Preparation method of coating type dye polarizing component and liquid crystal panel

A technology of polarizing light and dyes, applied in polarizing elements, optical elements, optics, etc., can solve the problems of reduced polarization degree of polarizer, easy agglomeration of dyes, low polarization degree of polarizer, etc.

Active Publication Date: 2019-06-07
TCL CHINA STAR OPTOELECTRONICS TECH CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the current dye-coated polarizer has the defect that dyes are easy to agglomerate during the manufacturing process, which will lead to a decrease in the degree of polarization of the dye-coated polarizer; and the low degree of polarization of the polarizer will make the liquid crystal Reduced contrast of the panel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of coating type dye polarizing component and liquid crystal panel
  • Preparation method of coating type dye polarizing component and liquid crystal panel
  • Preparation method of coating type dye polarizing component and liquid crystal panel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the drawings in the embodiments of the present invention. Apparently, the described embodiments are some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts shall fall within the protection scope of the present invention.

[0022] The preparation method of the coating-type dye polarizing assembly provided in the following examples of the present invention is used to prepare the coating-type dye polarizing assembly. The coating-type dye polarizing component includes a substrate and a coating-type dye polarizing layer coated on the substrate. The substrate may be a CF (Color Filter, color filter) substrate of a liquid crystal panel, or a TFT (Thin Film Transistor, thin film transistor) sub...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
wavelengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a coating type dye polarization component, wherein the coating type dye polarization component comprises a substrate; a polarization alignment film is arranged on the substrate; the preparation method comprises the following steps: heating a reaction vessel to a reaction temperature according to a hot bath method, maintaining the reaction temperature in the reaction vessel; placing a reaction monomer in the reaction vessel, stirring and fully dissolving, then standing for a first time interval; placing a dye in the reaction vessel, stirring and fully dissolving, then standing for the first time interval to obtain a polarization film solution; coating the polarization film solution on the polarization alignment film of the substrate by using a spin-coating method to obtain a polarization film; curing the polarization film through ultraviolet irradiation to obtain the coating type dye polarization component. The invention further provides a liquid crystal panel. The solution of the invention can improve a polarization degree of a polarizer and improve a contrast ratio of the liquid crystal panel.

Description

technical field [0001] The invention relates to the field of liquid crystal manufacturing, in particular to a method for preparing a coating-type dye polarizing assembly, and a liquid crystal panel with the coating-type dye polarizing assembly produced by the preparation method. Background technique [0002] The polarizer is a very important part of the LCD panel, which largely determines the key characteristics of the LCD panel, such as contrast, transmittance, brightness, thickness, etc. Among them, the dye-based polarizer absorbs dichroic organic dyes on PVA (polyvinyl alcohol), and stretches and aligns them to make it have polarized light performance. Dye-based polarizers have better resistance to high temperature and high humidity. Dye-based polarizers also include coated polarizers. Coated dye polarizer is a kind of polarizer with excellent reliability and can be thinned. One of the raw materials for the preparation of the coated dye polarizer is dye. [0003] Howe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G02B5/30G02F1/1335
CPCG02B5/3033G02F1/133528
Inventor 陈珍霞侯俊
Owner TCL CHINA STAR OPTOELECTRONICS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products