Optically transparent glue composition with organic silicone liquid and method for preparing optically transparent glue composition

An optically transparent and silicone technology, applied in the direction of adhesives, adhesive additives, non-polymer adhesive additives, etc., can solve the problems of large shrinkage rate of optically transparent glue, easy to corrode ITO, and light spots, etc., to shorten the production process and manufacturing time, reduce production costs, and increase productivity

Active Publication Date: 2016-06-22
新纶光电材料(深圳)有限公司
View PDF4 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to overcome the deficiencies of the prior art and solve the problems of acrylic resin optically transparent glue, such as large shrinkage, light spots, yellowing, and easy to corrode ITO, the present invention provides a silicone liquid optically transparent glue composition, which contains the following mass percentages: Components: Acrylate-terminated vinyl silicone oil 50%-70%, vinyl MQ silicone resin 8%-20%, vinyl MDT silicone oil 0%-20%, tackifier 0%-3%, hydrogen-containing silicone oil 0.1%~4%, photoinitiator 0.5%~3%, catalyst 0.001%~0.005%, inhibitor 0.001%~0.005%

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Optically transparent glue composition with organic silicone liquid and method for preparing optically transparent glue composition
  • Optically transparent glue composition with organic silicone liquid and method for preparing optically transparent glue composition
  • Optically transparent glue composition with organic silicone liquid and method for preparing optically transparent glue composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Weigh acrylate-terminated vinyl silicone oil, vinyl MQ silicone resin, hydrogen-containing silicone oil, 2-hydroxy-2-phenylacetophenone, and γ-methacryloxypropyltrimethoxysilane in the following proportions , 1,4-butynediol and karstedt platinum catalyst were added to the dynamic mixer respectively, stirred at a speed of 500r / min for 1h under a vacuum of -0.04MPa and a temperature of 35°C, and the obtained product was filtered , and packed into designated containers, and finally degassed by a high-speed degassing machine at a speed of 2500r / min, and finally packaged through a sealed pipe to obtain a silicone liquid optically transparent glue.

[0044] components

Embodiment 2

[0056] Weigh acrylate-terminated vinyl silicone oil, vinyl MQ silicone resin, vinyl MDT silicone oil, hydrogen-containing silicone oil, 2-hydroxy-2-phenylacetophenone, 1,4-butynediol and karstedt according to the ratios in the table below Platinum catalyst, and respectively added to the dynamic mixer, under the environment of vacuum degree of -0.04MPa, temperature of 35 ℃, stirring at the speed of 500r / min for 1h, the obtained product was filtered, and packed into the designated container, finally It is degassed by a high-speed degassing machine at a speed of 2500r / min, and finally packaged through a sealed pipe to obtain a silicone liquid optically transparent glue.

[0057]

[0058]

Embodiment 3

[0060] Weigh acrylate-terminated vinyl silicone oil, vinyl MQ silicone resin, vinyl MDT silicone oil, hydrogen-containing silicone oil, 2-hydroxy-2-phenylacetophenone, 1,4-butynediol, γ-Methacryloyloxypropyltrimethoxysilane and Karstedt platinum catalyst were added to the dynamic mixer respectively, and stirred at a speed of 500r / min for 1h at a vacuum degree of -0.04MPa and a temperature of 35°C , the obtained product is filtered and packed into designated containers, and finally degassed by a high-speed degassing machine at a speed of 2500r / min, and finally packaged through a sealed pipe to obtain a silicone liquid optically transparent glue.

[0061] components

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention provides an optically transparent glue composition with organic silicone liquid.The optically transparent glue composition mainly comprises acrylate-terminated vinyl silicone oil, vinyl MQ silicone resin, vinyl MDT silicone oil, tackifiers, hydrogen-containing silicone oil, photoinitiators, catalysts, inhibitors and the like.The invention further provides a method for preparing the optically transparent glue composition.The method includes proportionally preparing materials; blending the materials to obtain mixtures; purifying the mixtures; defoaming the mixtures at high speeds and packaging the mixtures at high speeds.The optically transparent glue composition and the method have the advantages that glue with the organic silicone liquid can be simultaneously subjected to ultraviolet curing and heat curing, accordingly, the problem of incapability of completing curing on the peripheral edges of screens at one step can be solved, production processes and the manufacturing time can be greatly shortened, the reject ratio of finished products can be reduced, and effects of saving energy and time, reducing the production cost and improving the productivity can be realized; the glue is excellent in impact resistance, bending resistance, high-temperature and high-humidity resistance and yellowing resistance and low in dimensional contraction rate after being cured; bubble and impurities in the optically transparent glue with the organic silicone liquid can be prevented by the aid of the method.

Description

technical field [0001] The invention relates to an optical adhesive and a preparation method thereof, in particular to a liquid optical adhesive and a preparation method thereof. Background technique [0002] The iPad Air 29.7 product launched by Apple in 2014 adopts full lamination technology, and the application scope of this technology has gradually spread from smartphones to medium and large-sized products such as tablets and notebook computers. Full lamination means that the panel and the touch screen are seamlessly pasted together with liquid glue or optical tape. Compared with frame paste, liquid glue or optical tape is used to fill the air layer between the touch screen and the display panel. On the one hand, it can Reduce glare and reduce the loss of light emitted by the LCD; increase the contrast (especially under strong light); improve the visibility and display performance indoors and outdoors, and the display effect is better. On the other hand, it is also help...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J183/06C09J183/07C09J183/05C09J11/06
CPCC08L2201/08C08L2201/10C08L2205/03C08L2205/035C09J11/06C09J183/06C08L83/04C08K5/5419C08K5/053C08K5/07
Inventor 张利利侯毅郭辉
Owner 新纶光电材料(深圳)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com