Problems solved by technology

[0002] When using metal mold centrifugal casting technology to produce the cylinder liner directly formed by the outer wall casting, the coating is the key; the existing coating for the cylinder liner is mainly ordinary thermal insulation coating, and its main function is to reduce the cooling speed of the blank during the casting process and ensure the roughness of the blank. The metallographic structure and internal quality protect the mold, and the outer diameter of the cast blank cannot meet the use requirements of the injection-type cylinder liner; while the existing coatings that can meet the production requirements of the cylinder liner are mostly complicated in formula, expensive, and relatively difficult to use. Harsh, which increases the manufacturing cost of the cylinder liner

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coating for centrifugal casting and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A coating for centrifugal casting, made of the following raw materials in parts by weight: 3 parts of rectorite, 0.4 parts of sodium carboxymethylcellulose, 55 parts of quartz powder, 0.3 parts of ammonium lauryl sulfate, and 43 parts of water .

[0013] The preparation method of the coating for centrifugal casting comprises the following steps: taking rectorite, sodium carboxymethyl cellulose, and water according to the parts by weight, mixing, stirring evenly; then adding quartz powder, stirring evenly; finally adding ten Stir the dialkyl ammonium sulfate evenly to get the coating.

[0014] Coating Application

[0015] The coating prepared in this example is used in the preparation process of the cast-in cylinder liner, which includes the following steps: ①Smelting the molten iron to 1500°C and starting to take it out of the furnace, the weight percentage of each component in the molten iron is as follows: C 3.2% , S 0.05%, Si 2.5%, P 0.7%, Mn 0.7%, Cr 0.3%, Cu 0.4%...

Embodiment 2

[0019] A coating for centrifugal casting, made of the following raw materials in parts by weight: 1 part of rectorite, 0.1 part of sodium carboxymethylcellulose, 50 parts of quartz powder, 0.01 part of ammonium lauryl sulfate, and 40 parts of water .

[0020] The preparation method of the coating for centrifugal casting comprises the following steps: taking rectorite, sodium carboxymethyl cellulose, and water according to the parts by weight, mixing, stirring evenly; then adding quartz powder, stirring evenly; finally adding ten Stir the dialkyl ammonium sulfate evenly to get the coating.

Embodiment 3

[0022] A coating for centrifugal casting, made of the following raw materials in parts by weight: 5 parts of rectorite, 0.7 parts of sodium carboxymethylcellulose, 60 parts of quartz powder, 0.5 parts of ammonium lauryl sulfate, and 45 parts of water .

[0023] The preparation method of the coating for centrifugal casting comprises the following steps: taking rectorite, sodium carboxymethyl cellulose, and water according to the parts by weight, mixing, stirring evenly; then adding quartz powder, stirring evenly; finally adding ten Stir the dialkyl ammonium sulfate evenly to get the coating.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
heightaaaaaaaaaa
heightaaaaaaaaaa
Login to View More

Abstract

A coating for centrifugal casting is prepared by the following raw materials in parts by weight: 1-5 parts of rectorite, 0.1-0.7 part of sodium carboxymethylcellulose, 50-60 parts of quartz powder, 0.01-0.5 part of dodecyl ammonium sulfate and 40-45 parts of water. The coating disclosed by the invention is simple in formula, low in cost and simple in manufacturing process; and a cast-in type cylinder sleeve meeting industry requirements can be prepared together with the centrifugal casting process.

Description

technical field [0001] The invention belongs to the technical field of production of cast-in cylinder liners for engines, and in particular relates to a coating for centrifugal casting and a preparation method thereof. Background technique [0002] When using metal mold centrifugal casting technology to produce the cylinder liner directly formed by the outer wall casting, the coating is the key; the existing coating for the cylinder liner is mainly ordinary thermal insulation coating, and its main function is to reduce the cooling speed of the blank during the casting process and ensure the roughness of the blank. The metallographic structure and internal quality protect the mold, and the outer diameter of the cast blank cannot meet the use requirements of the injection-type cylinder liner; while the existing coatings that can meet the production requirements of the cylinder liner are mostly complicated in formula, expensive, and relatively difficult to use. Harsh, thereby i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22C3/00
CPCB22C3/00
Inventor 侯起飞邹悟会高广东刘治军
Owner ZYNP GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com