Silica-calcia low-grade collophanite positive and inverse floatation process

A positive and negative flotation, low-grade technology, applied in flotation, solid separation, etc., can solve the problems of content reduction, difficulty in obtaining phosphorus concentrate, etc., and achieve the effect of improving utilization rate

Active Publication Date: 2015-09-16
WUHAN INSTITUTE OF TECHNOLOGY +1
View PDF9 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In phosphate rock flotation, direct flotation and single reverse flotation can only reduce the content of one of the gangue minerals, and it is difficult to obtain low-magnesium, low-sesquioxide, and low-silicon phosphorus concentrate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Silica-calcia low-grade collophanite positive and inverse floatation process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Embodiment 1: A kind of forward and reverse flotation process of siliceous calcareous colloidal phosphate rock, its steps are as follows:

[0021] 1) Silicon-calcium colloidal phosphate rock is crushed and ground to dissociate the mineral monomers, and the slurry is adjusted to a mass concentration of 20%, and then flows into the mixing tank, and the amount of 3.0kg / t raw ore is added to the slurry Sodium carbonate, 6.0kg / t raw ore water glass, adjust the pH value of the pulp to 9, and then add the fatty acid soap anionic collector MXO-135 with an amount of 2.0kg / t raw ore containing amide groups to adjust the pulp, and the pulp temperature is 20°C, after pulping, enter the positive flotation operation for aerated flotation, phosphate ore, carbonate minerals and some iron-aluminosilicate minerals enter the positive flotation foam product, and the positive flotation tailings are in the tank;

[0022] 2) The flotation foam flows into the reverse flotation stirring tank, a...

Embodiment 2

[0023] Embodiment 2: A kind of forward and reverse flotation process of siliceous calcareous colloidal phosphate rock, its steps are as follows:

[0024] 1) Silicon-calcium colloidal phosphate rock is crushed and ground to dissociate the mineral monomers, and the slurry is adjusted to a mass concentration of 40%, and then flows into the mixing tank, and the amount of 8.0kg / t raw ore is added to the slurry Sodium carbonate, the dosage is 0.5kg / t raw ore water glass, adjust the pH value of the pulp to 11, and then add the fatty acid soap anionic collector MXO-135 with an dosage of 0.5kg / t raw ore containing amide groups to adjust the pulp, the pulp The temperature is 35°C. After the slurry is adjusted, it enters the positive flotation operation for aerated flotation. Phosphate ore, carbonate minerals and some iron-aluminosilicate minerals enter the positive flotation foam product, and the positive flotation tailings are in the tank;

[0025] 2) The flotation foam flows into the ...

Embodiment 3

[0026] Embodiment 3: a kind of siliceous calcareous colloidal phosphate rock positive and negative flotation process, its steps are as follows:

[0027] 1) Silica-calcium colloidal phosphate rock is crushed and ground to dissociate the mineral monomers, and the slurry is adjusted to a mass concentration of 30%, and then flows into the mixing tank, and the amount of 5.5kg / t raw ore is added to the slurry Sodium carbonate, the dosage is 3.5kg / t raw ore water glass, adjust the pH value of the pulp to 10.25, and then add the fatty acid soap anionic collector MXO-135 with an dosage of 1.2kg / t raw ore containing amide groups to adjust the pulp. The temperature is 25°C. After the slurry is adjusted, it enters the positive flotation operation for aerated flotation. Phosphate ore, carbonate minerals and some iron-aluminosilicate minerals enter the positive flotation foam product, and the positive flotation tailings are in the tank;

[0028] 2) The flotation foam flows into the reverse ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a silica-calcia low-grade collophanite positive and inverse floatation process, which comprises the steps: 1 silica-calcia low-grade collophanite ores are broken up and grinded to enable phosphate minerals and gangue mineral monomers to dissociate, then are added with water to mix size, enter positive and inverse floatation, get rid of impurities in ores, and improve grade of phosphorite. Compared with the prior art, the silica-calcia low-grade collophanite positive and inverse floatation process has the advantages that the content of only one kind of gangue minerals can be reduced by adopting direct floatation and single inverse floatation, can reduce the contents of silicate minerals, carbonate minerals and iron and aluminum silicate minerals, can obtain low magnesium low power half oxide low silicon phosphate concentrate by adopting the silica-calcia low-grade collophanite positive and inverse floatation process, successfully achieves mineral processing enrichment of collophane calcium collophanite, and can improve use rate of phosphorus resource. The silica-calcia low-grade collophanite positive and inverse floatation process overcomes the defects that an existing floatation process can not be applied for mineral processing of silica-calcia collophanite which is high in content of high power half oxides.

Description

technical field [0001] The invention relates to a forward and reverse flotation process of silicon-calcium low-grade colloidal phosphate rock. Background technique [0002] Phosphate rock is a non-renewable basic raw material for the production of phosphate fertilizers and phosphorus chemical products. my country is rich in phosphate rock, with a resource reserve of 16.786 billion tons and an average grade of 16.95%. The high-grade (30%) ore that can be directly used can only be mined for more than ten years. It is complex, finely distributed, poor dissociation, and high in gangue minerals such as silicate minerals, carbonate minerals, and sesquioxides. Its development and utilization is a worldwide problem. In phosphate rock flotation, direct flotation and single reverse flotation can only reduce the content of one of the gangue minerals, and it is difficult to obtain low-magnesium, low-sesquioxide, and low-silicon phosphate concentrate. Contents of the invention [0003...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B03D1/02
Inventor 罗惠华李亮陈慧瞿定军饶欢欢杨婕刘连坤朱道鹏汤家焰苗华军侯慧芳张战利
Owner WUHAN INSTITUTE OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com