Crease resisting agent for cotton and preparation method and application of crease resisting agent for cotton

A technology of anti-wrinkle agent and condensation reaction, which is applied in the field of anti-wrinkle agent for cotton and its preparation, which can solve the problems that the anti-wrinkle performance of the finished fabric is not involved, and achieve the effects of remarkable anti-wrinkle effect, enhanced firmness, improved wrinkle resistance and washability

Active Publication Date: 2014-12-10
ZHEJIANG SCI-TECH UNIV
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese invention patent: ZL200910054839.2, a compound containing two dichloro-s-triazine rings is reported, and it is believed that the crosslinking point is formed through the reaction of the chlorine atom in the compound molecule with the functional group between the active groups in the organic fiber, It can improve the shape stability of the fabric and the dimensional stability of the fabric, but it does not involve the wrinkle resistance of the finished fabric

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Crease resisting agent for cotton and preparation method and application of crease resisting agent for cotton
  • Crease resisting agent for cotton and preparation method and application of crease resisting agent for cotton
  • Crease resisting agent for cotton and preparation method and application of crease resisting agent for cotton

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] 1. Dissolution of cyanuric chloride

[0033] In a reaction flask equipped with a stirrer and a thermometer, add cyanuric chloride [select 20.24g (0.1mol)], and dissolve it with a mixture of acetone and ice water [select 20mL ice water and 10mL acetone] (i.e., acetone aqueous solution) , and mechanically stirred for 10 minutes to promote its full dissolution.

[0034] 2. Add m-phenylenediamine disulphonic acid [choose 13.4g (0.05mol)] into 40mL water, under the condition of stirring, slowly (3min) add sodium carbonate (0.05mol) powder equal to the substance amount, after the sodium carbonate powder is added , and continue to stir for 5 minutes, so that the m-phenylenediamine disulphonic acid becomes sodium m-phenylenediamine disulphonate, and a sodium m-phenylenediamine disulphonate solution is obtained.

[0035] 3. Slowly add m-phenylenediamine disulphonate sodium solution dropwise into the three-necked flask dissolved with cyanuric chloride system to carry out the fir...

Embodiment 2

[0046] 1. Dissolution of cyanuric chloride

[0047] In a reaction flask equipped with a stirrer and a thermometer, add cyanuric chloride [select 20.24g (0.1mol)], and dissolve it with a mixture of acetone and ice water [select 20mL ice water and 10mL acetone] (i.e., acetone aqueous solution) , and mechanically stirred for 10 minutes to promote its full dissolution.

[0048] 2. m-Phenylenediamine disulphonic acid [choose 13.4g (0.05mol)] into 40mL of water, under the condition of stirring, slowly add sodium carbonate (0.05mol) powder of the same amount, after adding the sodium carbonate powder, continue stirring For 5 minutes, the m-phenylenediamine disulphonic acid was converted into sodium m-phenylenediamine disulphonate to obtain a sodium m-phenylenediamine disulphonate solution.

[0049] 3. Slowly add m-phenylenediamine disulphonate sodium solution dropwise into the three-necked flask dissolved with cyanuric chloride system for the first condensation, the reaction temperat...

Embodiment 3

[0054] 1. Dissolution of cyanuric chloride

[0055] In a reaction flask equipped with a stirrer and a thermometer, add cyanuric chloride [select 20.24g (0.1mol)], and dissolve it with a mixture of acetone and ice water [select 20mL ice water and 10mL acetone] (i.e., acetone aqueous solution) , and mechanically stirred for 10 minutes to promote its full dissolution.

[0056] 2. m-Phenylenediamine disulphonic acid [choose 13.4g (0.05mol)] into 40mL of water, under the condition of stirring, slowly add sodium carbonate (0.05mol) powder of the same amount, after adding the sodium carbonate powder, continue stirring For 5 minutes, the m-phenylenediamine disulphonic acid was converted into sodium m-phenylenediamine disulphonate to obtain a sodium m-phenylenediamine disulphonate solution.

[0057] 3. Slowly add m-phenylenediamine disulphonate sodium solution dropwise into the three-necked flask dissolved with cyanuric chloride system for the first condensation, the reaction temperat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a crease resisting agent for cotton. The crease resisting agent is a compound with a structure described in formula I or II, can be applied to cotton fabrics, and can be particularly applied to pure cotton fabrics. Hetero active polyfunctional groups in molecules of the crease resisting agent for the cotton and hydroxide radicals of cotton fibers are subjected to chemical crosslinking to generate a network structure to prevent the slippage of fiber macromolecules and improve the washable crease resistance of the cotton fabrics. The invention also discloses a preparation method of the crease resisting agent for the cotton. Raw materials are easy and simple to obtain, and the synthetic process is simple and easy to implement.

Description

technical field [0001] The invention relates to the field of fabric anti-wrinkle agents, in particular to an anti-wrinkle agent for cotton, a preparation method thereof and an application in cotton fabrics. Background technique [0002] Cotton fabrics have many excellent wearing and wearing properties, such as moisture absorption and breathability, soft touch, economical benefits, and comfortable wearing. However, cotton fabrics are prone to wrinkling during wearing. With the improvement of science and technology and production and living standards, the anti-wrinkle finishing of cotton fabrics has become an important process to improve the fabric's wearing performance and its added value, and is an important field of dyeing and finishing production. The traditional anti-wrinkle finishing of cotton fabrics mostly uses N-methylol finishing agents. After finishing, the anti-wrinkle effect is ideal and the cost is low, but there is a problem of formaldehyde release. , Anti-wrin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M13/364C07D251/50D06M101/06
Inventor 沈一峰杨雷姜建堂
Owner ZHEJIANG SCI-TECH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products