Firm silk film and processing method thereof

A processing method and silk technology, which are applied in the field of objects or materials for storage or transportation, can solve the problems that the safety and stability of film preservation cannot be guaranteed, the film cannot be used for dredging, and the packaging does not meet the requirements, and the decoration effect can be improved. , Strengthening strength, soft touch effect

Active Publication Date: 2017-03-22
绍兴永兴薄膜有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Films are more and more widely used in packaging and decoration. Although the simple film structure is easy to process, it does not meet the requirements of exquisite packaging on the one hand. On the other hand, the composition of the film will also affect the quality of the packaged substances. , especially when there are oil stains, water stains, etc. on the packaging, this kind of film cannot play a role in dredging, and long-term retention will cause damage to the internal protection items. Therefore, too thin film is very important for preservation safety and Stability cannot be guaranteed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Firm silk film and processing method thereof
  • Firm silk film and processing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The firm type silk film of this embodiment combines figure 1 and figure 2 , from bottom to top are the hard substrate 1, the bottom film 2, the fiber layer 3 and the silk layer 4, the bottom film 2 is bonded on the hard substrate 1, and the fiber layer 3 and the silk layer 4 are sequentially arranged on the bottom film 2, and The bottom of the fibrous layer 3 extends into the base film 2, and the joints of the fibrous layer 3 and the silk layer 4 intersect each other, forming an incoherent fuzzy boundary. In this embodiment, the fiber layer 3 is made of PET fibers, and the PET fibers extend into the bottom film 2, so that the bottom of the fiber layer 3 extends into the bottom film 2; the fiber layer 3 is bonded to the bottom film 2 by an auxiliary agent, and the corresponding , the silk layer 4 is bonded on the fiber layer 3 by an auxiliary agent.

[0024] The processing method of above-mentioned film comprises two steps:

[0025] (1) Forming of fiber layer and sil...

Embodiment 2

[0028] The firm type silk film of this embodiment combines figure 1 and figure 2 , from bottom to top are the hard substrate 1, the bottom film 2, the fiber layer 3 and the silk layer 4, the bottom film 2 is bonded on the hard substrate 1, and the fiber layer 3 and the silk layer 4 are sequentially arranged on the bottom film 2, and The bottom of the fibrous layer 3 extends into the base film 2, and the joints of the fibrous layer 3 and the silk layer 4 intersect each other, forming an incoherent fuzzy boundary. In this embodiment, the fiber layer 3 is made of PET fibers, and the PET fibers extend into the bottom film 2, so that the bottom of the fiber layer 3 extends into the bottom film 2; the fiber layer 3 is bonded to the bottom film 2 by an auxiliary agent, and the corresponding , the silk layer 4 is bonded on the fiber layer 3 by an auxiliary agent.

[0029] The processing method of the above-mentioned film includes two steps: (1) Forming of fiber layer and silk layer...

Embodiment 3

[0031] The firm type silk film of this embodiment combines figure 1 and figure 2 , from bottom to top are the hard substrate 1, the bottom film 2, the fiber layer 3 and the silk layer 4, the bottom film 2 is bonded on the hard substrate 1, and the fiber layer 3 and the silk layer 4 are sequentially arranged on the bottom film 2, and The bottom of the fibrous layer 3 extends into the base film 2, and the joints of the fibrous layer 3 and the silk layer 4 intersect each other, forming an incoherent fuzzy boundary. In this embodiment, the fiber layer 3 is made of PET fibers, and the PET fibers extend into the bottom film 2, so that the bottom of the fiber layer 3 extends into the bottom film 2; the fiber layer 3 is bonded to the bottom film 2 by an auxiliary agent, and the corresponding , the silk layer 4 is bonded on the fiber layer 3 by an auxiliary agent.

[0032] The processing method of the above-mentioned film includes three steps: (1) Forming of fiber layer and silk lay...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of articles for storage or transport of objects or materials and relates to a firm silk film and a processing method thereof. The firm silk film is formed by a hard substrate, a base film, a fiber layer and a silk layer from bottom to top. The base film is adhered to the hard substrate, the fiber layer and the silk layer are arranged on the base film sequentially, the bottom of the fiber layer extends into the base film, and joints of the fiber layer and the silk layer are intersected to form non-continuous inconspicuous bounds. The firm silk film is applicable to package decorative materials for clothes, shoes, hats and gift box packages and is attractive in appearance, good in hand feel, high in intrinsic firmness and capable of guaranteeing safety of internal article packages.

Description

technical field [0001] The invention relates to a firm silk film and a processing method thereof, and belongs to the technical field of articles used for storing or transporting articles or materials. Background technique [0002] Films are more and more widely used in packaging and decoration. Although the simple film structure is easy to process, it does not meet the requirements of exquisite packaging on the one hand. On the other hand, the composition of the film will also affect the quality of the packaged substances. , especially when there are oil stains, water stains, etc. on the packaging, this kind of film cannot play a role in dredging, and long-term retention will cause damage to the internal protection items. Therefore, too thin film is very important for preservation safety and Stability cannot be guaranteed. [0003] Based on this, this application is made. Contents of the invention [0004] Aiming at the above-mentioned defects of existing conventional de...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B32B7/12B32B7/04B32B9/02B32B9/04B32B27/36B32B27/06B32B27/12B32B37/10B32B37/12B65D65/40
CPCB32B5/02B32B5/024B32B5/26B32B7/04B32B7/12B32B37/10B32B37/12B32B2262/0284B32B2262/08B65D65/40
Inventor 沈韶良
Owner 绍兴永兴薄膜有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com