Layered aluminum alloy conductor and annealing process thereof

A technology of aluminum alloy conductors and annealing process, which is applied in the direction of metal/alloy conductors, etc., can solve the problems of poor flexibility and conductivity, single structure of aluminum alloy conductors, etc., achieve good extensibility, increase effective cross-sectional area, and high conductivity Effect

Active Publication Date: 2016-08-10
WUXI SUNAN CABLE
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the aluminum alloy conductor structure is relatively simple, and they are all single-layer round conductors.
Moreover, the existing conventional aluminum alloy cable conductors are generally not annealed when used in wires and cables, and their flexibility and conductivity are poor, so their use has certain limitations.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Layered aluminum alloy conductor and annealing process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Such as figure 1 As shown, a layered aluminum alloy conductor according to the present invention includes an aluminum alloy inner conductor 1, and an aluminum alloy equal ring layer I2 is arranged on the outside of the aluminum alloy inner conductor 1. An aluminum alloy integral ring layer 3 is arranged outside the ring layer I2, and an aluminum alloy equal ring layer II4 is arranged outside the aluminum alloy entire ring layer 3.

[0037] A kind of annealing process of layered aluminum alloy conductor, it comprises the following steps,

[0038] (1) First put the aluminum alloy inner conductor into the annealing furnace, heat it to 200°C within 15 minutes, keep it warm for 20 minutes, and cool it naturally;

[0039] (2) Then put the aluminum alloy into the annealing furnace, heat it to 230°C within 12 minutes, keep it warm for 30 minutes, and cool it naturally;

[0040] (3) Then put the aluminum alloy ring layer into the annealing furnace, heat it to 220°C within 11 m...

Embodiment 2

[0051] Such as figure 1 As shown, a layered aluminum alloy conductor according to the present invention includes an aluminum alloy inner conductor 1, and an aluminum alloy equal ring layer I2 is arranged on the outside of the aluminum alloy inner conductor 1. An aluminum alloy integral ring layer 3 is arranged outside the ring layer I2, and an aluminum alloy equal ring layer II4 is arranged outside the aluminum alloy entire ring layer 3.

[0052] A kind of annealing process of layered aluminum alloy conductor, it comprises the following steps,

[0053] (1) First put the aluminum alloy inner conductor into the annealing furnace, heat it to 200°C within 20 minutes, keep it warm for 20 minutes, and cool it naturally;

[0054] (2) Then put the aluminum alloy into the annealing furnace, heat it to 230°C within 16 minutes, keep it warm for 30 minutes, and cool it naturally;

[0055] (3) Then put the aluminum alloy ring layer into the annealing furnace, heat it to 220°C within 12 m...

Embodiment 3

[0066] Such as figure 1 As shown, a layered aluminum alloy conductor according to the present invention includes an aluminum alloy inner conductor 1, and an aluminum alloy equal ring layer I2 is arranged on the outside of the aluminum alloy inner conductor 1. An aluminum alloy integral ring layer 3 is arranged outside the ring layer I2, and an aluminum alloy equal ring layer II4 is arranged outside the aluminum alloy entire ring layer 3.

[0067] A kind of annealing process of layered aluminum alloy conductor, it comprises the following steps,

[0068] (1) First put the aluminum alloy inner conductor into the annealing furnace, heat it to 200°C within 25 minutes, keep it warm for 20 minutes, and cool it naturally;

[0069] (2) Then put the aluminum alloy into the annealing furnace, heat it to 230°C within 18 minutes, keep it warm for 30 minutes, and cool it naturally;

[0070](3) Then put the aluminum alloy ring layer into the annealing furnace, heat it to 220°C within 14 mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a layered aluminum alloy conductor and an annealing process thereof. The layered aluminum alloy conductor comprises an aluminum alloy inner conductor, wherein an aluminum alloy equally-divided ring layer I is arranged outside the aluminum alloy inner conductor, an aluminum alloy integral ring layer is arranged outside the aluminum alloy equally-divided ring layer I, and an aluminum alloy equally-divided ring layer II is arranged outside the aluminum alloy integral ring layer. The annealing process comprises the steps of: placing the aluminum alloy inner conductor in an annealing furnace, and subjecting the aluminum alloy inner conductor to heating, heat preserving and cooling; placing the aluminum alloy equally-divided ring layer I in the annealing furnace, and subjecting the aluminum alloy equally-divided ring layer I to heating, heat preserving and cooling; placing the aluminum alloy integral ring layer in the annealing furnace, and subjecting the aluminum alloy integral ring layer to heating, heat preserving and cooling; placing the aluminum alloy equally-divided ring layer II in the annealing furnace, and subjecting the aluminum alloy equally-divided ring layer II to heating, heat preserving and cooling; and finally, placing the aluminum alloy inner conductor, the aluminum alloy equally-divided ring layer I, the aluminum alloy integral ring layer and the aluminum alloy equally-divided ring layer II in the annealing furnace after tightly compressing and twisting. The layered aluminum alloy conductor has good extensibility, good flexibility and high conductivity, so that current is evenly distributed in the conductor structure, and effective sectional area of the conductor is enlarged.

Description

technical field [0001] The invention relates to a conductor structure and an annealing process thereof, in particular to an aluminum alloy conductor and an annealing process thereof. Background technique [0002] With the development of science and technology, high-quality, high-tech aluminum materials have been developed. In addition to the current situation of copper-poor and aluminum-rich resources in the world, the price of copper is more than three times that of aluminum. It is natural to replace copper with "aluminum". s Choice. [0003] At present, the aluminum alloy conductor structure is relatively simple, and they are all single-layer round conductors. Moreover, the existing conventional aluminum alloy cable conductors are generally not annealed when used in wires and cables, and their flexibility and conductivity are poor, so their use has certain limitations. Contents of the invention [0004] Purpose of the invention: the purpose of the present invention is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01B1/02C22F1/04C22C21/00
CPCC22C21/00C22F1/04H01B1/02
Inventor 戴银辉蒋浩胡小勇
Owner WUXI SUNAN CABLE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com