl chloride resin and a surface modification method thereof. The surface modification method comprises the following steps: uniformly coating ethylene-vinyl acetate copolymerized emulsion on the surface of polyvinyl chloride resin; then drying under the condition that the polyvinyl chloride resin is in contact with air to obtain the ethylene-vinyl acetate copolymerized emulsion surface modified polyvinyl chloride resin. When the polyvinyl chloride resin prepared by the surface modification method provided by the invention is used for producing a composite material, mechanical properties of the composite material can be improved; the filling amount of composite material filler and machining properties of the composite material are improved; the production operation is simple, easy and safe.

Description

technical field [0001] The invention belongs to the technical field of polyvinyl chloride, and in particular relates to a surface-modified polyvinyl chloride resin of ethylene-vinyl acetate copolymer emulsion and a surface modification method thereof. Background technique [0002] Polyvinyl chloride (PVC) is a general-purpose thermoplastic resin that is widely used. It has good flame retardancy, chemical corrosion resistance, wear resistance and other properties, and is low in price. It is widely used in construction, industry, agriculture and Packaging and other fields. However, conventional rigid polyvinyl chloride has the obvious disadvantage of high brittleness. At the same time, due to the incompatibility of the interface between polyvinyl chloride resin and hydrophilic fillers, it greatly limits its use as a high-performance structural material, and also greatly It limits its use in highly filled biomass materials. Therefore, the toughening modification of polyvinyl ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J7/04C08J7/00C08J3/00C08J3/20C08L27/06C08L23/08C08L97/02C08K13/02
CPCC08J3/005C08J3/20C08J7/00C08J7/0427C08J2327/06C08J2423/08C08L27/06C08L97/02C08L2205/035C08L2205/08C08L23/0853C08K13/02
Inventor 王寿元熊磊
Owner YUNNAN ZHENGBANG TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com