A kind of gold glaze glaze material, gold glaze Jun porcelain and preparation method thereof

A glaze and gold technology, applied in the field of Jun porcelain, can solve the problems of limiting the artistic appreciation and commercial value of Jun porcelain, and the inability to realize the good application of gold glaze.

Active Publication Date: 2019-01-29
大宋官窑股份有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the unique glaze formula and firing system of Jun porcelain, there is no report on the glaze formula and firing method of Jun porcelain gold glaze in the prior art. Therefore, it is impossible to realize the good application of gold glaze on Jun porcelain. Thereby limiting the appreciation of Jun porcelain art and the improvement of commercial value

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of gold glaze glaze material, gold glaze Jun porcelain and preparation method thereof
  • A kind of gold glaze glaze material, gold glaze Jun porcelain and preparation method thereof
  • A kind of gold glaze glaze material, gold glaze Jun porcelain and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0047] The present invention also provides a preparation method of gold-glazed Jun porcelain, comprising the following steps:

[0048] a) Mix the underglaze glaze material described in the above technical scheme with water, perform the first ball milling and the first sieving in sequence to obtain the underglaze slurry; the sieve hole size of the first sieving is 300 mesh, and the first The sieved balance shall not exceed 0.5%;

[0049] b) Mix the surface glaze glaze material described in the above technical solution with water, and perform the second ball milling and the second sieving in sequence to obtain the surface glaze slurry; the size of the second sieving sieve is 150 mesh to 200 mesh , the balance of the second sieve shall not exceed 0.5%;

[0050] c) applying the bottom glaze slurry obtained in step a) to the Jun porcelain body for the first glazing, then applying the top glaze slurry obtained in step b) for the second glazing, and finally firing to obtain the gold...

Embodiment 1

[0079] (1) The formula of gold glaze glaze is as follows:

[0080] Bottom glaze: 38 parts by weight of potassium feldspar, 11 parts by weight of talc, 5 parts by weight of glass powder, 17 parts by weight of zinc oxide, 3 parts by weight of magnesium oxide, 17 parts by weight of quartz, 6 parts by weight of iron ore, 3 parts by weight of soda stone parts by weight;

[0081] Surface glaze glaze material: 52 parts by weight of Yushan feldspar, 17 parts by weight of quartz, 14 parts by weight of calcite, 6 parts by weight of copper ore, 0.5 part by weight of copper oxide, 3 parts by weight of zinc oxide, 0.5 part by weight of tin oxide, 7.5 parts by weight of talc share.

[0082] (2) Mill the above-mentioned bottom glaze material, balls and water according to the mass ratio of 1:1.5:0.7 for 72 hours, pass through a 300-mesh sieve, and the sieved balance does not exceed 0.5%, to obtain the bottom glaze slurry;

[0083] At the same time, ball mill the above-mentioned surface glaz...

Embodiment 2

[0095] (1) The formula of gold glaze glaze is as follows:

[0096] Bottom glaze: 35 parts by weight of potassium feldspar, 12 parts by weight of talc, 3 parts by weight of glass powder, 18 parts by weight of zinc oxide, 2 parts by weight of magnesium oxide, 18 parts by weight of quartz, 8 parts by weight of iron ore, 4 parts by weight of soda stone parts by weight;

[0097] Surface glaze: 54 parts by weight of Yushan feldspar, 15 parts by weight of quartz, 16.5 parts by weight of calcite, 5 parts by weight of copper ore, 0.5 parts by weight of copper oxide, 3 parts by weight of zinc oxide, 0.5 parts by weight of tin oxide, 6 parts by weight of talc share.

[0098] (2) Mill the above-mentioned bottom glaze material, balls and water according to the mass ratio of 1:1.5:0.7 for 72 hours, pass through a 300-mesh sieve, and the sieved balance does not exceed 0.5%, to obtain the bottom glaze slurry;

[0099] At the same time, ball mill the above-mentioned surface glaze material, b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a golden glaze material and golden glaze jun porcelain and a preparation method thereof. The golden glaze material comprises a base glaze material and a surface glaze material, wherein the base glaze material comprises the following components in parts by weight: 35-40 parts of potash feldspar, 10-20 parts of talc, 3-8 parts of glass powder, 15-20 parts of zinc oxide, 2-3 parts of magnesium oxide, 15-20 parts of quartz, 3-8 parts of iron ore and 2-4 parts of soda lime; the surface glaze material comprises the following components in parts by weight: 50-55 parts of Yushan feldspar, 15-20 parts of quartz, 12-18 parts of calcite, 5-8 parts of copper ore, 0.5-1 part of copper oxide, 3-5 parts of zinc oxide, 0.5-1 part of stannic oxide and 6-8 parts of talc. Due to a unique glaze formula, the prepared golden glaze jun porcelain has an effect of golden textures, and is high in artistic ornamental value and commercial value.

Description

technical field [0001] The invention relates to the technical field of Jun porcelain, and more specifically relates to a gold glaze glaze material, a gold glaze Jun porcelain and a preparation method thereof. Background technique [0002] Jun porcelain began in the Tang Dynasty and flourished in the Song Dynasty. In the Song Dynasty, it was one of the five famous porcelains and was used by the royal family. Since 2000, Jun Porcelain, with its profound historical and cultural heritage and extraordinary kiln changes, has repeatedly entered important international venues in the name of national gifts, making the development of Jun Porcelain artworks unprecedentedly prosperous. [0003] Traditional Jun porcelain glazes are unrivaled in the porcelain forest by reducing copper and iron elements to produce magical kiln changes. The common ones are: kiln-changing glazes such as rose purple red glazes and Jun red red glazes colored with copper elements; single-color glazes such as az...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/02C03C8/00C04B41/86C04B41/52C04B33/24
CPCC03C8/00C03C8/02C04B33/24C04B41/5022C04B41/52C04B41/86C04B2235/6562C04B2235/6567C04B2235/658C04B2235/661
Inventor 李应洲贾海洋王京航苗占军
Owner 大宋官窑股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com