Ethylene-vinyl acetate copolymer/polyaniline composite conductive material and preparation method thereof

A kind of vinyl acetate, composite conductive technology

Inactive Publication Date: 2015-03-25
HENAN UNIV OF URBAN CONSTR
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a kind of ethylene-vinyl acetate copolymer / polyaniline composite conductive material and its preparation method, which can overcome the current defects of complicated preparation process and high cost, or slightly lacking performance of the prepared product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ethylene-vinyl acetate copolymer/polyaniline composite conductive material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] After mixing 700 grams of EVA and 300 grams of PEO, melt and granulate through a twin-screw extruder at a temperature of 160° C., and the speed of the twin-screw extruder is 100 rpm to obtain EVA / PEO blended pellets. Put the EVA / PEO pellets into the mold, heat-press in a flat bed for 30 minutes, the molding temperature is 150°C, and the pressure is 15Mpa to obtain the EVA / PEO blended film. The blended membrane was placed in water at 30° C., and the PEO was dissolved at a constant temperature for 4 hours to obtain a porous EVA membrane.

[0031] 5 grams of EVA porous membrane and 10 grams of aniline are added to 1000 parts by weight of 1mol / L hydrochloric acid aqueous solution, and after stirring for 0.5 hours, 100 grams of 1mol / L ammonium persulfate aqueous solution is added dropwise to the reaction solution. 0.5 hours, and continue to react for 1 hour after the dropwise addition to complete the reaction. During the whole process, the temperature of the reaction syst...

Embodiment 2

[0033] After mixing 600 grams of EVA and 400 grams of PEO, melt and granulate through a twin-screw extruder at a temperature of 150° C., and the speed of the twin-screw extruder is 200 rpm to obtain EVA / PEO blended pellets. Put the EVA / PEO pellets into the mold, hot press in a flat bed for 20 minutes, the molding temperature is 140°C, and the pressure is 15Mpa to obtain the EVA / PEO blended film. The blended membrane was placed in water at 60° C., and the PEO was dissolved at a constant temperature for 2 hours to obtain a porous EVA membrane.

[0034] 10 grams of EVA porous membrane and 30 grams of aniline are added to 1000 parts by weight of 1mol / L hydrochloric acid aqueous solution, and after stirring for 0.5 hours, 250 grams of 1mol / L ammonium persulfate aqueous solution is added dropwise to the reaction solution. After 0.5 hours, continue to react for 4 hours after the dropwise addition to complete the reaction. During the whole process, the temperature of the reaction syst...

Embodiment 3

[0036] After mixing 700 grams of EVA and 300 grams of PEO, melt and granulate through a twin-screw extruder at a temperature of 160° C., and the speed of the twin-screw extruder is 300 rpm to obtain EVA / PEO blended pellets. Put the EVA / PEO pellets into the mold, heat-press in a flat bed for 30 minutes, the molding temperature is 150°C, and the pressure is 15Mpa to obtain the EVA / PEO blended film. The blended membrane was placed in water at 80° C., and the PEO was dissolved at a constant temperature for 1 hour to obtain a porous EVA membrane.

[0037] 15 grams of EVA porous membrane and 45 grams of aniline are added to 1000 parts by weight of 1mol / L hydrochloric acid aqueous solution, and after stirring for 0.5 hours, 300 grams of 1mol / L ammonium persulfate aqueous solution is added dropwise to the reaction solution, and the dropwise addition time After 0.5 hours, continue to react for 3 hours after the dropwise addition to complete the reaction. During the whole process, the t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of composite conductive materials and particularly relates to an ethylene-vinyl acetate copolymer / polyaniline composite conductive material and a preparation method thereof. The preparation method comprises the steps of firstly preparing an ethylene-vinyl acetate copolymer porous membrane, and then carrying out in situ polymerization on the ethylene-vinyl acetate copolymer porous membrane and aniline so as to prepare the ethylene-vinyl acetate copolymer / polyaniline composite conductive material. According to the preparation method, the problem that conductive polyaniline is absorbed by an EVA matrix is thoroughly solved. The preparation method has the advantages that the preparation process condition is easily realized, the cost is saved, and the conductivity of the ethylene-vinyl acetate copolymer / polyaniline composite conductive material is excellent.

Description

[0001] technical field [0002] The invention belongs to the technical field of composite conductive materials, and in particular relates to an ethylene-vinyl acetate copolymer / polyaniline composite conductive material and a preparation method thereof. Background technique [0003] Since American scientists A.J.Heeger and A.G.MacDiarmid and Japanese scientist H.Shirakawa discovered that doped polyacetylene (PA) has metal conductive properties in 1977, the concept that organic polymers cannot be used as conductive materials has been completely changed, and a new technology was born. A new interdisciplinary subject-conductive polymer. After the discovery of conductive polyacetylene, a series of conjugated polymers such as polyparaphenylene, polypyrrole, and polyaniline have been doped to have high conductivity. The study of conductive polymer materials not only has theoretical academic value, but also has high application value. [0004] Compared with other conductive polyme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G73/02C08J9/26C08L23/08C08L79/02
Inventor 赵金安潘玮胡继勇张启陈树芳张军帅
Owner HENAN UNIV OF URBAN CONSTR
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More