Carbon fiber resin-based friction material and preparation method thereof

A carbon fiber resin-based, friction material technology, applied in the field of materials, can solve the problems of complicated production process of friction materials, low comprehensive performance of brake pads, unstable friction coefficient, etc., to improve chemical resistance, good mechanical properties, The effect of small compression set

Inactive Publication Date: 2016-12-21
广西驰胜农业科技有限公司
View PDF8 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the brake pads made of composite friction materials have low overall performance and various performance problems, such as insufficient strength and toughness, large thermal decay at high temperature, unstable friction coefficient during the heating process of the brake, and slippage may occur These problems mainly come from the selection of friction materials
In the prior art, to solve these problems, there are too many types of raw materials used in the preparation of friction materials, some as many as 25, resulting in high cost and uneconomical; in addition, some carbon fiber friction materials are not used in the preparation process. The surface treatment of carbon fiber will be carried out, so that it is difficult to mix carbon fiber and other raw materials evenly after mixing; if the surface of carbon fiber is modified, the production process of the friction material is slightly complicated, which is not conducive to vigorous promotion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carbon fiber resin-based friction material and preparation method thereof
  • Carbon fiber resin-based friction material and preparation method thereof
  • Carbon fiber resin-based friction material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The following examples can help those skilled in the art to understand the present invention more comprehensively, but cannot limit the present invention in any way.

[0021] Provide the formula of embodiment 1-5 raw material below, list as table 1:

[0022] Table 1 The raw materials, contents and specifications of friction materials in Examples 1-5 (unit: gram)

[0023]

[0024]

[0025] The friction materials of Examples 1-5 are made according to the following methods

[0026] A carbon fiber resin-based friction material, mainly made of nitrile rubber powder, mineral fiber, carbon fiber, calcium sulfate, bauxite, friction powder, aluminum oxide, white carbon black, plastic particles, muscovite, resin, aramid fiber and graphite The specific content of each raw material is shown in Table 1.

[0027] The preparation method of the carbon fiber resin-based friction material comprises the following steps:

[0028] 1) Weighing of raw materials: picking the raw mater...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a carbon fiber resin-based friction material and a preparation method thereof. The raw materials include nitrile rubber powder, mineral fiber, carbon fiber, calcium sulfate, bauxite, friction powder, aluminum oxide, white carbon black, plastic particles, white clouds resin, aramid and graphite. The manufacturing method steps are: weighing of raw materials, processing of carbon fibers, mixing of raw materials, drying of raw materials, pressing of raw materials and solidification of friction materials. The invention uses less material, is low in cost and has a long service life; at the same time, the carbon fiber is subjected to simple ultrasonic surface treatment to make it have better friction and wear performance; the invention is a brake pad with excellent performance and is worthy of vigorous promotion.

Description

【Technical field】 [0001] The invention relates to the technical field of materials, in particular to a carbon fiber resin-based friction material and a preparation method thereof. 【technical background】 [0002] At present, the brake pads made of composite friction materials have low overall performance and various performance problems, such as insufficient strength and toughness, large thermal recession at high temperature, unstable friction coefficient during the heating process of the brake, and slippage may occur These problems mainly come from the selection of friction materials. In the prior art, to solve these problems, there are too many types of raw materials used in the preparation of friction materials, some as many as 25, resulting in high cost and uneconomical; in addition, some carbon fiber friction materials are not used in the preparation process. The carbon fiber will be surface treated, so that it is difficult to mix the carbon fiber and other raw material...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): F16D69/02C09K3/14B29C43/02B29C43/58B29B13/06B29L31/16
CPCF16D69/023B29B13/06B29C43/02B29C45/58B29C2043/5816B29L2031/16F16D2200/006F16D2200/0082
Inventor 韩再满
Owner 广西驰胜农业科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com