Polymer modified binding material of sulphate aluminum cement base

A sulfoaluminate and bonding material technology, applied in the field of bonding materials, can solve the problems of poor aging resistance, long construction period, low early strength, etc., and achieve high wet adhesion, cost saving, and high lubricating ability. Effect

Active Publication Date: 2017-09-15
长荣新材料技术有限公司
View PDF7 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The invention solves the problems of low early strength, long construction period, easy efflorescence and poor aging resistance of the currently used prefabricated building boards and bonding materials between blocks, and well balances the construction time and openness of the materials. Time and fast hardening performance, greatly shortening the construction period and saving labor costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Components: The proportioning ratio of each component in this embodiment is shown in Example 1 in Table 1.

[0032] Preparation:

[0033] (1) Weigh the polymer rubber powder, water reducer, and defoamer according to the required parts by weight, add water and mix to prepare mixture A, and set aside;

[0034] (2) In addition, weigh modified cement, quartz sand, mineral admixture, and retarder according to the required parts by weight, mix to obtain mixture B, and set aside;

[0035] (3) Continue to mix and stir the mixture B obtained in step (2), gradually add the mixture A under the stirring state, and stir for 4 minutes until a uniform slurry is formed by stirring, then the sulphoaluminate cement-based bond can be obtained. Material.

Embodiment 2

[0037] Components: The proportioning ratio of each component in this embodiment is shown in Example 2 in Table 1.

[0038] Preparation:

[0039] (1) Weigh the polymer rubber powder, water reducer, and defoamer according to the required parts by weight, add water and mix to prepare mixture A, and set aside;

[0040] (2) In addition, weigh modified cement, quartz sand, mineral admixture, and retarder according to the required parts by weight, mix to obtain mixture B, and set aside;

[0041] (3) Continue to mix and stir the mixture B obtained in step (2), gradually add the mixture A under the stirring state, and stir for 8 minutes until a uniform slurry is formed by stirring, then the sulphoaluminate cement-based bond can be obtained. Material.

Embodiment 3

[0043] Components: The proportioning ratio of each component in this embodiment is shown in Example 3 in Table 1.

[0044] Preparation:

[0045] (1) Weigh the polymer rubber powder, water reducer, and defoamer according to the required parts by weight, add water and mix to prepare mixture A, and set aside;

[0046] (2) In addition, weigh modified cement, quartz sand, mineral admixture, and retarder according to the required parts by weight, mix to obtain mixture B, and set aside;

[0047] (3) Continue to mix and stir the mixture B obtained in step (2), gradually add the mixture A under the stirring state, and stir for 5 minutes until a uniform slurry is formed by stirring, then the sulphoaluminate cement-based bond can be obtained. Material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
densityaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polymer modified binding material of sulphate aluminum cement base. The polymer modified binding material of sulphate aluminum cement base is prepared from, by weight, 750-850 parts of modified cement, 900-1350 parts of quartz sand, 100-120 parts of mineral admixture, 5-8 parts of modified polymer gelatine powder, 2-4 parts of retarder, 4.5-9 parts of water reducing agent, 0.05-0.1 part of defoaming agent; the allowance is water. Meanwhile, the invention further discloses a preparation method of the polymer modified binding material, which includes steps of weighting raw materials at ratio, adding water to stir, and preparing to be slurry, and others. The binding material prepared by the invention can improve the binding ability between interfaces by modifying a polymer; the binding material is high in binding strength and good in flowability; the novel polymer modified binding material with good economic benefit and social benefit has advantages of preventing flash setting and fully saving material and cost.

Description

technical field [0001] The invention belongs to the technical field of bonding materials, in particular to a bonding material modified with polymers to modify sulphoaluminate cement. Background technique [0002] In recent years, with the development of prefabricated concrete structures in China, new requirements have been put forward for interface connection technology. No matter in the process of repairing, strengthening or bonding external wall insulation materials or ceramic tiles, it is necessary to consider the bonding performance of the interface of the construction materials used. Therefore, it is of great significance to improve the interface bonding performance of materials. Because polymers have good cohesive force and higher tensile strength compared with inorganic non-metallic materials, polymers are often used to modify cement materials to improve the bonding performance and tensile properties of cement materials. The most common It is the application of d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/06
CPCC04B28/06C04B2111/00637C04B2201/50C04B7/02C04B24/122C04B14/06C04B18/08C04B18/146C04B24/02C04B24/281C04B2103/22C04B2103/302C04B2103/50
Inventor 吴克峰
Owner 长荣新材料技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com