High-purity iron pearlescent pigment and manufacturing method thereof

A pearlescent pigment and a production method technology, which are applied in the directions of inorganic pigment processing, chemical instruments and methods, fibrous fillers, etc., to achieve the effects of improving vividness, simple operation method and strong applicability

Inactive Publication Date: 2015-04-29
ZHEJIANG COLORAY TECH DEV
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

So this method is not an ideal way to solve the problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-purity iron pearlescent pigment and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A high-purity iron pearlescent pigment, comprising a pearlescent pigment substrate 10, the outer surface of the pearlescent pigment substrate 10 is coated with Fe 2 o 3 cladding layer 11, the Fe 2 o 3 Between the cladding layer 11 and the pearlescent pigment substrate 10, several layers of composite layers 20 capable of reflecting and refracting light are coated, and the composite layers 20 are made of Fe 2 o 3 The cladding layer 11 and the auxiliary metal oxide layer 12 containing metal oxides of non-ferrous elements are composed, and the auxiliary metal oxide layer 12 is located between two layers of Fe 2 o 3 Between the cladding layers 11.

[0037] The aforementioned pearlescent pigment substrate 10 is one or more of natural mica, synthetic mica and glass. The metal oxide in the auxiliary metal oxide layer 12 is TiO 2 , ZrO 2 and one or more of ZnO.

[0038] Preferably, the composite layer 20 has four layers in total, and the metal oxide in the auxiliary met...

Embodiment 2

[0040] A preparation method of high-purity iron pearlescent pigment, comprising the following steps:

[0041] A. Feeding, add pearlescent pigment base material in the reaction vessel, add water, stir and heat up, add acid solution to adjust pH to acidic;

[0042] B. Add FeCl to the reaction vessel 3 solution, and add alkali solution to adjust the pH to be alkaline, and stir at constant temperature;

[0043] C. Add TiCl dropwise 4 or ZrCl 4 or ZnCl 2 solution into the reaction vessel, and stir;

[0044] D. Repeat steps B-C several times;

[0045] E. Add FeCl to the reaction vessel 3 solution, and adjust the pH to alkaline with alkali solution, and continue stirring at constant temperature;

[0046] F, washing the solid material in the reaction vessel with water, separating, drying and roasting to obtain high-purity iron pearlescent pigment.

[0047] Preferably, in step A, the temperature is raised to 80° C., and an acid solution is added to adjust the pH to 3; in step B, ...

Embodiment 3

[0051] Preparation of High Purity Bronze Pearlescent Pigment CR7500

[0052] 1. Put 30g of 10-60μm mica powder into a 1000ml beaker;

[0053] 2. Add water to 500ml, stir and heat up to 80°C;

[0054] 3. Control the speed at 350 rpm, and adjust the pH to 3.0;

[0055] 4. Begin to add 10ml of FeCl with a concentration of 1mol / L 3 solution, while maintaining a constant pH with 4mol / L NaOH solution, and stirring at constant temperature for 10 minutes after the addition;

[0056] 5. Drop 1ml of TiCl with a concentration of 2mol / L into the beaker 4 solution. Stir for 10 minutes after addition;

[0057] 6. Repeat steps 4 and 5 three times to complete 4 layers of TiO 2 the covering;

[0058] 7. Continue to drop about 270ml of FeCl with a concentration of 1mol / L 3 solution, while maintaining a constant pH with 4mol / L NaOH solution until the color reaches bronze, and continue to stir at constant temperature for 30 minutes;

[0059] 8. Wash and separate the materials in the beak...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of pearlescent pigments, and relates to a high-purity iron pearlescent pigment and a manufacturing method thereof. The high-purity iron pearlescent pigment comprises a pearlescent pigment base material; the outer surface of the pearlescent pigment base material is coated with a Fe2O3 coating layer; several composite layers capable of reflecting and refracting light rays are further coated between the Fe2O3 coating layer and the pearlescent pigment base material; each composite layer is composed of the Fe2O3 coating layer and an auxiliary metal oxide layer containing metal oxides of non-ferrous elements; the auxiliary metal oxide layer is located between two Fe2O3 coating layers. According to the invention, the color purity and brightness can be improved.

Description

technical field [0001] The invention belongs to the technical field of pearlescent pigments, and relates to a high-purity iron pearlescent pigment and a preparation method thereof. Background technique [0002] From the invention of pearlescent pigments, the iron series has been used in various fields as a large series. The preparation of ordinary iron series pearlescent pigments has already been patented at home and abroad, and the technology is already very mature. [0003] Pearlescent pigments are roughly divided into the following series according to the different coating materials: silver white series, interference series, gold series, iron series. Interference series, gold series, and iron series are usually called colored pearlescent pigment series because their colors are different from those of conventional natural pearls. [0004] After many years and technical improvements, many characteristic high-purity products have emerged in other color series. For example,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09C1/40C09C1/28C09C3/06
Inventor 卓仲标
Owner ZHEJIANG COLORAY TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com