Novel amphiphilic block acrylic resin retanning agent and preparation method thereof

An acrylic resin, amphiphilic block technology, applied in animal husbandry, chemical treatment of small raw hides/large raw hides/leather hides/furs, applications, etc., to achieve the effect of excellent acid resistance and stability

Inactive Publication Date: 2015-08-19
山东黎宁科技新材料有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are few reports on the preparation of amphiphilic block acrylic resin retanning agents by RAFT emulsion polymerization technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel amphiphilic block acrylic resin retanning agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] 1. Reversible addition-fragmentation chain transfer radical polymerization of acrylic acid: 90 parts of acrylic acid, 4.5 parts of RAFT reagent, 0.9 part of 4,4'-azobis(4-cyanovaleric acid) (V501), 0.5 part of carbonic acid Add sodium hydrogen, 256.7 parts of deionized water and 5 parts of mixed emulsifier into the reaction kettle, heat up to 80°C, and react for 3 hours to obtain polyacrylic acid macromolecule RAFT reagent; 2. Synthesis of amphiphilic block acrylic resin retanning agent: Continue to add 0.45 parts of 4,4'-azobis(4-cyanovaleric acid) (V501) to the reactor, add 10 parts of lauryl acrylate dropwise into the reactor within 2 hours, and continue the reaction after the addition is complete After 4 hours, after the reaction was completed, an amphiphilic block acrylic resin retanning agent was obtained.

Embodiment 2

[0018] 1. Reversible addition-fragmentation chain transfer radical polymerization of acrylic acid: 90 parts of acrylic acid, 4.5 parts of RAFT reagent, 0.9 part of 4,4'-azobis(4-cyanovaleric acid) (V501), 0.5 part of carbonic acid Add sodium hydrogen, 256.7 parts of deionized water and 5 parts of mixed emulsifier into the reaction kettle, heat up to 80°C, and react for 3 hours to obtain polyacrylic acid macromolecule RAFT reagent; 2. Synthesis of amphiphilic block acrylic resin retanning agent: Continue to add 0.45 parts of 4,4'-azobis(4-cyanovaleric acid) (V501) to the reactor, and add 10 parts of lauryl methacrylate dropwise into the reactor within 2 hours. The reaction was continued for 4 hours, and after the reaction was completed, an amphiphilic block acrylic resin retanning agent was obtained.

Embodiment 3

[0020] 1. Reversible addition-fragmentation chain transfer radical polymerization of methacrylic acid: 80 parts of methacrylic acid, 4 parts of RAFT reagent, 0.8 part of 4,4'-azobis(4-cyanovaleric acid) (V501) , 0.5 parts of sodium bicarbonate, 255.5 parts of deionized water and 5 parts of mixed emulsifier were added to the reaction kettle, the temperature was raised to 80°C, and the reaction was carried out for 3 hours to obtain a polymethacrylic acid macromolecule RAFT reagent; 2. Amphiphilic block acrylic resin Synthesis of retanning agent: continue to add 0.4 parts of 4,4'-azobis(4-cyanovaleric acid) (V501) to the reaction kettle, and drop 20 parts of lauryl acrylate into the reaction kettle dropwise within 2 hours After the addition, the reaction was continued for 4 hours. After the reaction was completed, an amphiphilic block acrylic resin retanning agent was obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a novel amphiphilic block acrylic resin retanning agent and a preparation method thereof. The invention is characterized in that the preparation method comprises the following steps: 1. (methyl) acrylic acid reversible addition-fragmentation chain transfer free-radical polymerization; and 2. synthesis of amphiphilic block acrylic resin retanning agent. The amphiphilic block acrylic resin retanning agent is a milk white thick liquid in appearance, the pH value is 3.0, and the effective substance content is 20-30 wt%. The product has the advantages of favorable acid-resistant stability, favorable alkali-resistant stability and favorable storage stability, enhances the absorption of the wet blue leather for the chrome tanning agent, enables the crust leather grain surface to be fine, compact and full, and obviously enhances the tearing strength of the crust leather.

Description

technical field [0001] The invention relates to the technical field of leather retanning technology, in particular to a novel amphiphilic block acrylic resin retanning agent and a preparation method thereof. Background technique [0002] In the leather industry, the retanning process is very important because it can make up for many defects of chrome tanning. Among the many types of retanning agents, the retanning agents based on acrylic monomers have been widely studied and applied. For decades, acrylic resin retanning agents can endow chrome tanned leather with various value-added properties, such as fullness, elasticity, and grain fullness; in recent years, amphiphilic acrylic resins with retanning and fatliquoring functions Tanning agents have attracted widespread attention; amphiphilic acrylic resin retanning agents are usually composed of hydrophilic and hydrophobic two parts, wherein the hydrophilic group (such as carboxyl) reacts with trivalent chromium in wet blue l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F293/00C08F220/18C08F2/26C08F2/30C14C3/22
Inventor 陈煜坤魏延伟
Owner 山东黎宁科技新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com