A kind of ag alloy heat insulation film and preparation method thereof

A technology of thermal insulation film and alloy, applied in chemical instruments and methods, metal layered products, synthetic resin layered products, etc., can solve the problems of easy oxidation of metal Ag film, low production efficiency, low deposition rate, etc. Spectral selective transmittance, high production efficiency, high infrared blocking effect

Active Publication Date: 2017-03-29
青岛久越新材料科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As far as the development trend of heat insulation film products is concerned, good heat insulation performance must also have high visible light transmittance. At present, precious metals and TiO2 can achieve this requirement. 2 Or a multilayer composite film of a dielectric film such as ITO, but due to TiO 2 The deposition rate of the dielectric film is very low, that is, the production efficiency is very low and the price is very high, which is not conducive to popularization
As far as the general metal film is concerned, high visible light transmittance and high heat insulation performance are contradictory. Through appropriate methods and processes, noble metal Ag film can achieve high visible light transmittance and good insulation performance to varying degrees. Thermal performance, but the metal Ag film has weather resistance problems such as easy oxidation and vulcanization

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ag alloy heat insulation film and preparation method thereof
  • A kind of ag alloy heat insulation film and preparation method thereof
  • A kind of ag alloy heat insulation film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Select the substrate PET with a thickness of 100 μm, and use a roll-to-roll magnetron sputtering coating machine equipped with a magnetron sputtering medium-frequency twin target. When the substrate PET passes through several coating areas with good airtight isolation with the coating roller rotation On its other side, nickel-chromium alloy (Ni80%Cr20%) with a thickness of 0.2nm, silver-copper alloy (Ag92.5%Cu7.5%) with a thickness of 5nm and nickel-chromium alloy with a thickness of 0.2nm ( Ni80%Cr20%) three-layer film, namely the Ag alloy heat insulation film.

[0036] In this embodiment, a winding magnetron sputtering multi-target coating machine is used, and the specific process parameters are listed in the following table:

[0037]

Embodiment 2

[0039] Select the substrate PET with a thickness of 13 μm, and use a roll-to-roll magnetron sputtering coating machine equipped with a magnetron sputtering intermediate frequency twin target. When the substrate PET passes through several coating areas with good airtight isolation with the coating roller On the other side, nickel-chromium alloy (Ni80%Cr20%) with thickness of 3nm, silver-copper alloy (Ag92.5%Cu7.5%) with thickness of 15nm and nickel-chromium alloy with thickness of 3nm (Ni80% Cr20%) three-layer film, namely the Ag alloy heat insulation film.

[0040] In this embodiment, a winding magnetron sputtering multi-target coating machine is used, and the specific process parameters are listed in the following table:

[0041]

Embodiment 3

[0043] Select the substrate PET with a thickness of 80 μm, and use a roll-to-roll magnetron sputtering coating machine equipped with a magnetron sputtering intermediate frequency twin target. When the substrate PET rotates with the coating roller and passes through several coating areas with good airtight isolation , on the other side, successively plate nickel-chromium alloy (Ni80%Cr20%) with a thickness of 1nm, silver-copper alloy (Ag92.5%Cu7.5%) with a thickness of 8nm and nickel-chromium alloy (Ni80%Cu7.5%) with a thickness of 1nm Cr20%) three-layer film, namely the Ag alloy heat insulation film.

[0044] In this embodiment, a winding magnetron sputtering multi-target coating machine is used, and the specific process parameters are listed in the following table:

[0045]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a Ag alloy heat-insulating film and a preparation method thereof. The heat-insulating film comprises a base material PET (Polyethylene Glycol Terephthalate), a first NiCr film coating layer, a second Ag alloy film coating layer, and a third NiCr film coating layer. The preparation method for the heat-insulating film comprises the following steps: on a reel-to-reel flexible magnetron sputtering coating machine, when the base material PET is rotated along with a film coating roller, plating NiCr, Ag alloy and NiCr three film layers on the other side of the base material PET through film coating areas of different targets. The Ag alloy heat-insulating film disclosed by the invention has the advantages of being high in visible light transmission, high in infrared ray resistance, good in weather resistance, high in production efficiency, low in cost and the like, so that the application field of the heat-insulating film is widened, the market area is enlarged, and development of the heat insulating film towards energy conservation and environment protection direction is promoted.

Description

technical field [0001] The invention belongs to the field of building and automobile film, and in particular relates to an Ag alloy heat-insulating film with spectrally selective permeability and a preparation method thereof. Background technique [0002] With the development of science and technology, the improvement of people's living standards and the concept of "low-carbon life", the performance requirements for thermal insulation films are getting higher and higher, and the demand is gradually increasing. At present, thermal insulation film has been widely used in the curtain wall glass of large buildings and the window glass of automobiles. Using it on the curtain wall glass of a large building can greatly reduce the cost of air conditioning, and make the appearance of the building have a beautiful color. At present, most of the car window glass is pasted with thermal insulation film, which reduces the damage of ultraviolet rays to the human body and interior decorati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B15/04B32B27/36B32B33/00C23C14/35C23C14/56C23C14/20
Inventor 谈琦
Owner 青岛久越新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products