Production method of pad cotton of cover plate of automobile spare tire

A technology for automobile spare tire cover and production method, which is applied in the directions of non-woven fabrics, textiles, papermaking, adhesives, etc., can solve the problems of tearing, poor tensile properties, poor production environment, substandard formaldehyde content, etc., and achieves improvement. Odor, reduce dust rate, improve the effect of production environment

Inactive Publication Date: 2015-11-18
WUXI GISSING AUTO ACOUSTIC PARTS TECH CO LTD
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing spare tire cover pad cotton mainly has the following problems: 1. The formaldehyde content is not up to the standard; 2. The tearing and tensile properties are poor; 3. The odor and dust performance are not up to the standard; 4. The production environment is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Production of GAC Fiat 343CHB spare board pad, its specifications are: L952mm×W727mm×H12mm, gram weight is 300g / m 2 , the production method of this type of automobile spare tire cover pad cotton comprises the following steps:

[0021] a. Weigh 3600g of cotton fiber, 900g of low melting point fiber and 200g of polyester fiber and mix the three fibers together to form a mixed fiber, and the cotton fiber contains 25% of the total weight of flame retardant cotton, low melting point The fiber is selected from low melting point fiber with 3~12 denier and length of 40~60mm, and the polyester fiber is selected from polyester fiber with 3~12 denier and length of 40~60mm;

[0022] b. Put the mixed fibers into the pre-opening equipment for pre-opening, and the feeding speed of the pre-opening equipment is controlled at 2 m / s;

[0023] c. Put the pre-opened mixed fibers into the fine-opening equipment for fine-opening, and the feeding speed of the fine-opening equipment is control...

Embodiment 2

[0031] Production of Anhui Chery A16 backing pad cotton, its specifications are: L852mm×W600mm×H12mm, gram weight is 1500g / m 2 , the production method of this type of automobile spare tire cover pad cotton comprises the following steps:

[0032] a. Weigh 3900g of cotton fiber, 1200g of low melting point fiber and 350g of polyester fiber and mix the three fibers together to form a mixed fiber, and the cotton fiber contains 35% of the total weight of flame retardant cotton, low melting point The fiber is selected from low melting point fiber with 3~12 denier and length of 40~60mm, and the polyester fiber is selected from polyester fiber with 3~12 denier and length of 40~60mm;

[0033] b. Put the mixed fibers into the pre-opening equipment for pre-opening, and the feeding speed of the pre-opening equipment is controlled at 4 m / s;

[0034] c. Put the pre-opened mixed fibers into the fine-opening equipment for fine-opening, and the feeding speed of the fine-opening equipment is co...

Embodiment 3

[0042] Production of Anhui Chery T21 backing pad cotton, its specifications are: L950mm×W750mm×H15mm, gram weight is 700g / m 2 , the production method of this type of automobile spare tire cover pad cotton comprises the following steps:

[0043] a. Weigh 3800g of cotton fiber, 1000g of low-melting fiber and 280g of polyester fiber and mix the three fibers together to form a mixed fiber;

[0044] b. Put the mixed fibers into the pre-opening equipment for pre-opening, and the feeding speed of the pre-opening equipment is controlled at 3 m / s;

[0045] c. Put the pre-opened mixed fibers into the fine-opening equipment for fine-opening, and the feeding speed of the fine-opening equipment is controlled at 1.2 m / s;

[0046] d. Put the finely opened mixed fibers into the homogenizer for homogenization and weighing. The gram weight parameter of the homogenizer is set at 700g / m2 2 ;

[0047] e. Put the uniformly weighed mixed fibers into the air-laid machine to form a web to form a fe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a production method of pad cotton of a cover plate of an automobile spare tire. The production method comprises following steps of material weighing; pre-opening; precise opening; even and orderly weighing; material spreading and net forming; drying at a set temperature; cold rolling and shaping; and cutting. In this way, problems of excessive formaldehyde, horizontal and longitudinal tearing and poor stretching performance of pad cotton of a spare tire are solved; dust producing rate of a hair felt is reduced; small of the product is improved; and production environment is improved.

Description

technical field [0001] The invention discloses a production method of an automobile spare tire cover pad and belongs to the technical field of automobile interior trim production. Background technique [0002] Spare tire cover pad is a material installed under the car spare tire cover, which plays the role of heat insulation, sound insulation, sound absorption and shock absorption. In the era of more and more pursuit of high performance, environmental protection, energy saving, light weight and personalization, the interior of the car, like the appearance of the car, has become an important factor for people to buy a car. Therefore, the requirements for automotive interior parts are getting higher and higher. In the prior art, performance indicators such as odor, formaldehyde content, dust content, and appearance of the spare tire cover pad have become bottlenecks, restricting the development of the spare tire cover pad. The existing spare tire cover pads mainly have the f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D04H1/4382D04H1/435D04H1/425D04H1/542
Inventor 赵云陈奇张丛见
Owner WUXI GISSING AUTO ACOUSTIC PARTS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap