A diatom mud coating and coating technology, applied in the coating field, can solve problems such as difficulty in grasping the size of the muzzle discharge, and it is not suitable for the northwest region with dry climate, etc., and achieve the effect of easy construction and good durability

Inactive Publication Date: 2017-03-29
甘肃连心涂料有限责任公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The diatom mud coating currently on the market, because of its strong adsorption, is very suitable for use in the south of the humid climate, but n

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0007] Example 1 A diatom mud coating, which is prepared by mixing the following raw materials in parts by weight (unit: kg): 215 parts of diatomite, 40 parts of heavy calcium, 40 parts of talcum powder, and 40 parts of titanium dioxide , 65 parts of latex powder, 2 parts of hydroxypropyl methylcellulose, 180 parts of white cement with a strength grade of 42.5, 20 parts of mica powder, 10 parts of woody white fiber, 3 parts of bentonite, 290 parts of snowflake white colored sand, water-reducing 1 part of anti-aging agent, 0.5 part of tensile fiber, and 0.2 part of negative ion powder.

Embodiment 2

[0008] Example 2 A diatom mud coating, which is prepared by mixing the following raw materials in parts by weight (unit: kg): 235 parts of diatomite, 60 parts of heavy calcium, 60 parts of talcum powder, and 60 parts of titanium dioxide , 85 parts of latex powder, 6 parts of hydroxypropyl methylcellulose, 220 parts of white cement with a strength grade of 42.5, 40 parts of mica powder, 20 parts of woody white fiber, 7 parts of bentonite, 295 parts of snowflake white colored sand, water-reducing 3 parts of anti-aging agent, 1.5 parts of tensile fiber, and 0.8 parts of negative ion powder.

Embodiment 3

[0009] Example 3 A diatom mud coating, which is prepared by mixing the following raw materials in parts by weight (unit: kg): 225 parts of diatomite, 50 parts of heavy calcium, 50 parts of talcum powder, and 50 parts of titanium dioxide , 75 parts of latex powder, 4 parts of hydroxypropyl methylcellulose, 200 parts of white cement with a strength grade of 42.5, 30 parts of mica powder, 15 parts of woody white fiber, 5 parts of bentonite, 292.5 parts of snowflake white colored sand, water-reducing 2 parts of anti-aging agent, 1 part of tensile fiber, and 0.5 part of negative ion powder.

[0010] In the above-mentioned Examples 1-3, diatomite is produced by Dahua Diatomite Products Co., Ltd., Linjiang City, Jilin Province; heavy calcium is produced by Sichuan Shimian Jufeng Powder Co., Ltd., KKS-1250; talcum powder is produced by Liaoning Qianhe Mining Industry Co., Ltd. Production, TLH-902; titanium dioxide produced by Billions, BLR-699; latex powder produced by Anhui Latex Pow...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a diatom ooze coating. The diatom ooze coating is prepared via uniform mixing of following raw materials, by weight, 215 to 235 parts of diatomite, 40 to 60 parts of heavy calcium carbonate, 40 to 60 parts of talcum powder, 40 to 60 parts of titanium dioxide, 65 to 85 parts of latex powder, 2 to 6 parts of hydroxypropyl methyl cellulose, 180 to 220 parts of white cement with strength grade of 42.5, 20 to 40 parts of mica powder, 10 to 20 parts of wood white fiber, 3 to 7 parts of bentonite, 290 to 295 parts of snow white colored sand, 1 to 3 parts of a water reducer, 0.5 to 1.5 parts of stretch-proof fiber, and 0.2 to 0.8 part of a negative ion powder. The diatom ooze coating is convenient for construction, is nontoxic, is odourless, is excellent in durability, and is suitable to be used in northwest regions with dry climate; and no pollution is caused.

Description

technical field [0001] The invention relates to a coating, in particular to a diatom mud coating. Background technique [0002] The diatom mud coating currently on the market, because of its strong adsorption, is very suitable for use in the south of the humid climate, but not suitable for the northwest region of the dry climate, and it is difficult to control the discharge of the muzzle during the construction process. the size of. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a diatom mud coating which is easy to construct and has good durability. [0004] In order to solve the above problems, a diatom mud coating according to the present invention is characterized in that: the coating is made by mixing uniformly the following raw materials in parts by weight: 215~235 parts of diatomite, 40~60 parts of heavy calcium , 40~60 parts of talcum powder, 40~60 parts of titanium dioxide, 65~85 parts of latex powder...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/04
CPCC04B28/04C04B2111/00482
Inventor 刘国应
Owner 甘肃连心涂料有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap