Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Alkali free glass

A technology of non-alkali glass and photoelastic constant, which is applied in the field of non-alkali glass, can solve the problems such as the deterioration of film properties, and achieve the effect of not easy to color unevenness, high strain point, and not easy to bend

Active Publication Date: 2020-04-14
ASAHI GLASS CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] (1) When the glass contains alkali metal oxides, the alkali metal ions diffuse into the above-mentioned thin film to deteriorate the film properties of the thin film, therefore, it is required to substantially not contain alkali metal ions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Alkali free glass
  • Alkali free glass
  • Alkali free glass

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0077] (Examples: Examples 1-6 and Examples 9-15, Comparative Examples: Examples 7-8)

[0078] Hereinafter, although an Example and a comparative example demonstrate this invention in detail, this invention is not limited to these Examples.

[0079] Raw materials of each component were prepared so that the glass composition became the target composition shown in Table 1 and Table 2 (glass composition (unit: mass %)), and melted at a temperature of 1600° C. for 1 hour using a platinum crucible. After melting, it was poured onto a carbon plate, held at the glass transition temperature + 30°C for 60 minutes, and then cooled to room temperature at 1°C per minute. The obtained glass was mirror-polished to obtain a glass plate, and various evaluations were performed.

[0080] In Tables 1 and 2, the average coefficient of thermal expansion at 50 to 350°C is shown (unit: ×10 -7 / ℃), specific gravity, Young's modulus (GPa), strain point (unit: ℃), glass transition temperature (unit:...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
strain pointaaaaaaaaaa
strain pointaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to View More

Abstract

　The present invention relates to non-alkali glass having a strain point of 680 to 735°C, an average thermal expansion coefficient at 50 to 350°C of 30 × 10-7 to 43 × 10-7 / °C, and a specific gravity of 2.60 or lower; and containing 58 to 65% SiO2, 18 to 22% Al2O3, 3 to 8% B2O3, 0 to 1.3% MgO, 6.3 to 10% CaO, 1.7 to 5% SrO, 0.5 to 5% BaO, and 0 to 2% ZrO2 by mass percentages based on oxides, where MgO + CaO + SrO + BaO is 12 to 23%, MgO / CaO is 0 to 0.2, MgO / (SrO + BaO) is 0 to 0.4, and SrO / BaO is 1.2 to 1.6.

Description

technical field [0001] The present invention relates to alkali-free glass. More specifically, it relates to an alkali-free glass suitable as various substrate glasses for displays, substrate glasses for photomasks, etc., which does not substantially contain alkali metal oxides, and which can be formed by a float method or a fusion method. Background technique [0002] Conventionally, various glass plates (glass substrates) for displays, especially glass used for glass plates on which thin films such as metals or oxides are formed on the surface, have required the following characteristics. [0003] (1) When the glass contains an alkali metal oxide, the alkali metal ions diffuse into the thin film to degrade the film properties of the thin film. Therefore, it is required that the glass does not substantially contain alkali metal ions. [0004] (2) When the glass sheet is exposed to high temperature in the film forming process, a high strain point is required in order to mini...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C3/091C03C3/093
CPCC03C3/091C03C3/093
Inventor 德永博文小野和孝
Owner ASAHI GLASS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com