A heat-resistant borosilicate flat glass and its preparation method

A borosilicate and flat glass technology, applied in the field of fireproof glass, can solve the problems of high melting temperature and forming temperature of borosilicate 4.0 glass, high technical difficulty, etc., achieve good clarification effect, improve melting quality, and avoid glass stability The effect of sexual decline

Active Publication Date: 2019-06-18
GLASS TECH RES INST OF SHAHE CITY OF HEBEI PROVINCE
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, Chinese glass companies can only produce borosilicate 3.3 flat glass. Borosilicate 4.0 glass has a high melting temperature and forming temperature, and the technology is difficult, so it cannot be produced smoothly at present.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A heat-resistant borosilicate flat glass and its preparation method
  • A heat-resistant borosilicate flat glass and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of heat-resistant borosilicate flat glass, by weight percentage, comprises the following components: SiO 2 78.1%, Al 2 o 3 1.1%, B 2 o 3 12.9%, Na 2 O 6%, CaO 1%, K 2 O 0.5%, ZrO 2 0.39%, GeO 2 0.01%.

Embodiment 2

[0029] A kind of heat-resistant borosilicate flat glass, by weight percentage, comprises the following components: SiO 2 82%, Al 2 o 3 1.89%, B 2 o 3 10%, Na 2 O 3%, CaO 1%, K 2 O 2%, ZrO 2 0.1%, GeO 2 0.01%.

Embodiment 3

[0031] A kind of heat-resistant borosilicate flat glass, by weight percentage, comprises the following components: SiO 2 79%, Al 2 o 3 2.2%, B 2 o 3 9%, Na 2 O 4%, CaO 2.7%, K 2 O 1%, ZrO 2 0.1%, GeO 2 2%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
melting pointaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention provides heat-resistant borosilicate flat glass and belongs to the technical field of fireproof glass. The heat-resistant borosilicate flat glass is prepared from, by weight, 78.1-82% of SiO2, 1-5% of Al2O3, 9-14% of B2O3, 3-6% of Na2O, 1-5% of CaO, 0.5-2% of K2O, 0.1-3% of ZrO2 and 0.01-2% of GeO2, wherein the total content of SiO2 and B2O3 accounts for 87.1-92% of the total content of all the materials, and the weight ratio of SiO2 to B2O3 is 5.5 to 8.6. The invention further provides a preparation method of the heat-resistant borosilicate flat glass; compared with current borosilicate flat glass in the market, the heat-resistant borosilicate flat glass has a higher glass softening point and a lower linear expansion coefficient, at the same time, the melting temperature and the molding temperature are relatively low; the glass is easy to manufacture and can serve as the fireproof glass applied in the fire protection field after being tempered.

Description

technical field [0001] The invention belongs to the technical field of fireproof glass, and relates to a fireproof borosilicate flat glass used in buildings, which is borosilicate 4.0 flat glass, and in particular to a heat-resistant borosilicate flat glass and a preparation method thereof. Background technique [0002] Borosilicate flat glass refers to the basic composition of SiO 2 , B 2 o 3 、Na 2 O glass. Borosilicate glass has excellent thermal properties, optical properties, mechanical properties and chemical properties, and is widely used in architectural fireproof glass, instrument glass, utensil cooker glass, photoelectric power source glass and other fields. [0003] There are two types of borosilicate flat glass currently on the market: borosilicate 3.3 glass and borosilicate 4.0 glass. The performance index of borosilicate 3.3 glass is that the glass softening point is about 820°C, and the expansion coefficient is 33×10 -7 / °C, melting temperature 1670°C, mo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C4/00C03C3/093
CPCC03C3/093C03C4/00
Inventor 程金树袁坚郭振强苏驰
Owner GLASS TECH RES INST OF SHAHE CITY OF HEBEI PROVINCE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com