Iron tower rust-protection anticorrosive conditioning fluid and preparation method thereof

Abstract

The invention relates to the field of iron tower rust protection and corrosion resistance technologies, and in particular relates to iron tower rust-protection anticorrosive conditioning fluid. The conditioning fluid is prepared from the following components in mass percent: 3 percent to 5 percent of film-forming agent, 1 percent to 3 percent of antirust agent, 3 percent to 5 percent of preservative, 2 percent to 4 percent of flatting agent, 3 percent to 5 percent of antioxidant, 4 percent to 6 percent of compound cleaning agent and 3 percent to 5 percent of corrosion inhibitor. The invention also discloses a preparation method of the iron tower rust-protection anticorrosive conditioning fluid. By adopting the iron tower rust-protection anticorrosive conditioning fluid, cleaning, corrosion prevention and rust protection can be finished in one step, a rust layer of an iron tower can be transformed, the construction process is simple, the corrosion prevention effect is good, and the conditioning fluid can be applied to an iron tower rust protection and corrosion resistance treatment process on a large scale.

Description

technical field [0001] The invention relates to the field of iron tower antirust and anticorrosion technology, in particular to an iron tower antirust and anticorrosion treatment liquid and a preparation method thereof. Background technique [0002] Generally, there is a layer of hot-dip galvanizing on the outer layer of traditional steel towers, but it is easy to blacken and crack after a long time, and galvanized is easy to rust, which reduces the strength of the tower components and affects their service life; some use Fluorocarbon coating is preferred, but its cost is high and it is not suitable for wide application, so there is no better solution. [0003] Transmission line towers are often made of hot-dip galvanized ordinary carbon steel. Part of the hot-dip galvanized surface is corroded during its operation. In severe cases, the galvanized layer is completely corroded and damaged, endangering the safe operation of the transmission line. Therefore, the rusted transmi...

AI Technical Summary

Problems solved by technology

Manual derusting or pickling is not easy to damage the protective zinc layer on the surface of the iron tower, and will cause environmental pollution

Both methods are difficult to completely remove rust, and are easy to rust and wrinkle. After treatment, there is no protective effect on the iron tower, and the paint surface does not adhere well. The outer layer is easy to foam after being encapsulated with paint, and the protection period is short.