Nano lotus fiber/alginate porous material and preparation method thereof

A technology of porous material and lotus fiber is applied in the field of nano lotus fiber/alginate porous material and its preparation, which can solve the problems of easily damaging human cells and tissues, and achieve the effects of low cost, convenient use and good water absorption.

Inactive Publication Date: 2016-08-24
QINGDAO UNIV
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Common chemical cross-linking agents in the prior art, such as hexamethylene glycol dihydrazide, polyethylene glycol-diamine and other dihydrazines or diamines, are toxic and difficult to completely remove, and are easy to damage human cells and tissues after use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nano lotus fiber/alginate porous material and preparation method thereof
  • Nano lotus fiber/alginate porous material and preparation method thereof
  • Nano lotus fiber/alginate porous material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] 0.02% of nanometer lotus fiber, 1.3% of oxidized sodium alginate, 0.6% of carboxymethyl chitosan, and the balance is solvent.

Embodiment 2

[0043] 0.05% of nano lotus fiber, 1% of oxidized sodium alginate, 10% of carboxymethyl chitosan, and the balance is solvent.

Embodiment 3

[0045] 0.08% of nanometer lotus fiber, 1.3% of oxidized sodium alginate, 5% of carboxymethyl chitosan, and the balance is solvent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a nanometer lotus fiber / sodium alginate porous material and a preparation method thereof, belonging to the field of preparation of porous materials and processing and utilization of sodium alginate. The porous material is composed of 0.02% to 0.08% by weight of nanometer lotus fiber, 1% to 20% of oxidized sodium alginate, 0.6% to 10% of carboxymethyl chitosan, and the balance of solvent, wherein, The solvent is selected from one of deionized water, distilled water, physiological saline, water for injection or Ringer's solution. The present invention selects nanometer lotus fiber as the reinforcing body, oxidized sodium alginate as the base material, and carboxymethyl chitosan as the crosslinking agent. agent, and cross-link at a temperature of 20°C to 50°C to obtain a nanometer lotus fiber / sodium alginate porous material. The nanometer lotus fiber / sodium alginate porous material prepared by the present invention is a biodegradable biomaterial in a short period of time, has low cost, is convenient to use, is non-toxic to the human body, is antibacterial, and has good water absorption, biodegradability and biological properties. compatibility.

Description

technical field [0001] The invention relates to the field of preparation of medical porous materials and the processing and utilization of sodium alginate, in particular to a nanometer lotus fiber / alginate porous material with oxidized sodium alginate as a base material and a preparation method thereof. Background technique [0002] The choice of biomaterial determines the biocompatibility of the constructed porous scaffold material. Sodium alginate is a natural material extracted from seaweed plants, and is one of the natural biomaterials approved by the US Food and Drug Administration (FDA) for use in medical fields such as tissue engineering. Sodium alginate, a polysaccharide, has a similar structure to aminoglycans, a component of the skin dermal matrix, and has good biocompatibility. Skin fibroblasts, liver cells, chondrocytes, and osteoblasts are easily absorbed in alginate porous materials. In addition, sodium alginate also has good film-forming, gelling, hygroscopic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L5/04C08L5/08C08L97/02C08J9/28C08J3/24C08B37/04
Inventor 韩光亭宫英张元明张劲峰潘颖于仁霞
Owner QINGDAO UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com