Polyamide filter material and production method thereof

A technology of polyamide and filter material, which is applied in the field of polyamide filter material and its preparation, can solve the problems of complex film production process, poor filtration function and index, difficulty in practical promotion, etc., and achieve high oil-water separation ability Effect

Inactive Publication Date: 2016-07-13
XIAN TIANHOU FILTRATION TECH
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are problems that the production process of this kind of film is complicated, and other filtering functions and indicators are not good, so it is difficult to get practical promotion.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyamide filter material and production method thereof
  • Polyamide filter material and production method thereof
  • Polyamide filter material and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0077] Embodiment 1: the material is PA6; the length of the filter material cylinder is 200mm, the outer diameter of the filter material cylinder is 100mm, the thickness of the filter material cylinder is 10mm, the average pore diameter of the outer layer of the filter element cylinder is 10 μm, and the average pore diameter of the inner layer of the filter element cylinder The average diameter of melt-blown fiber filaments is 0.1 μm, and the porosity is 80.2%; the type of filter oil is gasoline; the filtration effect applied to gasoline filters: the filtration efficiency of 5-10 μm particles is 99.09%; The capacity is 60.11g, when the rated volume flow rate is 10L / min, the original flow resistance is 10kpa, and the oil-water separation rate is 98.99%.

Embodiment 2

[0078] Embodiment 2: the material is PA6; the length of the filter material cylinder is 200mm, the outer diameter of the filter material cylinder is 100mm, the thickness of the filter material cylinder is 10mm, the average pore diameter of the outer layer of the filter cartridge is 100 μm, and the average pore diameter of the inner layer of the filter cartridge is The average diameter of the melt-blown fiber is 80 μm, and the porosity is 91.2%; the type of filter oil is lubricating oil; the filtering effect applied to the oil filter: the filtration efficiency of 5-10 μm particles is 92.01%; The capacity is 122.01g, when the rated volume flow rate is 10L / min, the original flow resistance is 12.01kpa, and the oil-water separation rate is 91.88%.

Embodiment 3

[0079] Embodiment 3: the material is PA6; the length of the filter material cylinder is 200mm, the outer diameter of the filter material cylinder is 100mm, the thickness of the filter material cylinder is 10mm, the average pore diameter of the outer layer of the filter cartridge is 100 μm, and the average pore diameter of the inner layer of the filter cartridge is The average diameter of the melt-blown fiber filament is 25 μm, and the porosity is 90.2%; the type of filter oil is lubricating oil; the filtering effect applied to the oil filter: the filtration efficiency of 5-10 μm particles is 92.05%; The capacity is 101.88g, when the rated volume flow rate is 10L / min, the original flow resistance is 12.35kpa, and the oil-water separation rate is 90.53%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Average pore sizeaaaaaaaaaa
Average pore sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a polyamide filter material. The filter material adopts a hollow cylindrical structure produced through melt-blowing process treatment of a polyamide material and adhesion and winding of blown superfine fibers; the filter material adopts a loose structure and filter holes with different hole diameters are formed; the hole diameters of the filter holes sequentially and gradually decrease from the outer layer of the cylindrical structure to the inner layer. The characteristic that the polyamide material is resistant to corrosion by multiple chemical raw materials is used, melt-blowing process treatment is performed, the structure identical with that of a common polypropylene filter element is obtained, on the premise that oil and alcohol corrosion resistance of the material is guaranteed, the filter material has better filter precision, pollutant-holding capacity and circulation drag parameters, and the filter requirement of oils, chemical waste liquor and chemical waste gas is met.

Description

technical field [0001] The invention relates to a filter material, a preparation device and a preparation method thereof, in particular to a polyamide filter material used for filtering oil products, chemical waste gas and waste liquid and a preparation method thereof. Background technique [0002] During the production, transportation and storage of engine fuel, a large number of impurities will be produced and mixed. Clean fuel oil will also produce pollutants such as metal oxides, precipitated colloids, and asphaltene after storage for a period of time. Severely polluted fuel will cause wear and carbon deposits in the engine's fuel injection system and combustion chamber, resulting in increased fuel consumption and a sharp increase in exhaust emissions after the fuel engine has been used for a period of time. The current common solution is to install an oil filter on the engine to remove impurities, colloids, asphaltene and moisture in the fuel. Clean fuel can improve c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01D39/16F02M37/22B29C47/92B29C47/00B29C53/56B29C48/92
CPCB29C48/05B29C48/92B29C53/566B29C2948/92514B29C2948/92704B29C2948/92904
Inventor 张钢柱
Owner XIAN TIANHOU FILTRATION TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap