Glass-welded plane double-vacuum-layer glass having installing holes at edge sealed by sealing strips

A sealing strip and double vacuum technology, applied in the field of flat double vacuum layer glass and its production, to achieve the effects of high sealing strength and air tightness, eliminating variable deformation and eliminating edge sealing stress

Inactive Publication Date: 2015-07-01
戴长虹
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a flat double-vacuum laminated glass with sealing strip and edge sealing glass welded with installation holes and its manufacturing method for the defects existing in the existing vacuum glass. This vacuum glass and its manufacturing method are Simple, high production efficiency, the prepared tempered vacuum glass can not only eliminate the edge sealing stress but also maintain the tempered characteristics of tempered glass, can produce tempered vacuum glass in large quantities, and can increase its service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass-welded plane double-vacuum-layer glass having installing holes at edge sealed by sealing strips

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0040] Embodiment: Referring to the accompanying drawings, the plane double-vacuum laminated glass is composed of upper glass 1, middle glass 9 and lower glass 2. Among the three glasses, at least the upper and lower glasses are tempered glass or semi-tempered glass, and at least one of the glasses is still low. Radiation glass, its production method is as follows: first according to the shape and size of the plane double vacuum layer glass that needs to be made, cut three pieces of flat glass of the required size, and drill at the corners of the upper glass 1, the middle glass 9 and the lower glass 2 One through hole is the installation hole 3, wherein the through hole on the upper glass 1 is larger than the through hole on the middle glass 9, and the three glasses are ground, chamfered, cleaned and dried; secondly, the upper glass 1 and the lower glass 2 Print and prepare the sealing strips 5 and 6 at the peripheral welding place of the intermediate glass 9 and the periphery ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a glass-welded plane double-vacuum-layer glass having installing holes at edge sealed by sealing strips, which comprises an upper glass, a lower glass and an intermediate glass, the installing holes are provided, 1-4 installing holes are provided, at least a sealing strip is respectively provided at lower surface circumference of the upper glass and the intermediate glass and the circumference of the installing hole, at least two sealing strips are provided at upper surface circumference of the intermediate glass and the lower glass, at least a sealing strip is arranged at the lower glass corresponding to the installing hole, three glasses are rapidly heated, and the circumference can be welded together by pressurizing through a glass solder in a vacuum furnace. The vacuum glass and its production method have the advantages that the process is simple and the production efficiency is high, the prepared vacuum glass can eliminate the stress of the sealed edge and can keep the toughening characteristic of the toughened glass, large-batch production of toughened vacuum glass is realized, and usage life is increased.

Description

technical field [0001] The invention relates to the technical field of glass deep processing, in particular to a plane double-vacuum-layer glass with sealing strip edge-sealing glass welded with installation holes and a manufacturing method thereof. Background technique [0002] As a new type of glass with the most energy-saving potential, vacuum glass has achieved large-scale production after more than ten years of research and development, and has been well applied in many fields, especially in the construction field; but there are also obvious The shortcomings are mainly low production efficiency, small production capacity, and inability to produce tempered vacuum glass, etc., which limit its popularization and application in a wider range; the existing large-scale production of vacuum glass uses high temperature (430-480°C) normal pressure The production process of lower edge sealing, low temperature (180-300°C) vacuuming and sealing, because it needs to be kept warm for...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03B23/24
CPCY02P40/57
Inventor 戴长虹
Owner 戴长虹
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products