Bicolor Eu-MOFs/CDs fluorescent material as well as preparation and application thereof

A two-color fluorescence, eu-mofs technology, applied in luminescent materials, fluorescence/phosphorescence, material excitation analysis, etc., can solve problems such as unsatisfactory sensitivity of fluorescence sensors, and achieve the effects of convenient post-processing, low cost investment, and simple synthesis route.

Inactive Publication Date: 2016-01-06
FUZHOU UNIV
View PDF2 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, fluorescent materials such as rhodamine, allyl acridine orange, naphthalimide and their derivatives all have good responses to water, and sensors prepared based on these dyes have also achieved good results in the detection of water content. However, the current fluorescent sensors still have the disadvantage of unsatisfactory sensitivity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bicolor Eu-MOFs/CDs fluorescent material as well as preparation and application thereof
  • Bicolor Eu-MOFs/CDs fluorescent material as well as preparation and application thereof
  • Bicolor Eu-MOFs/CDs fluorescent material as well as preparation and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] 26mLDMF, 2mL cyclohexanol and 2mL distilled water were mixed as solvent; 33.8mg europium nitrate (Eu(NO 3 ) 3 ), 21mgH 3 BTC and 2.4mg of carbon-based quantum dots co-doped with nitrogen and sulfur elements (N,S-CDs) were dissolved in the obtained solvent; 3 Adjust the solution to a pH value of 5; stir the prepared mixed solution at room temperature for 2 hours, put the mixed solution in an oven, heat it to 85°C under normal pressure and keep it reacting for 16 hours; After washing with DMF and ethanol and centrifuging three times, Eu-MOFs / N,S-CDs two-color fluorescent material was obtained by vacuum drying at 80°C for 5 hours, which is based on the fluorescence colorimetry of rare earth metal organic framework complex-carbon-based quantum dot organic solvent water content sensor.

Embodiment 2

[0037] 18mL of DMF, 6mL of cyclohexanol and 6mL of distilled water were mixed as solvent; 2.6mg of europium chloride (EuCl 3 ), 2.1mgH 3 BTC and 0.3mg of carbon-based quantum dots co-doped with nitrogen and sulfur elements (N,S-CDs) were dissolved in the obtained solvent; 3 Adjust the solution to a pH value of 4; stir the prepared mixed solution at room temperature for 0.5 hours, then place the mixed solution in an oven, heat it to 60°C under normal pressure, and keep the reaction for 48 hours; centrifuge after the reaction, and the obtained precipitate Washed with DMF and ethanol in sequence, centrifuged three times, and vacuum-dried at 50°C for 5 hours to prepare Eu-MOFs / N,S-CDs two-color fluorescent material, which is based on rare earth metal organic framework complex-carbon-based quantum dot organic solvent water content fluorescence Colorimetric sensor.

Embodiment 3

[0039] 27mLDMF, 2.7mL cyclohexanol and 0.3mL distilled water were mixed as solvent; 446mg europium nitrate hexahydrate (Eu(NO 3 ) 3 ·6H 2 O), 210mgH 3 BTC and 24mg of carbon-based quantum dots (N,S-CDs) co-doped with nitrogen and sulfur elements were dissolved in the obtained solvent; 3 Adjust the pH value of the solution to 6; stir the prepared mixed solution at room temperature for 5 hours, then transfer the mixed solution to a hydrothermal reaction kettle with a polytetrafluoroethylene liner and heat it to 100°C, and keep the reaction for 2 hours; after the reaction is completed After centrifugation, the resulting precipitate was washed with DMF and ethanol in sequence, and after centrifugation three times, it was vacuum-dried at 100°C for 2 hours to obtain Eu-MOFs / N,S-CDs two-color fluorescent material, which is based on rare earth metal organic framework complex-carbon-based quantum dot organic Fluorescent colorimetric sensor for solvent water content.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a bicolor Eu-MOFs / CDs fluorescent material as well as preparation and an application thereof. Europium ions, trimesic acid and carbon quantum dots are used as raw materials, and the bicolor fluorescent material is prepared through heat treatment in a solvent prepared by mixing N,N-dimethylformamide, distilled water and cyclohexanol. Under irradiation of ultraviolet lamps, the material can emit red fluorescence when dispersed in organic solvents and can emit blue fluorescent when dispersed in water, so that fluorescent colorimetric sensors for measuring water content in organic solvents can be prepared from the material, the prepared sensors are high in sensitivity, good in stability and low in cost and have higher population value and brighter application prospect.

Description

technical field [0001] The invention belongs to the field of material preparation, and in particular relates to a Eu-MOFs / CDs two-color fluorescent material and a preparation method and application thereof. Background technique [0002] Metal-organic frameworks (Metal-Organic Framworks, MOFs) is the fastest-growing direction of coordination chemistry in the past ten years, and it is a new scientific research topic involving inorganic chemistry, organic chemistry and coordination chemistry. MOFs generally refer to crystalline materials with periodic grid structures formed by the connection of inorganic clusters and organic ligands. MOFs are mostly composed of carboxylic acid organic ligands and metal ions. This kind of material has high porosity, large adsorption capacity, good thermal stability, various organic and inorganic components in its structure, and relatively simple synthesis method. As an important class of hybrid inorganic-organic materials, MOFs have attracted ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K11/06C09K11/65G01N21/64
Inventor 董永强池毓务蔡建华
Owner FUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com