Apparatus for rapid measurement of grain size and magnetic domain wall width of grain-oriented silicon steel sheets

A technology of grain-oriented silicon steel and grain size, which is applied in the field of analysis and detection devices for grain-oriented silicon steel sheets, can solve the problems of waste, complicated magnetic field, and complicated grain-size changes of grain-oriented silicon steel, so as to achieve the effect of rapid magnetization and avoid mutual pollution.

Active Publication Date: 2018-07-03
武汉钢铁有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The above-mentioned device mainly has the following disadvantages: ①The sample size is limited, and only smaller samples can be observed, while the grain changes of grain-oriented silicon steel are relatively complicated, and it is difficult for small-sized samples to represent the actual situation of large-sized samples; ② The observation suspension is in direct contact with the sample, and it cannot be reused after use, which is wasteful, and it takes time and effort to repeatedly configure the suspension; ③ Due to the intermediate magnetic field formed by the double-sided winding, the magnetic field at the center is more complicated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Apparatus for rapid measurement of grain size and magnetic domain wall width of grain-oriented silicon steel sheets
  • Apparatus for rapid measurement of grain size and magnetic domain wall width of grain-oriented silicon steel sheets
  • Apparatus for rapid measurement of grain size and magnetic domain wall width of grain-oriented silicon steel sheets

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] The present invention will be further described in detail below in conjunction with the accompanying drawings and specific embodiments.

[0026] Such as figure 1 Shown is a device for measuring the grain size and magnetic domain wall width of grain-oriented silicon steel sheets in the prior art, and its structure has been described in detail in the background technology section, and will not be repeated here.

[0027] Such as Figure 2-4 As shown, the device designed by the present invention for quickly measuring the grain size and magnetic domain wall width of grain-oriented silicon steel sheets mainly includes two independent parts of the display part 1 and the sample stage 17, and the display part 1 includes a display window 12 and contact layer 13. The display window 12 is a rectangular transparent hard plastic plate, and a handle 9 is respectively arranged on both sides thereof. The contact layer 13 is a wear-resistant flexible plastic film, and its periphery is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a device for rapidly measuring grain size and magnetic domain wall width of oriented silicon steel sheet, which comprises a sample stage and a displaying part; the displaying part includes a display window and a contact layer, and the display window is transparent A glass plate or a transparent hard plastic plate, a liquid storage cavity for filling the visible suspension is formed between the display window and the contact layer; The suspension injection hole, and the closed air hole of the liquid storage chamber used to balance the pressure in the liquid storage chamber, the suspension injection hole and the closed air hole of the liquid storage chamber can be opened or closed as required; the sample table is provided with a magnetic The yoke is provided with a magnetizing winding, and when the magnetizing winding is energized, the oriented silicon steel sample placed on the sample stage can be magnetized. The device adopts the principle of powder grain method, which can quickly and accurately measure the grain size and magnetic domain wall width of grain-oriented silicon steel sheets.

Description

technical field [0001] The invention relates to an analysis and detection device for an oriented silicon steel sheet, in particular to a device for rapidly measuring the grain size and the width of a magnetic domain wall of an oriented silicon steel sheet. Background technique [0002] Silicon steel is a very important functional metal material, especially grain-oriented silicon steel, which has always been known for its complicated preparation process and high technical requirements. The loss of grain-oriented silicon steel is one of the core performance evaluation bases. [0003] Long-term studies have found that the loss of grain-oriented silicon steel is closely related to its grain size and magnetic domain wall width. If the grain size is too small, the grain boundaries will increase relatively, and the hysteresis loss will increase significantly during the repeated magnetization process. However, if the grain size is too large, the domain wall motion speed will increa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N15/02G01N15/10
Inventor 党宁员姚腊红胡守天朱业超程祥威周前华
Owner 武汉钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com