Sheet-shaped mould plastic for manufacturing inspection well lid and preparation method for sheet-shaped mould plastic

A technology of sheet molding compound and manhole cover, applied in the field of sheet molding compound, can solve the problems of unsatisfactory mechanical strength, poor material interface bonding, difference in thermal expansion coefficient, etc. Effect

Inactive Publication Date: 2014-12-10
LINAN JUFENG URBAN SUPPORT EQUIP
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The mechanical strength of BMC material is not very ideal (bending strength is generally 80---120MPa), so only steel bars can be added to increase the load
The addition of steel bars has two major defects in the material: ①The surface of the steel bar is rusty, which often leads to poor bonding of the material interface (if the interface of the composite material is not well bonded, the effect of 1+1>2 will not be produced); ②The steel bar is Metal materials, BMC materials are non-metal materials, the two materials are due to the difference in thermal expansion coefficient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sheet-shaped mould plastic for manufacturing inspection well lid and preparation method for sheet-shaped mould plastic

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] In the process of making the manhole cover, the material sheet molding compound used is very important, and its intermediate core material is composed of glass fiber cloth impregnated with resin paste, the content of glass fiber cloth is 20-40 parts, and the resin paste includes the following materials :

[0033] 19-23 parts of unsaturated resin; 6-8 parts of low shrinkage agent; 1.4-1.6 parts of styrene; 0.5-1.5 parts of curing agent; 1.5-1.7 parts of zinc stearate; 0.3 parts; 40-50 parts of heavy calcium carbonate 800-1000 mesh.

[0034] Preferably, the resin paste is made of the following materials: 21 parts of unsaturated resin; 7 parts of low shrinkage agent; 1.5 parts of styrene; 1 part of curing agent; 1.6 parts of zinc stearate; 0.02 parts of benzoquinone; 0.25 parts of pigment paste part; 45 parts of heavy calcium carbonate 800-1000 order, and wherein heavy calcium carbonate is waste material, and the present invention turns waste into wealth, has stronger env...

Embodiment 2

[0038] Such as figure 1 As shown, the technological process of sheet molding compound (SMC) production mainly includes resin paste preparation, pasting operation, infiltration, thickening and other processes. Combined with the preparation method of resin paste, the preparation process of sheet molding compound (SMC) is as follows:

[0039] 1) 19-23 parts of unsaturated resin, 6-8 parts of low shrinkage agent, 1.4-1.6 parts of styrene, 0.5-1.5 parts of curing agent, 1.5-1.7 parts of zinc stearate, 0.01-0.03 parts of benzoquinone, Put 0.2-0.3 parts of the pigment paste into the batching kettle 2, stir for 30-60 minutes and add a thickener, the thickener is 40-50 parts of heavy calcium carbonate 800-1000 mesh;

[0040]2) After stirring for 60-120 minutes, add magnesium oxide and stir quickly for 20-30 seconds to make a resin paste; the SMC product equipment is equipped with a trough, and the resin paste is immediately poured into the trough; there are 2 sets of film rolls on the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention firstly provides an environment-friendly and low-cost sheet-shaped mould plastic for manufacturing an inspection well lid. A middle core material of the sheet-shaped mould plastic consists of glass fiber cloth which is soaked with resin paste, wherein the content of glass fibers is 20-40 parts, and the resin paste comprises the following materials in parts by weight: 19-23 parts of unsaturated resin, 6-8 parts of a low shrinkage agent, 1.4-1.6 parts of styrene, 0.5-1.5 parts of a curing agent, 1.5-1.7 parts of zinc stearate, 0.01-0.03 part of benzoquinone, 0.2-0.3 part of pigment paste, and 40-50 parts of ground calcium carbonate of 800-1000 meshes. The invention further provides a method for preparing the sheet-shaped membrane plastic. The sheet-shaped mould plastic provided by the invention adopts base raw materials, and further adopts waste ground calcium carbonate, is low in cost and beneficial to environmental protection and energy conservation. The sheet-shaped mould plastic manufactured by virtue of the method is high in technical content, stable in process, relatively low in cost, strong in bearing capacity; and a product manufactured by virtue of the sheet-shaped mould plastic has the characteristics of tight matching, wear resistance, corrosion resistance, a light structure, an attractive style, light weight and easiness in installation, is remarkable in social benefit and economic benefit.

Description

technical field [0001] The invention relates to a sheet-shaped molding compound, in particular to a sheet-shaped film plastic for making manhole covers; the invention also relates to a preparation method of the sheet-shaped molding compound. [0002] Background technique [0003] SMC--sheet molding compound: SMC is the abbreviation of Sheet molding compound, that is, sheet molding compound. The main raw materials are composed of SMC non-alkali yarn, unsaturated resin, low shrinkage additive, filler and various auxiliary agents. SMC has the advantages of superior electrical properties, corrosion resistance, light weight, easy and flexible engineering design, and its mechanical properties can be compared with some metal materials, so it is widely used in transportation vehicles, construction, electronics, electrical, manhole covers and other industries . [0004] Usually, among the SMC materials for making manhole covers, they are generally composed of three categories: syn...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F283/01C08K7/00C08K7/14C08K3/26C08K5/098
Inventor 陶坚朱圣光
Owner LINAN JUFENG URBAN SUPPORT EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap