Low-water-adsorbing cable material for high-speed railway motor train unit and preparation method of low-water-adsorbing cable material
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology for high-speed railways and EMUs, which is applied to insulated cables, cables, circuits, etc., can solve problems such as hindering safe evacuation and fire-fighting work, unable to meet market demand, loss of life and property, etc., achieving superior water resistance, low water absorption, Good thermal stability
Inactive Publication Date: 2015-07-29
ANHUI KANGLIYA CO LTD
View PDF3 Cites 9 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
When the cable burns, it releases a large amount of smoke and toxic and corrosive gas, which seriously hinders people's safe evacuation and fire fighting work, causing serious loss of life and property.
At the same time, the cable materials for high-speed railway EMUs currently on the market still have the disadvantage of high water absorption, which leads to their short service life and cannot meet market demand.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0015] A low-water-absorbing cable material for high-speed railway EMUs, made of the following raw materials (kg): polypropylene 86, polybutylene terephthalate 52, chloroether resin 33, vaseline 4, crystalline silica powder 24 , Tridecafluorooctyltriethoxysilane 5, p-hydroxybenzoic acid hydrazide 1.5, zinc pyrrolidone carboxylate 3, stannous octoate 2.5, glyceryl tristearate 5, calcined kaolin 18, tribasic butene Lead diacid 3.5, α-phenylindole 1.5, composite flame retardant 24, antioxidant 1520 2;
[0016] The preparation method of described composite flame retardant is as follows:
[0017] (1) Take palygorskite, attapulgite and barium metaborate according to the ratio of mass ratio 5:3:2, mix uniformly, pulverize, pass through a 150 mesh sieve, and then ball mill at 650r / min for 1h;
[0018] (2) Add water to the powder obtained by the above ball mill and stir to prepare a suspension with a concentration of 50g / L, and then add a certain volume of 1mol / L Mg(NO 3 ) 2 solutio...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a low-water-absorbing cable material for a high-speed railway motor train unit and a preparation method of the Low-water-adsorbing cable material. The low-water-absorbing cable material for the high-speed railway motor train unit comprises the following raw materials in parts by weight: 81 to 92 parts of polypropylene, 43 to 55 parts of polybutylene terephthalate, 27 to 39 parts of poly (vinyl chloride co-isobutyl vinyl ether), 3 to 5 parts of vaseline, 22 to 26 parts of crystal silicon micro-powder, 4 to 6 parts of triethoxy-1H,1H,2H,2H-tridecafluoro-n-octylsilane, 1 to 2 parts of 4-hydroxybenzoic acid hydrazide, 3 to 4 parts of zinc pyrrolidone carboxylic acid, 2 to 3 parts of stannous octoate, 4 to 6 parts of glyceryl tristearate, 15 to 20 parts of calcined kaolin, 3 to 4 parts of lead maleate tribasic, 1 to 2 parts of alpha-phenylindole, 21 to 27 parts of a composite fire retardant, and 1.5 to 2.5 parts of an anti-oxidant 1520. The cable material produced by the preparation method provided by the invention is low in water absorption and superior in water resistance, further has excellent performance such as high intensity, excellent thermal stability, shock resistance, aging resistance, corrosion resistance, fatigue resistance, environment friendliness and flame retardance, and the like, and has a very wide application prospect.
Description
technical field [0001] The invention relates to a cable material, in particular to a low water-absorbing cable material for high-speed railway EMUs and a preparation method thereof. Background technique [0002] With the rapid development of the economy, wires and cables have been widely used in the high-speed railway motor car industry. In recent years, electrical fire accidents of high-speed railway trains have occurred frequently, and the flame retardant problem of wires and cables has gradually attracted the attention of countries all over the world. When the cable burns, it releases a large amount of smoke and toxic and corrosive gas, which seriously hinders people's safe evacuation and fire fighting work, causing serious loss of life and property. At the same time, the cable materials for high-speed railway EMUs currently on the market generally have the disadvantage of high water absorption, which leads to short service life and cannot meet market demand. Therefore,...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.